Characterization of ZnO:AI films deposited by r.f.magnetron-sputtering at low temperature

Transparent conducting ZnO:AI thin films with good adhesion and Iow resistivity have been prepared on organic substrates and Coming 7059 glass substrates by r.f. magnetron-sputtering technique at Iow substrate temperature (25-210℃). Structural and photoelectric properties of the deposited films are investigated. The deposited films are polycrystalline with hexagonal structure and a preferred orientation with the c-axis perpendicular to the substrate. Only the (002) peak is observed.High quality films with resistivity as Iow as 1.0 x 10- 3Ω@ cm and 8.4 x 10- 4Ω@ cm, the average transmittance over 74% and 85% in the wavelength range of the visible spectrum have been obtained on different substrates.     

Light-Gradient-Induced Spiral Wave Drifts in a Belousov-Zhabotinsky Reaction

The dynamic behaviour of spiral tip in the light-sensitive Belousov-Zhabotinsky reaction under the influence of an externally applied light gradient was experimentally studied. The gradient causes different drifts for different spiral patterns. The centre of the spiral wave moved toward the region of lower light intensity. The direction of an additional perpendicular drift depended on the chirality of the spiral wave. The dependences of the drifting angle and the drifting velocity on light gradient have been measured.     

退火温度对低温生长MgxZn1－xO薄膜光学性质的影响

用射频磁控溅射法在80℃衬底温度下制备出Mg_xZn_1-xO(x=0.16)薄膜，用X射线衍射(XRD)、光致发光(PL)和透射谱研究了退火温度对Mg_xZn_1-xO薄膜结构和光学性质的影响.测量结果显示，Mg_xZn_1-xO薄膜为单相六角纤锌矿结构，并且具有沿c轴的择优取向；随着退火温度的升高，(002)XRD峰强度、平均晶粒尺寸和紫外PL峰强度增大，(002)XRD峰半高宽(F 关键词： xZn_1-xO薄膜')" href="#">Mg_xZn_1-xO薄膜 射频磁控溅射 退火     

Pseudo-Spin-Valve Trilayer Using Amorphous CoNbZr Layer： Giant Magnetoresistance, Domain Structures and Potentials for Spin-Electronic Devices

We propose a pseudo-spin-valve (PSV) trilayer using amorphous CoNbZr Mloy for soft magnetic layers. The giant magnetoresistance (GMR), domain structures and their variation upon thermal annealing are investigated. The GMR effect is not only stable up to 300℃ but also enhanced due to the improvement of the interfaces between Cu and magnetic layers. With high annealing temperature, the magnetoresistance (MR) ratio decreases rapidly as a result of serious layer interdiffusion. Dense stripe domains, which disappear after annealing at 300℃ for 1h, are observed in the sandwiched films. It is found that after patterning to elliptic stripe with aspect ratio of 6:1, the trilayers have a single domain and their MR ratio increases. The dynamic MR behaviour under an ac magnetic field indicates that the patterned stripes have good linear MR responses. Therefore, it is believed that the CoNbZr/Cu/Co PSV trilayers have strong potentials for spin-electronic devices including magnetic random access memory.     

X光光电子能谱法测定胶片中氟,硅和铝的研究

应用Ｘ光光电子能谱法测定了几种彩色胶片表面层中氟的１ｓ能级的结合能；分别比较了水处理前后、溅蚀前后胶片护膜层氟的变化，表明氟化物分布在护膜最表层，是一种易溶于水的氟化物；测定了彩色片护膜层所含硅２ｐ能级的结合能，与自制彩色片护膜层测定结果比较，优质片含一种较多负电性，用与自制片的无机硅不同的硅化物作毛面剂；对溅蚀前后优质片和自产彩色片中的硅铝比变化进行比较，提出优质彩色片Ｆ－４００的护膜层可能是双     

微波作用下乙酰苯胺的N—烷基化反应

探讨了在微波照射下，用相转移催化剂进行了乙酰苯胺的Ｎ－烷基化反应，该反应速度快，产率令人满意。     

三倍频激光等离子体X射线转换研究

利用“星光Ⅱ”高功率激光装置三倍频激光（波长０.３５μｍ,能量５—９０Ｊ,焦斑直径约２００μｍ,脉冲宽度４００—８００ｐｓ）辐照多种材料（Ｃ,Ａｌ,Ｃｕ,Ａｕ）靶,对于不同激光功率密度,研究软Ｘ射线转换和发射能谱．结合０.３５μｍ激光辐照Ａｌ靶的质量烧蚀率和等离子体喷射速度与激光功率密度的定标关系进行数值模拟,对于激光功率在１０^１３—１０^１５Ｗ／ｃｍ²理论模拟结果与实验结果符合得很好 关键词：     

The optical properties of MgxZnl-xO thin films

Mg_xZn_1-xO thin films have been prepared on silicon substrates by radio frequency magnetron sputtering at 60℃. The thin films have hexagonal wurtzite single-phase structure and a preferred orientation with the c-axis perpendicular to the substrates. The refractive indices of Mg_xZn_1-xO films are studied at room temperature by spectroscopic ellipsometry over the wavelength range of 400--760\,nm at the incident angle of 70℃. Both absorption coefficients and optical band gaps of Mg_xZn_1-xO films are determined by the transmittance spectra. While Mg content is increasing, the absorption edges of Mg_xZn_1-xO films shift to higher energies and band gaps linearly increase from 3.24.eV at x=0 to 3.90\,eV at x=0.30. These results provide important information for the design and modelling of ZnO/ Mg_xZn_1-xO heterostructure optoelectronic devices.     

Raman Spectroscopy of Nitrogen Clathrate Hydrates

在253 K和16 MPa的压力下,于实验室内合成了氮气水合物,用显微共焦拉曼光谱对其N-N和O-H键伸缩振动的光谱特征进行了研究．结果表明,氮气水合物中的N-N和O-H键的拉曼峰分别为2322.4和3092.1 cm^-1,与天然的空气水合物中的数据十分接近．另外,还测定了液氮和溶解于水中的氮分子中N-N键的拉曼峰值,分别为2326.6和2325.0 cm^-1．氮气笼型水合物分解的拉曼谱图表明,氮分子同时进入水合物的大笼和小笼中,但由于氮分子在大、小笼中的环境氛围十分接近,其拉曼位移相差不大,故拉曼谱图只能显示N-N键伸缩振动一个峰．     

高重复频率激光在非掺杂氧化铋玻璃中诱导TiO2晶体析出

使用聚焦后的800nm,150 fs,250 kHz的高重复频率飞秒脉冲激光研究它在非掺杂氧化铋玻璃内部三维选择性的诱导析晶.通过拉曼光谱测定发现析出的晶体是TiO2且为金红石相.研究表明,经过250 kHz的飞秒激光辐照一段时间后,玻璃内部由于脉冲能量的连续累积会使得激光辐照区域出现热累积效应,达到玻璃的析晶温度后诱导晶体析出.通过连续移动激光束,可以实现连续刻写TiO2晶线,通过EDX测试显示聚焦区域出现了由于热累积效应而形成热驱动使得离子发生迁徙.实验结果表明这种方法适用于在透明介质材料中三维选择性刻写晶体以制备集成光学器件.