1.
采用自由基聚合法将共聚物接枝到多壁碳纳米管(MWCNT)上制备超疏水表面。结果表明,以α-甲基苯乙烯(AMS)与甲基丙烯酸丁酯(BMA)为单体,经自由基聚合可得到共聚物AMS-co-BMA(PAB),其热降解产物接枝到MWCNT表面可制得与水滴静态接触角为165°,滚动角小于3°的超疏水表面。SEM分析结果表明,共聚物的接枝一方面增大了管间的空隙,增加了表面粗糙度,另一方面又为降低表面能提供了条件。不同pH值液滴测试及放置时间的影响结果表明,该超疏水表面具有较好的稳定性和耐久性。 相似文献
2.
利用共沉淀-水热法制备了钴掺杂二氧化钛光催化剂,以催化降解水中草甘膦效率为指标,采用响应面法对钴掺杂二氧化钛光催化剂的制备条件进行优化。结果表明,钴掺杂二氧化钛光催化剂的最佳制备工艺为:水热反应温度139.64℃、水热反应时间23.75h、煅烧温度408.17℃和煅烧时间4.04h。利用最佳制备条件下制得的钴掺杂二氧化钛光催化剂催化降解水中草甘膦,降解效率接近80%,与纯二氧化钛相比,催化降解效率有较大幅度提升。 相似文献
3.
WANG Ling ZHANG Xiao-xia YUAN Hong-ming CHEN Yan DONG Zhong-ping PANG Guang-sheng FENG Shou-hua 《高等学校化学研究》2008,24(1):1-3
Cu2O particles with different morphologies and scales were prepared sonochemically on the solid-liquid interface of CuCl and water, by adjusting the reaction factors. The products were characterized by powder X-ray diffraction(XRD) and scanning electron microscopy(SEM). The formation and morphology of Cu2O crystals were influenced by high-intensity ultrasound, reaction temperature, and addition of CuCl. The results indicate that micrometer Cu2O was crystallized in cubic and octahedral shapes, whereas, nanometer Cu2O was not produced in well-shaped crystals. 相似文献
4.
采用实时红外光谱仪(RT-FTIR)研究了单体结构、单体配比以及活性稀释剂结构对樟脑醌(CQ)/胡椒环(BDO)引发的光聚合动力学的影响,结果发现,UDMA虽然黏度较低,但是易发生链转移反应且在聚合体系中含量较高(70 wt%),可作为氢给体猝灭激发态CQ,从而影响CQ和BDO之间的相互作用.Bis-GMA虽然黏度大,但是反应活性高,当其与少量具有给氢能力的活性稀释剂TEGDMA配合使用时,不仅对聚合体系的反应活性影响较小,而且可显著降低体系的黏度,大大提高自由基的活动能力,有利于改善CQ/BDO的引发活性. 相似文献
5.
HOU Ying SHI Zhan YANG Ming LI Guang-hua FENG Shou-hua State key Laboratory of Inorganic Synthesis Preparative Chemistry College of Chemistry Jilin University Changchun P. R. China 《高等学校化学研究》2005,21(4):406-410
IntroductionThe syntheses of metal-organic coordination poly-mers have been attracting increasing attention owing tothe potential applications of their functional materials incatalysis,non-linear optics,magnetism sensors andmolecular recognition[1—7].Coordination polymers crys-tallized from polyaromatic acids and metal-ions are ofgreat interest for their polymeric structures and porousproperties[8—12].Their network topologies based on mo-lecular building blocks are usually controlled and mod… 相似文献
6.
Single-phase Na5YSi4O12(NYS) was prepared by both conventional solid state reaction and sol-gel process. The formation of NYS was monitored by means of X-ray diffraction (XRD) and scanning electron microscope(SEM) techniques. The thermal stability of major impurity phases corresponding to different polymerization states of silicon was discussed. The conditions for preparing single-phase NYS ceramic with a high ionic conductivity were given. 相似文献
7.
8.
PENG Wen HU Bin CHEN Yan HU Wei-wei GUO Li YUAN Hong-ming FENG Shou-hua 《高等学校化学研究》2011,27(2):161-165
Pyrochlore titanate oxides, R2Ti2O7(R=Gd3+, Tb3+, Dy3+), were synthesized under mild hydrothermal conditions. The crystal growth of pyrochlore titanate oxides and taking place of chemical reaction in the hydrothermal processing were sensitive to the alkalinity, temperature, reaction time, the nature of the rare earth ion and the composition of initial reaction mixture. The as-prepared samples were characterized by powder X-ray diffraction, scanning electron microscopy, Raman spectrum and variable temperature dc magnetic susceptibility(SQUIDS). The magnetic studies gave 7.29×10–23 A•m2/Gd3+ and –8.28 K, 8.75×10–23 A•m2 /Tb3+ and –19.7 K, and 8.85×10–23 A•m2/Dy3+ and 0.84 K effective moments and Weiss constants for Gd2Ti2O7, Tb2Ti2O7 and Dy2Ti2O7, respectively. 相似文献
9.
YU Yang LIU Dan HU Wei-wei LI Jia PENG Yu ZHOU Qi YANG Fen LI Guang-hua SHI Zhan FENG Shou-hua 《高等学校化学研究》2012,28(2):186-190
Three metal molybdate hydrates,Fe(H2O)2(MoO4)2·H3O(FeMo),NaCo2(MoO4)2(H3O2)(CoMo)and Mn2(MoO4)3·2H3O(MnMo),were synthesized by the mixed-solvent-thermal methods and characterized by singlecrystal X-ray... 相似文献
10.
LI Min YUAN Hong-ming XU Wei HAN Mei YAO Lin-ran YANG Ming FENG Shou-hua 《高等学校化学研究》2012,28(5):788-791
A double perovskite oxide Ba2FeSbO6 was hydrothermally synthesized and structurally characterized by X-ray diffraction. This solid compound shows a single phase and has a trigonal structure with space group R m and cell parameters of a=0.57261 nm and c=1.40244 nm. The dielectric constant and loss tangent of the solid measured in a frequency range from 100 Hz to 1 MHz at temperatures from 313 K to 513 K reveal a relaxation process of frequency dependence of the real part(ε') of dielectric constant and dielectric loss tand. The frequency dependence of electrical property led to the framework of conductivity and electric modulus formalisms. The scaling behavior of imaginary part of electric modulus suggests that the relaxation describes the single mechanism at various temperatures. The variation tendency of the alternating current impedance indicates the thermally activated conduction process follows Jonsche’s power law. 相似文献