研究了LiF为助熔剂体系下的δ-LiZnPO4的结晶特性,通过自发结晶得到了尺寸为1~3 mm的透明块状δ-LiZnPO4和Li4Zn(PO4)2共晶体,通过PXRD衍射分析和元素分析确定了共晶体的相组成,并对从共晶体中分离出的δ-LiZnPO4晶体结构进行了分析.结果表明:δ-LiZnPO4晶体具有非中心对称结构,属于正交晶系,空间群为Pna21,晶格常数a=1.00085 nm,b=0.49390 nm,c=0.66545 nm,Z=4;δ-LiZnPO4是由PO4、ZnO4和LiO4四面体构筑成的具有类似ABW型分子筛结构的化合物.采用水热法制备了尺寸约为10 μm的纯相透明的δ-LiZnPO4晶体.粉末倍频测试表明,δ-LiZnPO4晶体倍频效应约为KDP的1.7倍,紫外截止边约为218 nm,是一种有潜在应用价值的紫外非线性光学晶体. 相似文献
2.
β-LiZnPO_4 single crystal was successfully synthesized via hydrothermal method. It crystallizes in the trigonal space group R3 with a = b = 13.6490 ?, c = 9.1123 ?, γ = 120.00° and Z = 18. Structure of the crystal is constructed by LiO_4, ZnO_4 and PO_4 tetrahedral units to form a three-dimensional(3 D) framework. The crystal has a high transmission ranging from 350 to 800 nm with UV cut-off edge at 220 nm. The nonlinear optical efficiency of the as-prepared β-LiZnPO_4 is about 1.2 times as large as that of KDP(KH_2PO_4) standard. Additionally, band structure and density of states calculations for β-LiZnPO_4 were performed using the total-energy code CASTEP, based on density functional theory(DFT). 相似文献
3.
A potassium silicophosphate,K2SiP4O13,has been synthesized in molten polyphosphoric acid.It crystalizes in the triclinic space group P1-(No.2)with a=4.8327(10),b=7.7403(15),c=14.485(3)?,a=82.29(3)°,β=83.31(3)°,γ=81.95°,V=529.02(19)?3,Z=2.The crystallographic structure features 2D layers of[SiP4O13]∞in the ab plane with counter cations K+residing among the layers,and the anionic framework of[SiP4O13]∞is composed of six-fold coordinated Si atoms and tetraphosphate anions by sharing vertex O atoms.The title compound was characterized by powder X-ray diffraction,IR and Raman spectroscopies,UV-vis diffuse reflectance spectroscopy,thermogravimetry and differential scanning calorimetry. 相似文献
4.
采用提拉法生长出尺寸为φ25mm×40mm的透明Er^3+:KLa(WO4)2(简称Er:KLW)晶体,并确定了较佳的生长工艺。X射线粉末衍射分析结果表明该晶体为四方晶系白钨矿结构(I41/a空间群),晶格常数为a=b=0.5444(3)nm,c=1.2120(6)nm。测量了Er:KLW晶体的拉曼谱,发现了380,450和808cm^-1等钨酸根的特征振动峰。测量了晶体的吸收光谱,应用J-O理论计算了晶体中Er^3+离子的强度参量(Ω2,Ω4,Ω6);荧光光谱测量结果表明该晶体在1529nm附近有很强的荧光发射峰,利于产生受激辐射。 相似文献
5.
本文报道了一种新的硼酸盐化合物-Ba0.87Sr3.13B14O25,采用泡生法已生长出尺寸为35mm×25mm×5mm的晶体.该晶体为单斜晶系,C2/m空间群,a=1.6425(3)nr,b=0.77739(16)nm,c=1.6665(3)nm,β=119.22(3)°,Z=4.结构中B3O8六元环通过O原子和BO3三角形相互连接,构成三维的硼氧阴离子骨架,金属阳离子占据多面体间的空隙.测量了BSBO晶体的透过谱,该晶体的显微硬度为578kg/mm2. 相似文献