1
1.
A new nickel(Ⅱ)-dicyanamide compound, [Ni(dca)2(en)]n (1) (dca=dicyanamide anion, [N(CN)2]-); en=ethylene diamine), has been synthesized and its structure has been determined by single crystal X-ray diffraction analysis. The crystal is monoclinic, space group P21/n with unit cell dimensions: a=0.694 3(1) nm, b=1.041 5(2) nm, c=1.4132(2) nm, and β=90.381°, Z=4, V=1.011 0(3) nm3. In this compound, the adjacent nickel atoms are connected by dca all in μ1,5-bridging mode to form ladder-like units, which are linked with double dca bridges to generate a regular infinite stair-like structure. Temperature-dependent magnetic susceptibility was also characterized for this compound. CCDC: 208276. 相似文献
2.
以Al2O3和碳粉为原料,采用碳热还原法制备了AlN粉体,探讨了原料摩尔比、合成温度和保温时间等因素对AlN粉体合成的影响.通过XRD,SEM等测试对粉体进行了表征.在1650℃保温4h,合成出粒径约为1~5μm的纯AlN粉末,原料粒度越细越有利于AlN的生成,C/Al2O3摩尔比应略大于3.以石蜡为主粘结剂,通过热压铸成型方法成型AlN陶瓷散热罩素坯,经低温排胶、无压烧结工艺后得到高导热率AlN基陶瓷散热罩.研究了素坯排胶过程及陶瓷烧结过程的影响因素,排胶过程中缓慢升温至300℃,可避免素坯坍塌;排胶后素坯在1800℃无压烧结4h制得的AlN陶瓷LED散热罩密度为3.24 g/cm3,室温热导率高于100 W/m·K. 相似文献
3.
The reaction of L-histidine,CdCl2(2.5H2O and 4,4'-bipyridine in methane/water gave rise to a two-dimensional coordination polymer [CdCl2(4,4'-bipyridine)]( which has been characterized by single-crystal X-ray diffraction.The polymer crystallizes in the orthorhombic sys-tem,space group Cmmm with a = 12.083(7),b = 11.771(7),c = 3.781(2)(A),V = 537.8(6)(A)3,Z = 2,C10H8N2CdCl2,Mr = 339.48,Dc = 2.097 g/cm3,F(000) = 328 and μ(MoKα) = 2.490 mm-1.The final R = 0.0658 and wR = 0.1398 for 257 observed reflections with I≥2σ(I). 相似文献
4.
1 INTRODUCTION The design and synthesis of metal-organic coor- dination polymers are of current interest owing to their intriguing architectures and potential applica- tions, such as catalysis, fluorescence and magne- tism[1~4]. Many transition metal-organic polymers have been synthesized and exhibit interesting magneticproperties[5~9]. Among them, coordination polymers constructed by dicarboxylate ligands have attracted considerable attention due to their rich coordination modes and di… 相似文献
5.
A series of Bi3+-doped YAG:Ce3+, Mn2+ ceramics was synthesized successfully by gel-casting method and structurally characterized by XRD and SEM. The doping effect and related mechanism of Bi3+ upon the luminescent property were studied. It can be assigned to the energy transfer of multipolar interaction from Bi3+ to Ce3+, leading to the improvement of emission intensity about 58% for 0.0001 Bi3+ and 0.05 Mn2+ doping. In addition, the emission is significantly red-shifted with the peak at 590 nm for the Y2.9939 Ce0.006 Bi0.0001 Al4.96 Mn0.02 Si0.02 O12 ceramic specimen with in-line transmittance 81.6% at 1100 nm. The LED module assembled from Y2.9939 Ce0.006 Bi0.0001 Al4.96 Mn0.02 Si0.02 O12 ceramic owns correlated color temperature(CCT) of 3960 K and luminous efficiency(LE) of 92 lm/W, implying that doping Bi3+ shows a good sensitization effect in the YAG:Ce3+, Mn2+ ceramic system and further serving as an attracting phosphor candidates for warm WLEDs applications. 相似文献
6.
7.
Fe2AlB2 powder material was prepared by the direct reaction of iron,aluminum and boron powders in a tubular furnace.The effects of different Al contents,temperature and raw material pretreatment on the purity of product were studied.The mixed powder with the stoichiometric ratio of 1.5Al/2Fe/2B was processed by CIP (Cold Isostatic Pressing),and then calcined at 1150℃ for 120 min.The product containing a small amount of impurities is treated with alkaline solution to obtain high-purity Fe2Al B2 powder.Zr B2-Fe2Al B2 composite ceramic was successfully prepared at 1250℃ by hot pressing sintering.The density,hardness and fracture toughness were 96.2%,22±0.3 GPa and 5.78±0.5 MPa·m1/2,respectively. 相似文献