Effect of CNT incorporation on PAN/PPy nanofibers synthesized by electrospinning method

In this study, carbon nanotubes (CNTs) added polyacrylonitrile/polypyrrole (PAN/PPy) electrospun nanofibers were produced. Average diameters of the nanofibers were measured as 268 and 153 nm for 10 and 25 wt% of PPy contents, respectively. A relatively higher strain to failure values (23.3%) were observed for the low PPy content. When as-grown CNTs (1 and 4 wt%) were added into the PAN/PPy blends, disordered nanofibers were observed to form within the microstructure. To improve the interfacial properties of CNTs/PAN/PPy composites, CNTs were functionalized with H₂SO₄/HNO₃/HCl solution. The functionalized CNTs were well dispersed within the nanofibers and aligned along the direction of nanofibers. Therefore, beads formation on nanofibers decreased. The impedance of the nanofibers was found to decrease with the PPy content and CNT addition. These nanofibers had a great potential to be used as an electrochemical actuator or a tissue engineering scaffold.     

Investigation of complexes tannic acid and myricetin with Fe(III)

The pH dependence of the complexes was determined by both potentiometric and spectrophotometric studies. Stability constants and stoichiometries of the formed complexes were determined using slope ratio method. Fe(III) was formed complexes with tannic acid of various stoichiometries, which in the 1:1 molar ratio at pH<3, in the 2:1 molar ratio at pH 3-7 and in the 4:1 molar ratio at pH>7. Fe(III) was formed complexes with myricetin in the 1:2 molar ratio at pH 4 and 5 and in the 1:1 molar ratio at pH 6. Stability constant values were found to be 10(5) to 10(17) and 10(5) to 10(9) for Fe(III)-tannic acid complexes and Fe(III)-myricetin complexes. Both tannic acid and myricetin were possessed minimum affinities to Cu(II) and Zn(II). They had less affinity for Al(III) than for Fe(III).