Effects of Substrate Temperature on Helium Content and Microstructure of Nanocrystalline Titanium Films

Helium-charged nanocrystalline titanium films have been deposited by HeAr magnetron co-sputtering. The effects of substrate temperature on the helium content and microstructure of the nanocrystalline titanium films have been studied. The results indicate that helium atoms with a high concentration are evenly incorporated in the deposited titanium films. When the substrate temperature increases from 60℃ to 350℃ while the other deposition＇parameters are fixed, the helium content decreases gradually from 38.6 at.% to 9.2at.%, which proves that nanocrystalline Ti films have a great helium storage capacity. The 20 angle of the Bragg peak of （002） crystal planes of the He-charged Ti film shifts to a lower angle and that of （100） crystal plane is unchanged as compared with that of the pure Ti film, which indicates that the lattice parameter c increases and a keeps at the primitive value. The grain refining and helium damage result in the diffraction peak broadening.     

Morphology of Platinum Nanowire Array Electrodepostied Within Anodic Aluminium Oxide Template Characterized by Atomic Force Microscopy

Unifrom platinum nanowires were synthesized by electrodepositing the platinum under a very low altering current frequency(20Hz) and increasing voltage(5-15V）in the proes of anodic aluminium oxide(AAO) template. Atomic force microscopy observation indicates that the template membranes we obtained have hexagonally clse-packed nanochannels.The platinum nanowires have highly ordered arrays after partially dissolving the aluminium oxide membrane.With the increasing dissolvoing time,the platinum nanowire array collapsed.A concave topography of the aluminium substrate was observed after the aluminium oxide membrane was dissolved completely and the platinum nanowires were released from the template.Platinum nanowires were also characterized by transmission electron microscopy and the phase structure of the Al/AAO/Pt composite was proven by x-ray diffraction.     

Effects of Processing Parameters on Microstructure and Properties of Nanoscale ZrC/ZrB2 Multilayered Coatings

ZrC/ZrB2 multilayered coatings with bilayer periods of 3.5-40nm are synthesized by rf magnetron sputtering. Analyses of x-ray diffraction, scanning electron microscopy and nanoindentation indicate that multilayered coatings possess much higher hardness and greater fracture resistance than monolithic ZrC and ZrB2 coatings. A maximum hardness （41.TCPa） and a critical fracture load （73.7mN） are observed in the multilayer with A = 32 nm deposited at the substrate bias -40 V. Higher residual stress built in the ZrC layer can be released by periodic insertion of ZrB2 into the ZrC layer. A clear multilayered structure with mixed ZrB2（001）, ZrB2 （002） and ZrC （111） orientations should be responsible for the enhanced mechanical properties.     

反应离子镀光学薄膜的微观结构分析

用反应离子镀方法制备了ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜，用透射电子显微镜分别观察了由反应离子镀方法及传统蒸镀法二种不同工艺制得的ＴｉＯ２单层膜及ＴｉＯ２／ＳｉＯ２多层膜的断面结构，并对ＴｉＯ２单层膜进行了喇曼分析和卢瑟福背散射分析。     

La2O3掺杂对SrTiO3压敏电容双功能陶瓷显微结构及电性能的影响

用CALPHAD技术优化计算了稀土卤化物熔盐TbCl3-ACl(A=Li，Na，K，Rb，Cs)五个二元系相图以及其热力学性质。优化采用了短程有序-扩展似化学模型，得到了热力学性质和相图自洽一致的结果，并与相应的实验相图进行了比较，对其中差异的部分进行了分析和修正。讨论了热力学优化结果，并探讨了过剩热力学性质变化的规律和特征。     

Characterization of the Nanoscale Microstructure of an Immersion Silver on Sputtered Copper

1 INTRODUCTION Silver and its compounds have received much attention due to their current and potential applica- tions in many areas[1, 2]. As a metal with the highest electrical and thermal conductivities, silver was one of the most important noble metals used in electrical industries in the last century. Several decades ago, however, the development of silver application in electronic area seemed not so quick. The fear for some undesirable phenomena involving silver, like “electrochemi…     

A fibrous hypercrosslinked sorbent prepared on PP-ST-DVB matrix via post-crosslinking reaction

A fibrous sorbent possessing abundant micropore structure was firstly prepared via post-crosslinking reaction on the PP-ST-DVB original fiber. Its micromorphology and sorptive properties were investigated, and the results demonstrated that the novel fibrous hypererosslinked sorbent has narrow pore-size distribution, small average porous radius （1.90 nm）, high specific surface area （362.31 m^2/g）, and fine sorptive properties for small organic molecules.     

Y2O3, La2O3, Sm2O3对氧化铝瓷烧结及力学性能的影响

研究了3种稀土氧化物对氧化铝陶瓷烧结性能和力学性能的影响.结果表明 含Y2O3,La2O3,Sm2O3的添加剂促进了氧化铝瓷的烧结,提高了氧化铝瓷的力学性能.Y2O3和Sm2O3掺量为0.50%,La2O3掺量为0.75%时氧化铝瓷在1600或1620 ℃保温2 h烧结,相对密度达98.9%以上,强度超过439 MPa,断裂韧性达5.15 MPa·m1/2以上.微观结构分析表明,Y2O3,La2O3,Sm2O3抑止氧化铝晶粒生长,细化晶粒,使晶粒尺寸较均匀形成致密化结构.     

Zr掺杂对MgB2超导微观结构和超导电性的影响

将Mg粉、Zr粉和B粉按比例混合获得Mg1-xZrxB2(x=5%10%和20%),压制成型后,在流通氩气的条件下于800℃烧结2h.利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)分析烧结后样品的显微结构和化学组成,采用差热分析(DTA)观察Zr掺杂对MgB2分解温度的影响,并用物性测试仪(PPMS)测试样品的超...     

Relationships among Preparative Technique,Phase Composition and Bending Strength of Bauxite Porcelain

1 INTRODUCTION Bauxite porcelain is a novel “K2O–Al2O3–SiO2” system ceramic by using sintered bauxite, clay and potash feldspar and albite as the main raw materials with the Al2O3’s content of 50%～60(massfraction). Compared to the traditional“K2O–Al2O3–SiO2” feldspar porcelain by using quartz, bolus alb and potash feldspar and albite as the main raw materials, the bauxite porcelain possesses such advantages as high mechanical strength, excellent electrical insula- tion prop…