PHOTOLUMINESCENCE STUDY ON Hg1-xCdxTe THIN FILM IMPLANTED WITH As ION

Photoluminescence spectra of a series of MBE-grown Hg_1-xCd_xTe samples with the same mole fraction of about x≈0.39 have been measured at different temperatures from 5 to 100 K. By aid of the temperature and exciting laser power dependence of photoluminescence peak energy and relative intensity, as well as of the comparison with other measurements, four main structures dominating in the photoluminescence spectra are attributed to band to band, D^oX, A^oX and D^oA^o transitions. A deep donor state level located at about 8.5meV below the bottom of the conduction band has been observed and is determined to be due to the arsenic-occupied mercury vacancies. Two acceptor levels located at about 14.5 meV and about 31.5 meV above the top of the valance band have also been found from the measuements, which are identified as the mercury vacancies and As in anion site, respectively.     

半导体超晶格的多声子拉曼散射研究

半导体超晶格的多声子拉曼散射研究／张树霖，杨昌黎，侯勇田（北京大学物理系北京１００８７１）彭中灵，李杰，袁诗鑫（中科院上海技物所上海２０００８３）Ｒ．Ｐｌａｎｅｌ（ＭｉｃｒｏｓｔｒｕｃｔｕｒｅｓａｎｄＭｉｃｒｏｅｌｅｃｔｒｏｎｉｃｓＬａｂｏｒａｔｏｒ...     

PHOTOLUMINESCENCE STUDY ON Hg1-xCdxTe THIN FILM IMPLANTED WITH As ION

Photoluminescence spectra of a series of MBE-grown Hg_1-xCd_xTe samples with the same mole fraction of about x≈0.39 have been measured at different temperatures from 5 to 100 K. By aid of the temperature and exciting laser power dependence of photoluminescence peak energy and relative intensity, as well as of the comparison with other measurements, four main structures dominating in the photoluminescence spectra are attributed to band to band, D^oX, A^oX and D^oA^o transitions. A deep donor state level located at about 8.5meV below the bottom of the conduction band has been observed and is determined to be due to the arsenic-occupied mercury vacancies. Two acceptor levels located at about 14.5 meV and about 31.5 meV above the top of the valance band have also been found from the measuements, which are identified as the mercury vacancies and As in anion site, respectively.     

STUDY OF MOLECULAR BEAM EPITAXIAL GROWTH AND OPTICAL CHARACTERISTICS OF HgCdTe

HgCdTe epilayers were grown by molecular beam epitaxy on GaAs(211)B substrates. Process of the HgCdTe epitaxial growth can be monitored by reflection high-energy electron diffraction. Results of the infrared transmission spectrum, Raman scattering spectrum and infrared photoluminescence spectrum in magnetic field have been studied.     

(CdSe)_l(ZnSe)_3/ZnSe短周期超晶格多量子阱的共振Ramam谱

在(CdSe)_1(ZnSe)_3/ZnSe短周期超晶格多量子阱中,根据一维线性链模型计算的结果与实验结果的比较表明,我们在不同的共振条件下分别观察到了来自多量子阱的阱中和垒中ZnSe限制纵光学声子模的Raman散射。与GaAs/AlAs量子阱的偏振选择定则不同,在共振条件下,我们在两种偏振配置下都观察到了阱中ZnSe限制模LO_1,并认为这种不同可能来源于样品特殊的电子子带结构和光学声子行为。     

(CdSe)1(ZnSe)3/ZnSe短周期超晶格多量子阱的共振Ramam谱

在(CdSe)₁(ZnSe)₃/ZnSe短周期超晶格多量子阱中,根据一维线性链模型计算的结果与实验结果的比较表明,我们在不同的共振条件下分别观察到了来自多量子阱的阱中和垒中ZnSe限制纵光学声子模的Raman散射。与GaAs/AlAs量子阱的偏振选择定则不同,在共振条件下,我们在两种偏振配置下都观察到了阱中ZnSe限制模LO₁,并认为这种不同可能来源于样品特殊的电子子带结构和光学声子行为。 关键词：     

Ge/ZnSe(100)异质结能带偏移的同步辐射光电子能谱研究

利用同步辐射光电子能谱研究了Ge/ZnSe（100）极性界面的能带连接问题．表面灵敏的芯能级谱显示出Ge原子与Se原子在界面处存在较弱的化学反应．利用芯能级技术，测量了该异质结的价带偏移，为1.76±0.1eV．用界面键极性模型对ZnSe（100）极性表面对价带偏移的影响进行了讨论，理论与实验符合较好 关键词：