变In组分沟道的MM-HEMT材料电子输运特性研究

在变缓冲层高迁移率晶体管（MM_HEMT）器件中，二维电子气的输运性质对器件性能起着决定作用.通过低温下二维电子气横向电阻的量子振荡现象，结合变温度的Hall测量，系统研究了不同In组分沟道MM_HEMT器件中子带电子迁移率和浓度随温度的变化关系.结果表明，沟道中In组分为0.65的样品，材料电学性能最好，In组分高于0.65的样品，严重的晶格失配将产生位错，引起迁移率下降，大大影响材料和器件的性能. 关键词： 变缓冲层高迁移率晶体管 Shubnikov_de Hass 振荡     

Influence of spacer layer thickness on the current-voltage characteristics of pseudomorphic AlAs/In0.53Ga0.47As/InAs resonant tunnelling diodes

This paper investigates the dependence of current voltage characteristics of AlAs/In0.53Ga0.47As/InAs resonant tunnelling diodes （RTDs） on spacer layer thickness. It finds that the peak and the valley current density J in the negative differential resistance （NDR） region depends strongly on the thickness of the spacer layer. The measured peak to valley current ratio of RTDs studied here is shown to improve while the current density through RTDs decreases with increasing spacer layer thickness below a critical value.     

High sensitivity Hall devices with AlSb/InAs quantum well structures

AlSb/InAs quantum well (QW) structures and InAs films on GaAs (001) substrates were grown by molecular beam epitaxy (MBE). We investigated the dependence of electron mobility and two-dimensional electron gas (2DEG) concentration on the thickness of an InAs channel. It is found that electron mobility as high as 19050 cm2·V-1·s-1 has been achieved for an InAs channel of 22.5 nm. The Hall devices with high sensitivity and good temperature stability were fabricated based on the AlSb/InAs QW structures. Their sensitivity is markedly superior to Hall devices of InAs films.     

Influence of Ⅴ/Ⅲ ratio on the structural and photoluminescence properties of In0.52AlAs/In0.53GaAs metamorphic high electron mobility transistor grown by molecular beam epitaxy

A series of metamorphic high electron mobility transistors （MMHEMTs） with different Ⅴ/Ⅲ flux ratios are grown on CaAs （001） substrates by molecular beam epitaxy （MBE）. The samples are analysed by using atomic force microscopy （AFM）, Hall measurement, and low temperature photoluminescence （PL）. The optimum Ⅴ/Ⅲ ratio in a range from 15 to 60 for the growth of MMHEMTs is found to be around 40. At this ratio, the root mean square （RMS） roughness of the material is only 2.02 nm; a room-temperature mobility and a sheet electron density are obtained to be 10610.0cm^2/（V.s） and 3.26×10^12cm^-2 respectively. These results are equivalent to those obtained for the same structure grown on InP substrate. There are two peaks in the PL spectrum of the structure, corresponding to two sub-energy levels of the In0.53Ga0.47As quantum well. It is found that the photoluminescence intensities of the two peaks vary with the Ⅴ/Ⅲ ratio, for which the reasons are discussed.     

不同量子阱宽度的InP基In0.53GaAs/In0.52AlAs高电子迁移率晶体管材料二维电子气的性能研究

用Shubnikov-de Haas(SdH)振荡效应，研究了在1.4 K下不同量子阱宽度(10—35 nm)的InP基高电子迁移率晶体管材料的二维电子气特性.通过对纵向电阻SdH振荡的快速傅里叶变换分析，得到不同阱宽时量子阱中二维电子气各子带电子浓度和量子迁移率.研究发现，在Si掺杂浓度一定时，阱宽的改变对于量子阱中总的载流子浓度改变不大，但是随着阱宽的增加，阱中的电子从占据一个子带到占据两个子带，且第二子带上的载流子迁移率远大于第一子带迁移率.当量子阱宽度为20 nm时，处在第二子能级上的电子数与处在 关键词： 量子阱宽 二维电子气 Shubnikov-de Haas振荡 高电子迁移率晶体管