Performance evaluation of PVdF gel polymer electrolytes

A series of gel polymer electrolytes containing PVdF as homo polymer, a mixture of 1:1 Ethylene Carbonate (EC) : Propylene Carbonate (PC) as plasticizer and lithium-bistrifluoromethane sulphone imide [imide — LiN (CF₃SO₂)₂] has been developed. Amounts of polymer (PVdF), plasticizer and the imide lithium salt have been varied as a function of their weight ratio composition in this regard. Dimensionally stable films possessing appreciable room temperature conductivity values have been obtained with respect to certain weight ratio compositions. However, conductivity data have been recorded at different possible temperatures, i.e., from 20 °C to 65 °C. XRD and DSC studies were carried out to characterize the polymer films for better amorphicity and reduced glass transition temperature, respectively. The electrochemical interface stability of the PVdF based gel polymer electrolytes over a range of storage period (24 h – 10 days) have been investigated using A.C. impedance studies. Test cells containing Li/gel polymer electrolyte (GPE)/Li have been subjected to undergo 50 charge-discharge cycles in order to understand the electrochemical performance behaviour of the dimensionally stable films of superior conductivity. The observed capacity fade of less than 20% even after 50 cycles is in favour of the electrochemical stability of the gel polymer electrolyte containing 27.5% PVdF −67.5 % EC+PC −5% imide salt. Cyclic voltammetry studies establish the possibility of a reversible intercalation — deintercalation process involving Li⁺ ions through the gel polymer electrolyte.     

Fabrication of high performance thin films from metal fluorocomplex aqueous solution by the liquid phase deposition

The hetro-structured oxide thin films from metal fluorocomplex solution have been prepared by the liquid phase deposition (LPD) method. The Pt/Nb₂O₅ and Au/Nb₂O₅ composite films can be prepared from a mixed solution of niobium source, H₃BO₃, Pt(NH₃)₄Cl₂ and HAuCl₄ aqueous solutions under the ambient temperature and atmosphere. In the case of Au/SiO₂ composite film, (NH₄)₂SiF₆ solution is used as a mother solution. The Pt and Au ionic species are deposited in Nb₂O₅ and SiO₂ matrices. They are reduced to their metallic state after treatment above 200 °C. The size of dispersed particles can be controlled by heat treatment temperature. It is also clear that, gold nanoparticles are also found to interact with SiO₂, although the interaction is smaller than that with Nb₂O₅ showing the size of Au nanoparticles remain smaller in Nb₂O₅ that in SiO₂.     

Quest towards ultimate performance in superconducting nanowire single photon detectors

正In 2007,superconducting nanowire single photon detectors(SSPD or SNSPD)[1]made an outstanding impact in the field of quantum information technology by demonstrating quantum key distribution(QKD)over a 200-km optical fiber with a 42-dB optical loss using a practical SNSPD system[2].This successful demonstration was realized thanks to its extremely     

An effective noise removal technique for recovering the shapes of diamond abrasive grains in SLM images degraded by clustered spike noise

A new noise-removal technique is applied to scanning laser microscopic (SLM) images to remove clustered spike noise in the images and to recover the shapes of diamond abrasive grains degraded by the noise. For achievement of this purpose, noise points in the SLM image are accurately detected by taking advantage of their properties in the space and spatial-frequency regions. The noise points are removed by a method of smoothing that is based on linear interpolation; that is, their pixel values are replaced by the interpolated values of their non-noise neighboring points. Noise-point information in the space region is acquired from image segmentation based on pixel classification, while noise-point information in the frequency region is derived from redundant wavelet decomposition for the SLM image. Fisher's linear discriminant method is used to yield the two noise-point images. The degraded grain shapes in the SLM images at different noise levels are satisfactorily recovered with a single iteration of smoothing without losses in sharp edges although a single smoothing needed four interpolations. Thus, the present noise-removal technique is shown to be effective for recovering the original shapes of the grains in every SLM image.     

Complete assignment of the 1H and 13C NMR spectra of antimicrobial 4‐arylamino‐ 3‐nitrocoumarin derivatives

Herein, we describe the synthesis and complete assignment of the ¹H and ¹³C NMR chemical shifts of a series of antimicrobial 4‐arylamino‐3‐nitrocoumarin derivatives based on a combination of ¹H and ¹³C NMR, ¹H‐¹H‐COSY, NOESY, HSQC and HMBC experiments. Conformational effects upon the chemical shifts of the coumarin moiety arising from the anisotropy of the aryl side group are briefly discussed. This study provides the first complete and fully assigned NMR data for this important group of antimicrobial compounds and bridges the gap existing in the literature with regard to NMR structural data for 4‐arylamino‐3‐nitrocoumarins. Copyright © 2010 John Wiley & Sons, Ltd.     

Restoration of computed tomographic images degraded by poisson noise

A computer simulation was performed to restore the resemblance between a test object and the reconstructed image from projections with Poisson noise in the projection data. For this purpose, several smoothing techniques are applied for noisy raw data and the reconstructed image from the smoothed data. This results in appreciable improvements in resemblance.     

Protein-templated organic/inorganic hybrid materials prepared by liquid-phase deposition

Organic/inorganic hybrid thin films for protein recognition have been prepared by the liquid-phase deposition (LPD) coupled with template synthesis, i.e., molecular imprinting, where pepsin (Pep) was used as a model protein and titanium oxide was deposited on gold substrates in the presence of Pep-poly-L-lysine (PL) complexes. The complexes remained in the templated film after the deposition, and the binding sites for Pep were constructured after Pep was removed from the film. Surface plasmon resonance signals on the deposited films were measured to examine the binding behaviors toward proteins. The binding of Pep on the templated film was reversible, and the binding isotherm of Pep depicted a saturation curve with a binding constant of 7.3 x 105 M(-1), which was 10 times higher than that of albumin. In contrast, titanium oxide films prepared without PL did not show any selectivity; therefore, the hybridization of PL as the organic binder with the inorganic material is necessary to obtain selective binding sites for Pep. It was also shown that the hybridization process should proceed without denaturing the template protein, in order to obtain selective binding sites for the template. The procedure for preparation of the films was simple to perform, and the process for hybridization of the thin films with nanometer-order thickness was easily controlled by changing the LPD reaction time period. Consequently, the proposed LPD coupled with template synthesis is among the most appropriate methods to prepare hybrid materials with protein recognition ability, which proceeds under mild conditions in aqueous solution.     

Electroluminescence from Si quantum dots/SiO2 multilayers with ultrathin oxide layers due to bipolar injection

Si quantum dots/SiO₂ multilayers with ultrathin oxide layers (2.4 nm) were fabricated on a p-type Si substrate in order to enhance the hole injection. Besides the luminescence band at 900 nm which was also shown in photoluminescence spectra, another strong luminescence band near the infrared region (1200 nm) can be observed in electroluminescence spectra. It can be assigned to the band-edge emission from the quasi 2-dimensional potential well in the Si substrate. Moreover, it is interesting to find the reduction of photoluminescence intensity under biased conditions which can be attributed to the occurrence of non-radiative Auger recombination process in charged Si quantum dots.