Magnetism and magnetoresistance of Er1-xSmxMn6Ge6(x=0.2－1.0) compounds

Magnetic and transport properties of Er_{1-x}Sm_xMn_6Ge_6(x=0.2-1.0) have been investigated by x-ray diffraction (XRD) and magnetization measurement. Analysis of the XRD patterns indicates that the samples with x≤0.4 mainly consist of HfFe_6Ge_6-type phase and the samples with 0.6≤x≤1.0 mainly consist of YCo_6Ge_6-type phase (P6/mmm). The lattice constants and the unit cell volume increase with increasing Sm content. The antiferro－ferri－ferromagnetic transitions can be observed with increasing Sm content. The samples with x=0.2 and 0.4 order antiferromagnetically at 420 and 425K, respectively. The samples with x=0.6, 0.8 and 1.0 order from ferri- to ferromagnetically over the whole magnetic ordering temperature range. The corresponding Curie temperatures are 435, 441 and 446K, respectively. The magnetoresistance (MR) isotherms of the sample with x=0.8, measured at various temperatures, are analysed. The magnitude of MR is found to be positive below 55K and gradually increases to a relatively large value of about 5.02% at 5K in a field of 5T as the temperature is lowered. A possible explanation for the positive MR is given.     

Direct measurement of the interfacial barrier height of the manganite p–n heterojunction

A manganite p-n heterojunction composed of Lao.67Sro.33MnO3 film and 0.05 wt% Nb-doped SrTiO3 substrate is fabricated. Rectifying behavior of the junction well described by the Shockley equation is observed, and the transport properties of the interface are experimentally studied. A satisfactorily logarithmic linear dependence of resistance on temperature is observed in a temperature range of 150 K-380 K, and the linear relation between bias and activation energies deduced from the R - lIT curves is observed. According to activation energy, the interfacial barrier of the heterojunction is obtained, which is 0.91 eV.     

Magnetic properties and magnetoresistance of HfFe2Ge2-type Dy1-xGdxMn6Ge6 (x=0.1－0.6) compounds

The magnetic properties and magnetoresistance effects of Dy_{1-x}Gd_xMn_6Ge_6 (x=0.1－0.6) compounds have been studied by magnetic properties and resistivity measurements in applied magnetic fields up to 5T. The compounds with x=0.1, 0.2, 0.4 and 0.5 order antiferromagnetically at 425, 428, 430 and 432K, respectively, and there are second magnetic phase transitions below 100K. The compound with x=0.6 exhibits a transition from ferrimagnetic to antiferromagnetic, then to ferrimagnetic state again with decreasing temperature. Furthermore, it displays a field-induced metamagnetic transition, and its threshold field decreases with increasing temperature. The magnetoresistance curve of the compound with x=0.6 in applied magnetic fields up to 5T is presented and the magnetoresistance effects are related to the metamagnetic transitions.     

Giant magnetoresistance in Y0.9La0.1Mn6Sn6 compound

Magnetic transitions and magnetoresistance effect of the HfFe_6Ge_6-type Y_{0.9}La_{0.1}Mn_6Sn_6 compound have been investigated in the temperature range of 5－380K. The sample displays antiferromagnetic behaviour in the whole temperature range below Néel temperature T_N=309K. The metamagnetic transition from antiferromagnetism to ferromagnetism can be induced by an applied field. The metamagnetic transition field decreases monotonically from 2T at 5K to 0.4T at 300K. The giant magnetoresistance effect is observed with the metamagnetic behaviour, such as -10.4% at 245K under a field of 5T.     

Magnetic entropy change and magnetic phase transition of LaFe11.4Al1.6Cx （x=0-0.8） compounds

The unit cell volume and phase transition temperature of LaFe11.4Al1.6Cx compounds have been studied. The magnetic entropy change, refrigerant capacity and the type of magnetic phase transition are investigated in detail for LaFe11.4Al1.6Cx with x=0.1, All the LaFe11.4Al1.6Cx （x=0-0.8） compounds have the cubic NaZn13-type structure. The addition of carbon atoms brings about a considerable increase in the lattice parameter. The bulk expansion results in the change of phase transition temperature （Tc）, Tc increases from 187K to 269 K with x varying from 0.1 to 0.8, Meanwhile an increase in the lattice parameter can also cause a change of the magnetic ground state from antiferromagnetic to ferromagnetic. Large magnetic entropy change IASI is found over a large temperature range around Tc and the refrigerant capacity is about 322J/kg for LaFe11.4Al1.6C0.1. The magnetic phase transition belongs in weakly first-order one for x=0.1.     

NaZn13型结构LaFe13－xAlxCy化合物的磁熵变与磁相变的研究

研究了NaZn₁₃型结构LaFe_13-xAl_xC_0.1(x=1.6，1.8)间隙化合物的磁制冷能力和磁相变.利用麦克斯韦关系式计算得到，高Al含量LaFe_13-xAl_x碳化物的最大磁熵变值|ΔS|_m低于低Al含量碳化物的最大磁熵变值.随Al含量的增加，化合物的磁熵变峰展宽，但由于磁熵变大幅降低，衡量磁制冷能力的q值随之降低.基于朗道相变原理，考虑到自旋涨落的影响，磁自由能可以展开到磁化强度的6次方项，材料的相变类型由磁化强度的4次方项系数a₃(T)的符号来进行判断.随着Al含量的增加，研究的碳化物相变由弱的一级相变转为二级相变. 关键词： 13-xAl_x碳化物')" href="#">LaFe_13-xAl_x碳化物 磁制冷能力 磁相变     

NaZn13型结构LaFe13-xAlxCy化合物的磁熵变与磁相变的研究

研究了NaZn13型结构LaFe13-xAlxC0.1(x=1.6,1.8)间隙化合物的磁制冷能力和磁相变.利用麦克斯韦关系式计算得到,高Al含量LaFe13-xAlx碳化物的最大磁熵变值|ΔS|m低于低Al含量碳化物的最大磁熵变值.随Al含量的增加,化合物的磁熵变峰展宽,但由于磁熵变大幅降低,衡量磁制冷能力的q值随之降低.基于朗道相变原理,考虑到自旋涨落的影响,磁自由能可以展开到磁化强度的6次方项,材料的相变类型由磁化强度的4次方项系数a3(T)的符号来进行判断.随着Al含量的增加,研究的碳化物相变由弱的一级相变转为二级相变.     

Effect of charge order transition on tunneling resistance in Pr_(0.6)Ca_(0.4)MnO_3/Nb-doped SrTiO_3 heterojunction

An oxide p–n heterojunction composed of Pr0.6Ca0.4MnO3film, with a charge order(CO) transition, and 1wt% Nbdoped SrTiO3substrate is fabricated, and the transport properties of the interface are experimentally studied. The rectifying behavior of the junction, well described by the Newman equation, is observed, indicating that tunneling is the dominant process by which the carriers pass through the interface. Above and below the CO transition temperature, satisfactory linear dependencies of junction resistance on temperature are observed, but the slopes of the two resistance-temperature relations are different. The CO process is believed to be relevant to this difference.