纳米β-Ni(OH)2与球型Ni(OH)2的热性能比较研究

用配位沉淀法合成出纳米级Ni（OH）2，并对其进行XRD，TEM，DSC分析，分析结果表明，所得纳米β-Ni（OH）2为可用作电极材料的β-Ni（OH）2，粒径为30－40nm，且热分解温度比普通球镍低10℃左右，摩尔分解热比普通球镍低4－7kJ，从理论上分析了产生此现象的原因。     

THERMODYNAMIC ANALYSIS AND FORMATION ENTHALPY CALCULATION OF OXYGEN VACANCY DEFECT IN DOPED LITHIUM NIOBATE CRYSTALS

Based on the thermodynamic analysis of oxygen vacancy defects in lithium niobate (LiNbO₃ (LN)) and the data of thermogravimetric experiment, the formation enthalpies of congruent and several rare-earth (RE) doped LN crystals have been calculated. It was found that the formation enthalpy of oxygen vacancies can be decreased evidently by doping with valence-changeable RE ions. The experimental results were discussed and a new reduction process for photorefractive LN crystals at a relatively low temperature was proposed, and the reduction-treated crystals showed good effect in practical use.     

光折变LiNbO3晶体在Li2CO3粉末中的还原

利用吸收光谱和Ｘ射线粉末衍射，对ＬｉＮｂＯ＿３晶体在Ｌｉ２＿ＣＯ＿３粉末中的还原过程进行了分析和研究，认为其中Ｌｉ￣＋离子在晶格中的扩散迁移是造成还原过程发生的一个重要因素。由此导致的可能的吸收光谱和晶格常数的变化，与实验结果完全符合。     

国外普通化学教材及其课程的特点

本文对一些国外普通化学教材和教学计划进行了分析研究 ,从教材内容、教材的表现形式以及教学方法等方面总结出国外普通化学教材及其课程的特点     

Pb1-xLaxTi1-x/4O3纳米晶的结构

改性钛酸铅;制备;晶胞常数;XRD;Pb1-xLaxTi1-x/4O3纳米晶的结构     

纳米级β-Ni(OH)2电极材料的制备

采用均相沉淀法使ＮｉＣｌ_2溶液与沉淀剂ＮａＯＨ反应,制备出纳米级Ｎｉ（ＯＨ）_2超微粉末。用ＸＲＤ检测,证实其为电极用β－Ｎｉ（ＯＨ）_2,用ＴＥＭ对样品进行形貌分析,结果表明,所得产物为不规则的颗粒状的纳米晶,粒径为 ２０～４０ ｎｍ。研究还初步探讨了沉淀剂浓度、反应温度、配合剂用量等实验参数对纳米粉组成和结构的影响。并应用正交实验法,对工艺条件进行了优化。将制备出的纳米级Ｎｉ（ＯＨ）_２按一定比例掺入普通的球型微米级Ｎｉ（ＯＨ）_２中,充放电测试结果表明,比容量可增加约１０％。     

Ce：Fe：LiNbO_3晶体的生长及其二波耦合效应的研究

本文介绍了Ｃｅ：Ｆｅ：ＬｉＮｂＯ＿３晶体的生长，测试了晶体的二波耦合指数增益系数和衍射效率，它具有很高的指数增益系数和衍射效率并且具有温度增强效应。