排序方式: 共有17条查询结果,搜索用时 15 毫秒
1.
研究了230MeV的208Pb27+辐照Al2O3样品及随后在600,900,1100K高温条件下退火后的光致发光特性。从辐照样品的测试结果可以清楚地看到在波长为390,450nm处出现了强的发光峰。辐照量为1×1013ions/cm2时,样品的发光峰最强。经过600K退火2h后测试结果显示,380nm发光峰剧烈增强,而其他发光峰显示不明显。在900K退火条件下,380nm的发光峰开始减弱,而在360,510nm出现了明显的发光峰,至到1100K退火完毕后380nm的发光峰完全消失,而360,510nm的发光峰相对增强。从被辐照样品的FTIR谱中看到,波数在460~510cm-1间的吸收是振动模式,经过离子辐照后,吸收带展宽,随着辐照量的增大,Al2O3振动吸收峰消失,说明Al2O3振动模式被完全破坏。1000~1300cm-1之间为Al—O—Al桥氧的伸缩振动模式,辐照后吸收带向高波数方向移动,说明其振动模式受到影响。辐照剂量较小的样品,损伤程度相对较低,经退火晶化后,振动模式基本恢复到单晶状态;辐照剂量较高的样品,损伤程度大,退火处理后表面变得较粗糙,振动模式并未出现,说明结构破坏严重。 相似文献
2.
利用傅立叶变换红外光谱仪对注He尖晶石样品随退火温变化而引起光吸收性能的变化进行了研究。 发现尖晶石样品在626.4 cm-1附近的吸收峰随注入剂量的增加向小波数方向移动, 而在随后退火过程该吸收峰随退火温度的增加而向大波数方向回复。 该吸收峰的回复行为依赖于注入剂量和退火温度。 认为在626.4 cm-1附近吸收峰随注入剂量和退火温度的这种变化与尖晶石中He的俘获以及释放有关。 The infrared absorption behavior of helium implanted spinel with annealing temperature was studied by Fourier transformed infrared (FTIR) spectroscopy. It was found that the absorbance peak at 626.4 cm-1 shifted to smaller wave numbers with the increase of implantation fluence, while on subsequent annealing the absorbance peak shifted back to larger wave numbers with the increase of annealing temperature. The shift of the peak at 626.4 cm-1 with He implantation/annealing is considered to be related with the trapping and release of helium atoms in lattice sites in the spinel crystal. 相似文献
3.
沿Si的(100)面注入He离子, 能量为30 keV、 剂量为5×1016 ions/cm2。 注入后样品切成几块, 在真空炉中分别做退火处理, 退火温度从600 ℃到1 000 ℃, 退火时间均为30 min。 利用原子力显微镜研究了各个样品表面形貌的演化。 发现样品表面形貌与退火温度相关联。 假设在气泡中He原子与空位的比值很高, 导致样品内部存在高压的He泡, 从而使样品表面形貌发生变化。 探讨了在Si中He泡随退火温度的演化和He原子在材料中的释放机制及其对表面的影响。 相似文献
4.
利用20 keV的He离子注入表面蒸镀了Au薄膜的尖晶石(MgAl2O4)样品, 随后对注入样品进行了退火处理。 在紫外可见光谱上观察到了由于金属纳米颗粒的存在而引起的较强的表面等离子体共振吸收峰, 提供了材料中金属纳米颗粒形成的光谱证据。 并对形成的Au纳米颗粒的尺寸随退火温度以及He注入剂量的变化进行了研究。 Spinel deposited with a thin Au film was implanted with helium ions, and annealed in vacuum condition subsequently. The surface Plasmon resonance absorbance peak due to the existence of metallic nanoparticles in the dielectric matrix was observed on the Ultraviolet Visible Spectrometry, indicating the formation of metallic nanoparticles in spinel. The dependence of Au particles size with annealing temperature and implantation doses was also investigated. 相似文献
5.
主要研究了铅离子辐照注碳4H—SiC样品在3个不同退火温度下傅立叶变换红外光谱的变化。从红外谱的变化可以知道铅辐照注碳4H-SiC样品在一定深度内出现了非晶层,波数在960—1450cm^-1范围内出现了干涉带,干涉带强度随着退火温度的升高而 变弱。1373K退火后样品的卢瑟福背散射分析结果显示,一定深度内硅原子的背散射产额明显减少。4H-SiC specimens were implanted with C-ions and then irradiated with Pb-ions, and subsequently annealed at three different temperatures. The samples were investigated by using Fourier transformation infrared spectrum(FTIR) and Rutherford backward scattering(RBS). The obtained FTIR spectra showed that there is a buried amorphous layer close to the ion-incident surface and there are several interference fringes in the range from 960 to 1 450 cm ^-1. The intensity of fringes decreases with the increase of annealing temperature. The obtained RBS spectra showed that the yield of Si atoms in 4H-SiC crystal decreases in a well-defined depth region after annealing at 1 373 K. 相似文献
6.
Single-crystalline Si (100) samples were implanted with 30 keV He2+ ions to doses ranging from 2.0×1016 to 2.0×1017ions /cm2 and subsequently thermally annealed at 800℃ for 30min. The morphological change of the samples with the increase of implantation dose was investigated using atomic force microscopy (AFM). It was found that oblate-shaped blisters with an average height around 4.0nm were found on the 2.0×1016 ions /cm2 implanted sample surface; spherical-shaped blisters with an average height around 10.0nm were found on the 5.0×1016 ions /cm2 implanted sample surface; strip-shaped and conical cracks were observed on the sample He-implanted to a dose of 1.0×1017 ions /cm2. Exfoliations occurred on the sample surface to a dose of 2.0×1017 ions /cm2. Mechanisms underlying the surface change were discussed. 相似文献
7.
利用高能离子研究了110 keV 的He+注入Al2O3单晶及随后230 MeV的208Pb27+辐照并在不同温度条件下退火样品的光致发光的特性. 从测试结果可以清楚地看到在375 nm,390 nm,413 nm 和450 nm 出现了强烈的发光峰. 经过600 K退火2 h后测试结果显示,390 nm发光峰增强剧烈,而别的发光峰显示不明显. 在900 K退火条件下,390 nm的发光峰开始减弱相反在510 nm出现了较强的发光峰,到1100 K退火完毕后390 nm的发光峰完全消失,而510 nm的发光峰相对增强. 从辐照样品的FTIR谱中看到,波数在460—510 cm-1间的吸收是振动模式,经过离子辐照后,吸收带展宽,随着辐照量的增大,Al2O3振动吸收峰消失,说明Al2O3振动模式被完全破坏. 1000—1300 cm-1之间为Al-O-Al桥氧的伸缩振动模式,辐照后吸收带向高波数方向移动. 退火后的FTIR谱变化不大. 相似文献
8.
9.
4H-SiC晶体经能量为100 keV,剂量为3×1016 cm-2的氦离子高温(500 K)注入后,再在773—1273 K温度范围内进行了退火处理,最后使用纳米压痕仪测量了样品注入面的硬度.测试结果表明,在500—1273 K温度范围内样品的硬度随退火温度升高呈现先增大后减小再增大的趋势,其中773 K退火样品的硬度增大明显.分析认为,退火样品的硬度变化是由退火过程中缺陷复合与氦泡生长导致样品内部的Si—C键密度、键长和键角改变引起的.
关键词:
SiC
注入
氦泡
纳米压痕 相似文献
10.
In the present work, a Cz-Silicon wafer is implanted with helium ions to produce a buried porous layer, and then thermally annealed in a dry oxygen atmosphere to make oxygen transport into the cavities. The formation of the buried oxide layer in the case of internal oxidation (ITOX) of the buried porous layer of cavities in the silicon sample is studied by positron beam annihilation (PBA). The cavities are formed by 15 keV He implantation at a fluence of 2×10^16 cm^-2 and followed by thermal annealing at 673 K for 30 min in vacuum. The internal oxidation is carried out at temperatures ranging from 1073 to 1473 K for 2 h in a dry oxygen atmosphere. The layered structures evolved in the silicon are detected by using the PBA and the thicknesses of their layers and nature are also investigated. It is found that rather high temperatures must be chosen to establish a sufficient flux of oxygen into the cavity layer. On the other hand high temperatures lead to coarsening the cavities and removing the cavity layer finally. 相似文献