Spectra and lasing properties of Er~(3+),Yb~(3+):phosphate glasses

The effects of Al_2O_3, Yb_2O_3, Er_2O_3 and OH~- on spectral properties of P_2O_5.Na_2O.SrO.Al_2O_3.Yb_2O_3.Er_2O_3 erbium phosphate glass were studied. 5, 8, and 13 mol% Al_2O_3, 4, 5, 6, 7 and 8 mol% Yb_2O_3 and0.05, 0.2, and 0.4 mol% Er_2O_3 were used. It was found that Al_2O_3 can improve fluorescent lifetime ofEr~(3+)ions, but the integrated absorption cross section of Er~(3+)ions decreases with the increase of Al_2O_3concentration. Evaluating from energy transfer efficiency of Yb~(3+)to Er~(3+)and spectral parameters ofYb~(3+)and Er~(3+),we conclude that 6 mol% Yb_2O_3 and 0.4 mol% Er_2O_3 are needed for LD pumped     

光纤通信系统中偏振损耗对偏振态的影响

推导出具有偏振相关损耗(PDL)器件的Stokes模型,研究了光纤通信系统中PDL对光信号偏振态(SOP)的影响。数值模拟结果表明,入射信号光偏振度(DOP)小于1时,PDL对出射信号光的DOP和强度有直接影响;当入射光DOP等于1时,PDL对出射信号光的DOP没有影响,但随PDL的增加,出射光强度迅速减小,且信号光的SOP变化加剧。     

OH-对磷酸盐铒玻璃光谱性质的影响

本文系统研究了Yb³⁺、Er³⁺共掺磷酸盐铒玻璃中OH^-含量与铒玻璃荧光寿命和光谱性质的关系.结果表明OH^-基团的存在使得Er³⁺离子的荧光强度显著降低,荧光寿命大大缩短.比较了三种不同Al₂O₃含量(5mol%,8mol%和13mol%)的铒玻璃在2.9μm波长处的红外吸收系数与铒离子荧光寿命的关系,发现玻璃中OH^-在2.9μm的吸收系数和Er³⁺的⁴Ⅰ_13/2能级离子衰减速率成线性关系,不同Al₂O₃含量的玻璃具有不同Er³⁺和OH^-基团的相互作用参量和不同的荧光寿命值及量子效率.并从玻璃结构上解释了Al₂O₃含量对除水机制和光谱性质的影响.经过充分除水后的铒玻璃荧光寿命可达到9.1ms.     

Cr3+,Yb3+,Er3+共掺磷酸盐铒玻璃转镜调Q激光性质研究

研究了Cr³⁺,Yb³⁺,Er³⁺共掺磷酸盐铒玻 璃转镜调Q激光性质.三种Er₂O₃掺杂浓度的激光实验结果表明，在Er₂O₃名义掺杂浓 度为0.5wt％时，玻璃的综合激 光性质最好，重复频率为0.1Hz时，它的激光阈值功率为14.5mJ，最大输出能量为9.6mJ ，斜率效率为0.55％.在同种实验条件下，比较了Cr14和Kigre公司生产的QE-7S激光性质参数，实验表明，前者激光阈值功率稍低，而后者的斜率效率和最大输出功率略高. 关键词： 3+-Yb³⁺-Er³⁺共掺')" href="#">Cr³⁺-Yb³⁺-Er³⁺共掺 磷酸 盐玻璃 光谱性质 激光性质     

Yb~(3+),Er~(3+)共掺磷酸盐铒玻璃光谱性质研究

研究了Yb3+ ,Er3+ 共掺磷酸盐铒玻璃的吸收光谱和荧光光谱性质。通过测定和计算各种Yb3 + ,Er3 + 共掺磷酸盐铒玻璃光谱参数 ,初步探明了Yb3+ 离子浓度、碱金属氧化物R2 O(R =Li,Na ,K)和碱土金属氧化物MO(M =Zn ,Mg ,Ca,Ba)的引入及网络生成体P2 O5 的含量对Yb3 + ,Er3 + 共掺磷酸盐铒玻璃光谱性质的影响。在Yb3+ ,Er3+共掺磷酸盐铒玻璃中实现了Er3+ 荧光寿命达 7 5ms,受激发射截面为 0 8× 10 - 2 0 cm2 的光谱特性 ,为今后该玻璃的激光实验提供了重要参数     

Spectroscopic properties of Er~(3+)-doped AlF_3-La_2O_3-Al_2O_3-SiO_2 glasses

Er~(3+)-doped fluoride lanthanum aluminosilicate glasses with compositions of (65-x/2)SiO_2·(25-x/2)Al_2O_3·xAlF_3·9.1La_2O_3·0.6Er_2O_3·0.3Yb_2O_3(x=4, 8, 12, 20, 30) (mol%) were prepared and their glass transition temperatures and spectroscopic properties were investigated.The Ω_2, Ω_4, and Ω_6 intensity parameters of glasses were calculated by Judd-Ofelt theory from absorption curves. It was found that glasses transition temperature and melting temperature decreased with the increase of fluoride content in glass,Ω_2 decreased gradually with the increase of AlF_3 content,but both Ω_4 and Ω_6 did not increase until AlF_3 content increased to 30 mol%.The quantum efficiency of ~4I_(13/2) to ~4I_(15/2) transition of Er~(3+) ions increases with the increase of AlF_3 content in glass.Fluorescent lifetime is longer in glass containing more AlF_3 content.     

铽镓石榴石单晶的生长、表征及其挥发机理研究

使用预先烧结好的多晶原料,在一定比例的N2和CO2混合气氛下,采用提拉法生长出了高质量的铽镓石榴石(TGG)单晶.采用XRD、ICP和热力学计算进行分析,结果表明,晶体生长过程中的挥发机制为Tb3Ga5O12的分解,分解产物为Tb3 GaO6,Ga2O和O2.CO2被Ga2O还原产生O2,抑制了Tb3Ga5O12的分解.TGG单晶的化学分子式存在Tb富集或Ga缺失,为Tb3Ga4.4～4.5O11.1～11.3非化学计量比相.将晶体毛坯加工成φ2.8 mm×10.7 mm的晶棒,消光比测试结果表明镀增透膜后消光比平均可提高18.8 dB.     

TSTGT蓝宝石晶体位错腐蚀形貌分析

采用化学腐蚀-金相显微镜法,利用熔融的KOH对顶部籽晶温度梯度法(TSTGT)生长的直径320 mm的蓝宝石单晶中不同部位的晶片做了位错腐蚀形貌分析.研究表明,(0001)面的位错腐蚀坑呈三角形,腐蚀晶界具有延伸性.对比不同腐蚀时间、不同腐蚀温度和不同表面粗糙度下的腐蚀效果,发现使用KOH腐蚀剂在400℃腐蚀15min时,效果最好.表面粗糙度越小,位错图像越清晰.     

Yb3+,Er3+离子共掺磷酸盐铒玻璃的Judd-Ofelt光谱参数与光谱性质

研究了含Er3+离子浓度较高(155×1020cm-3)的磷酸盐玻璃中Yb3+敏化离子浓度和Al2O3含量对Er3+离子光谱性质的影响.根据掺Er3+磷酸盐玻璃的吸收光谱,利用JuddOfelt理论计算了强度参数Ωt(t=2,4,6)、Er3+离子的4I132→4I152能级跃迁振子强度、自发辐射几率等光谱参数.用McCumber理论计算了Er3+离子的受激发射截面,结果表明Yb3+离子浓度不影响Er3+离子的受激发射截面,但会影响Er3+离子荧光强度,Yb3+含量越高,Er3+的荧光越强.对掺Er3+磷酸盐玻璃的荧光上转换光谱测试表明,Yb3+含量越高,上转换荧光越强,玻璃上转换主要表现为双光子吸收机理研究了含Er3+离子浓度较高(155×1020cm-3)的磷酸盐玻璃中Yb3+敏化离子浓度和Al2O3含量对Er3+离子光谱性质的影响.根据掺Er3+磷酸盐玻璃的吸收光谱,利用JuddOfelt理论计算了强度参数Ωt(t=2,4,6)、Er3+离子的4I132→4I152能级跃迁振子强度、自发辐射几率等光谱参数.用McCumber理论计算了Er3+离子的受激发射截面,结果表明Yb3+离子浓度不影响Er3+离子的受激发射截面,但会影响Er3+离子荧光强度,Yb3+含量越高,Er3+的荧光越强.对掺Er3+磷酸盐玻璃的荧光上转换光谱测试表明,Yb3+含量越高,上转换荧光越强,玻璃上转换主要表现为双光子吸收机理 关键词： Er3+离子 磷酸盐玻璃 光谱性质 JuddOfelt参数     

Cr3+,Yb3+,Er3+共掺磷酸盐铒玻璃中Ce3+和Cr3+离子对光谱性质的影响

研究了 Cr3+ ,Yb3+ ,Er3+共掺磷酸盐铒玻璃的吸收光谱和荧光光谱性质。通过测定和计算各种 Cr3+ ,Yb3+ ,Er3+ 共掺磷酸盐铒玻璃的光谱参数 ,初步探明了 Ce3+ 和 Cr3+ 离子浓度含量对 Cr3+ ,Yb3+ ,Er3+ 共掺磷酸盐铒玻璃光谱性质的影响。结果表明 ,Ce O2 含量为 2 .8mol- %,Cr2 O3含量为 0 .0 8wt.- %玻璃的光谱性质较好。Ce3+ 离子价态的变化也对玻璃的光谱性质有重要影响。 Ce3+ 离子的存在更有利于对抽运光的吸收和能量的传递。在 Cr3+ ,Yb3+ ,Er3+共掺磷酸盐铒玻璃中实现了 Er3+荧光寿命达 8m s,受激发射截面为 0 .8× 1 0 - 2 0 cm2的光谱特性 ,为今后该玻璃的激光实验提供了重要参数。