LOW-TEMPERATURE HEAT CAPACITIES AND THERMODYNAMIC PROPERTIES OF LANTHANUM AND CERIUM TRIISOTHIOCYANATE HYDRATESI (Ⅰ)——La(NCS)_3, 7H_2O AND Ce(NCS)_3. 7H_2O

The heat capacities of La(NCS)_3. 7H_2O and Ce(NCS)_3. 7H_2O have been measured from 13 to 300K with a fully-automated adiabatic calorimeter. The construction and procedures of the calorimetric system are described in detail. No obvious thermal anomaly was observed for both compounds in the experimental temperature range. The polynomial equations for calculating the heat capacity values of the two compounds in the range 13—300K were obtained by the least-squares fitting based on the experimental C_p data. The C_p values below 13K were estimated by using the Debye and Einstein heat Capacity functions. The standard molar thermodynamic functions were calculated from 0 to 300K. Gibbs energies of formation were also calculated.     

稀土元素异硫氰酸盐水合物,RE(NCS)_3·nH_2O的低温热容和热力学性质的研究——Ⅰ.La(NCS)_3·7H_2O和Ce(NCS)_3·7H_2O

本文用全自动绝热量热计从13到300K测定了两种稀土元素异硫氰酸盐七水合物,La(NCS)_3·7H_2O和Ce(NCS)_3·7H_2O的热容。较详细描述了量热计结构和操作。在实验温区对两种化合物均未观察到明显的热异常现象。根据实验热容数据,用最小二乘拟合方法得到了计算这两种化合物13—300K热容值的多项式方程。13K以下的热容值用Debye和Einstein热容函数进行了估算。计算出了O—300K的标准热力学函数,标准生成Gibbs能也被计算出来。     

溅射气氛对RF反应磁控溅射制备ZnO薄膜微结构及光致发光特性的影响

用射频反应磁控溅射法在不同溅射压强和氩氧比下制备了ZnO薄膜,通过X射线衍射(XRD)、扫描电镜(SEM)和光致发光(PL)谱等研究了溅射压强和氩氧比对ZnO薄膜结构和光学性质的影响。测量结果显示,所制备的ZnO薄膜为六角纤锌矿结构,具有沿c轴的择优取向;溅射压强P=0.6Pa,氩氧比Ar/O2=20/5.5sccm时,(002)晶面衍射峰强度和平均晶粒尺寸较大,(O02)XRD峰半峰全宽(FWHM)最小,光致发光紫外峰强度最强。     

聚离子复合物单分子膜的聚集结构研究

LB膜在非线性光学材料、生物传感器等众多领域有着诱人的应用前景,受到了广泛的关注.为了充分发挥LB 膜的功能,必须制备高度取向、无缺陷的LB 膜,因此充分把握LB膜的构成单元单分子膜的聚集结构显得十分重要.由于气液界面离子复合结构的形成对单分子膜的聚集结构产生很大的影响,近年,有关这方面的工作越来越活跃.本文以探讨     

预应变对中碳钢扭转疲劳特性的影响

应用扭转疲劳试验机对退火后的非预应变45#钢及其3种预应变材料进行 实验. 实验结果表明：预应变量小于5%时,与非预应变材料相比疲劳极限降低10\%; 预应变量大于5{%}时,随着预应变量的增加,其疲劳极限有恢复的趋势,当预应变量达到 8%时,预应变材料与非预应变材料的疲劳极限几乎相等;当循环应力达到1*10^7$时,各种试件表面都有明显的停留裂纹存在.