Fabrication of Dendrimer－like PAMAM Based on Silica Nanoparticles

A G 4.0 dendrimer-like poly (amido amine) (PAMAM) based on silica nanoparticles was fabricated via a divergent approach.It was built from γ-aminopropyi silica nanoparfides (APSN) core via repetitive addition of acrylate (MA) and hexylenediamine (HDA). FT-IR and EA were used to monitor the progress of dendrimer during each step. The amino group content of the resulting product increased from 0.49 to 3.72 mmol/g after the 4th generation. In addition, the percentage of grafting increased with increasing generation and reached to 65.9% after 4th generation. It was found that the resulting silica nanoparticles could be dispersed in methanol with a mean hydrodynamic particle diameter of 152.7 nm although the silica nanoparticles had agglomerated during the storage period.     

纳米二氧化锆制备过程的DSC、TGA和XRD研究

用ＤＳＣ、ＴＧＡ和ＸＲＤ技术研究了在沉淀法制备纳米ＺｒＯ２的过程中，残留ＮＨ４Ｃｌ、ｐＨ值、滴加方式、以及结构稳定剂Ｙ２Ｏ３的添加量对结晶过程的影响。结果表明，残留ＮＨ４Ｃｌ使结晶化温度降低，使放热过程变为吸热过程。而ｐＨ值、滴加方式和结构稳定剂的添加对结晶过程无明显影响。     

球形SiO2-Al2O3的制备、结构和性能

将Na2SiO3·9H2O 溶液通过强酸性阳离子树脂进行离子交换得到酸性硅溶胶,再将硅溶胶与铝溶胶及六次甲基四胺混合后采用油柱成型法制备了球形SiO2-Al2O3复合氧化物. 通过XRD、BET 及TPD等手段对样品进行测试和表征, 结果表明, 600 ℃焙烧得到的SiO2-Al2O3中SiO2以无定型形式存在, 其比表面、孔容与表面酸性随SiO2含量的增加而提高, 孔径、堆密度随SiO2含量的提高而减小, 压碎强度基本保持不变.     

LaPO4纳米微粒的制备及表征

Surface-modified LaPO4 nanoparticales were synthesized in the mixture solvent of water-ethanol with the surface modification age of dialkylphosphate. The conditions of synthesis and characterization were discussed. The results indicated that nanoparticle core of LaPO4 and surface-modified layer were formed. The surface-modified nanoparticles of LaPO4 can be dispersed in organic solvent and has better lubricating properties.     

炸药爆炸法合成的纳米金刚石粉

综合介绍了用炸药爆炸法合成的金刚石粉的制备方法、性质和结构特点, 以及一些可能的应用途径。着重指出, 这种金刚石粉是由纳米尺寸的颗粒组成的一种金刚石新品种。     

表面修饰ZrO_2纳米微粒的结构表征及摩擦学行为研究(英文)

采用XPS,FTIR,DSC,TGA等多种现代分析手段表征了硬脂酸修饰ZrO2 纳米微粒的结构.在四球摩擦磨损试验机上,首次评价了表面修饰ZrO2 纳米微粒用作润滑油添加剂的摩擦学性能,结果表明ZrO2 纳米微粒具有良好的抗磨减摩性     

氧化锆陶瓷的摩擦磨损行为与机理

氧化锆陶瓷的工程应用前景广阔，在许多场合都必须与水或水溶液接触，但有关这种陶恣在水中的摩擦磨损行为和机理的研究报道不多见，而且已有的工作也不够深入。因此，对氧化锆陶瓷分别在水润滑和干摩擦下的摩擦学特性及其磨损机理进行了考察。     

高温固体润滑研究的现状及发展趋势

从高温固体润滑剂及高温自润滑材料等方面对高温固体润滑的研究现状进行了综述,并在此基础上提出了高温摩擦学领域的几个值得注意的问题。     

MOSi2及其复合材料摩擦学性能研究

通过热压烧结制备了MoSi2及3种MoSi2基复合材料，考察了其相组成和结构，测定了其硬度和断裂韧性，评价了其摩擦磨损行为，并探讨了力学性能、摩擦界面特性和偶件材料特性等对MoSi2及其复合材料摩擦学行为的影响．结果表明：MoSi2同GCrl5钢和WC-Co硬质合金配副时表现出较高的摩擦系数，其磨损强烈依赖于偶件材料特性；第二相的引入对MoSi2的磨损行为具有显著影响，其中SiC第二相可以改善MoSi2的摩擦磨损性能；摩擦界面特性和偶件材料特性则对MoSi2及其复合材料的摩擦磨损性能具有决定性影响．     

二硫化钼表面氧化行为的研究（Ⅱ）─—二硫化钼摩擦表面氧化与电子转移的研究

利用电子自旋共振谱和Ｘ射线光电子能谱研究了二硫化钼ＭｏＳ＿２摩擦表面的氧化和电子转移，发现ＭｏＳ＿２在摩擦过程中是以Ｍｏ￣（４＋）经由Ｍｏ￣（５＋）过渡态继而与氧作用生成稳定的Ｍｏ￣（６＋），并且是以ＭｏＯ＿３的形式存在，证明ＭｏＳ＿２的摩擦表面除有一般认为的Ｍｏ￣（４＋）和Ｍｏ￣（６＋）这两种化学状态以外，还有Ｍｏ￣（５＋）自由基离子这种从未发现的的中间态。Ｍｏ￣（５＋）是４ｄ￣１电子构型，其在室温下于空气或氧气中是稳定的，然而在摩擦环境或添加剂的作用下，Ｍｏ￣（５＋）所含不成对电子很容易发生转移而生成Ｍｏ￣（６＋），这种研究结果更加深入地揭示了ＭｏＳ＿２摩擦表面氧化过程的复杂性，因此，应当从摩擦化学角度重新认识ＭｏＳ＿２摩擦氧化产物及其形成机制，这于研究摩擦环境和添加剂对润滑剂的抗氧化协同效应具有重要意义。