PHOTOLUMINESCENCE STUDY ON Hg1-xCdxTe THIN FILM IMPLANTED WITH As ION

Photoluminescence spectra of a series of MBE-grown Hg_1-xCd_xTe samples with the same mole fraction of about x≈0.39 have been measured at different temperatures from 5 to 100 K. By aid of the temperature and exciting laser power dependence of photoluminescence peak energy and relative intensity, as well as of the comparison with other measurements, four main structures dominating in the photoluminescence spectra are attributed to band to band, D^oX, A^oX and D^oA^o transitions. A deep donor state level located at about 8.5meV below the bottom of the conduction band has been observed and is determined to be due to the arsenic-occupied mercury vacancies. Two acceptor levels located at about 14.5 meV and about 31.5 meV above the top of the valance band have also been found from the measuements, which are identified as the mercury vacancies and As in anion site, respectively.     

分子束外延HgCdTe材料生长参数的实时监测研究

报道了用椭圆偏振技术和红外辐射测温技术对ＨｇＣｄＴｅ生长关键参数实时监测的结果，建立了ＨｇＣｄＴｅ材料在生长温度下的标准光学常数数据库，在研究中对生长过程中材料的发射率以及红外辐射强度进行了理论分析，为生长温度的实时精确控制提供了理论依据，并在实验上获得了小于±１℃的生长温度控制精度．     

GaAs／AlGaAs多量子阱红外探测器电极引接损伤研究

从柱形流变模型出发讨论了压焊引接电极时受压面的压强分布，压力损伤半径和深度以及超声压焊时的损伤，并讨论了ＧａＡｓ／ＡｌＧａＡｓ多量子阱红外探测器的超声压焊的压力损伤和Ｉｎ球熔焊的Ａｕ丝力损伤。     

CdTe/ZnTe应变量子阱的静压光致发光研究

在77K和0—50kbar静压范围内研究了阱宽分别为m=4.8,12个单原子层的(CdTe)_m/(ZnTe)_n应变量子阱的静压光致发光。在常压下,m=8和12的量子阱的发光峰比m=4的量子阱的发光峰显著变宽。表明在这两个阱中应变已发生弛豫。用Kronig-Penney模型计算的峰值能量证实了这一点。在所测静压范围内峰宽无明显增加。它们的压力系数从m=12的6.81meV/kbar增加到m=4的8.24meV/kbar。计算表明,势垒高度随压力增加而增加是使压力系数随阱宽减小而增加的主要原因。     

MBE生长的p－Hg_（1－x）Cd_xTe外延薄膜变磁场下的Hall系数及电导率

本文报道了利用分子束外延技术在ＧａＡｓ（２１１）Ｂ衬底上生长Ｈｇ１－ｘＣｄｘＴｅ／ＣｄＴｅ异质结，并通过ＶａｎｄｅｒＰａｕｗ（ＶｄＰ）方法测量Ｐ－Ｈｇ１－ｘＣｄｘＴｅ外延薄膜在不同温度及磁场下Ｈａｌｌ系数和电导率，采用最小二乘法对实验数据下行拟合，得到了混合导电机制下电子、重空穴和轻空穴的迁移率及载流子浓度．     

［（Cdse）_m（ZnSe）_n］_p－Znse多量子阱中的多声子散射

对用原子层外延方法，在［００１］晶向ＧａＡｓ衬底上生长的［（Ｃｄｓｅ）ｍ（Ｚｎｓｅ）ｎ］ｐ－ＺｎＳｅ应变量子阱结构，在１０～３００Ｋ温度范围内测量了喇曼散射光谱，观察到两种类ＺｎＳｅＬＯ声子限制模．利用改变样品温度和入射光能量实现了共振喇曼散射，观察到高达７阶的类ＺｎＳｅＬＯ声子模．并讨论了多声子喇曼散射和热萤光过程的区别．     

Pb_(1-x)Sn_xTe材料等离子体反射边的温度漂移现象

本文报道对Pb_(0.8)Sn_(0.2)Te单晶以及p-PbSnTe/p~ -PbSnTe和n-PbTe/p-PbSnTe/p~ -PbSnTe液相外延层进行观察得到的等离子体(Plasma)反射边的温度漂移现象。认为这是由于电极化有效质量m_s和散射弛豫时间τ共同影响的结果,其中m_s随温度的升高而变大,起着主要的作用。本文最后对浓度为1.45×10~(19)/cm~3的单晶样品进行了模拟计算,在计算光谱与实验光谱达到一致的情况下,得到了m_s,τ随温度的变化曲线。     

静压下（CdSe）_m／（ZnSe）_n－ZnSe超短周期超晶格量子阱的共振喇曼散射研究

在静压和液氮温度下观察到（ＣｄＳｅ）ｍ／（ＺｎＳｅ）ｎ短周期超晶格中重空穴激子的复合发光和多达４阶的类ＺｎＳｅＬＯ多声子喇曼散射，并观察到厚ＺｎＳｅ势垒层的带边发光和限制在厚势垒层中的类ＺｎＳｅＬＯ声子散射．结果表明，加压后（ＣｄＳｅ）ｍ／（ＺｎＳｅ）ｎ短周期超晶格中的类ＺｎＳｅ的１ＬＯ和２ＬＯ声子模频率分别以３．７６和７．１１ｃｍ－１／ＧＰａ的速率向高频方向移动，超晶格阱层光致发光峰的压力系数为５９．８ｍｅＶ／ＧＰａ．与（ＣｄＳｅ）ｍ／（ＺｎＳｅ）ｎ短周期超晶格共振时的类ＺｎＳｅ１ＬＯ声子模频率比与ＺｎＳｅ势垒层共振时的类ＺｎＳｅ１ＬＯ声子模频率低２．０ｃｍ－１，反映了（ＣｄＳｅ）ｍ／（ＺｎＳｅ）ｎ短周期超晶格中ＬＯ声子的限制效应     

CdTe/ZnTe超晶格的多声子共振喇曼谱研究

用共振喇曼散射研究了CdTe/ZnTe应变层超晶格的多声子谱.实验结果表明,我们首次观察到了多达10级的ZnTeLO的多声子喇曼散射,和反映超晶格结构的子带跃迁介入多声子共振喇曼散射过程的实验现象.     

CdTe/ZnTe应变量子阱的静压光致发光研究,

在77K和0—50kbar静压范围内研究了阱宽分别为m=4.8,12个单原子层的(CdTe)_m/(ZnTe)_n应变量子阱的静压光致发光。在常压下,m=8和12的量子阱的发光峰比m=4的量子阱的发光峰显著变宽。表明在这两个阱中应变已发生弛豫。用Kronig-Penney模型计算的峰值能量证实了这一点。在所测静压范围内峰宽无明显增加。它们的压力系数从m=12的6.81meV/kbar增加到m=4的8.24meV/kbar。计算表明,势垒高度随压力增加而增加是使压力系数随阱宽减小而增加的主要原因。