激光重熔工艺参数对热障涂层热震性能的影响

在GH536高温合金基材上等离子喷涂氧化钇部分稳定氧化锆(8YSZ)热障涂层后,采用连续CO2激光进行表面陶瓷层激光重熔,得到了表面形貌、组织结构符合质量要求的涂层。热震试验结果表明,在本试验的失效判据下,等离子喷涂及激光重熔试样的失效形式和机理不同,等离子喷涂试样为热震应力失效,激光重熔试样以热震应力和TGO应力共同作用形式失效。激光能量密度为4.0J/mm2时,激光重熔试样具有略高于等离子喷涂试样的热震寿命,当激光能量密度较高时,激光能量分布不均导致的组织及结构的不均匀,柱状晶粗化是能量密度较高的表征,扩展到喷涂态陶瓷层中的裂纹是激光重熔试样热震寿命降低的主要原因。     

COLORATION EFFECT OF PULSED LASER ON WO3

When laser pulses irradiate the surface of the sample WO₃, an interesting coloration effect is obtained. Only by one pulse of XeCl laser irradiation (wavelength: 308 nm, pulse duration: 36 ns, output power: 100 mJ/pulse), a significant color change appears. X-ray photoelectron spectroscopy (XPS) shows that a partial reduction process of WO₃ occurs and conduction band electrons appears. X-ray diffraction pattern indicates that the lattice parameters of the colored samples are increased. A molten layer can be seen in scanning electron microscopy (SEM) image. It may be concluded that the coloration effect of pulsed laser undergoes a process different from that of electro- or photo- chromism, and may be attributed to thermochromism and substoichiometric WO₃ is formed. The coloration process is characterized by its high speed and stability.     

激光重熔处理工艺对等离子喷涂热障涂层组织的影响

研究了激光不同工艺参数对等离子喷涂ＺｒＯ２热障涂层组织结构的影响,结果表明：随着激光输出功率的增大,重熔组织由单一柱晶结构变为等轴晶＋柱晶双层结构。ＺｒＯ２层最高显微硬度也随之增大,这与等轴晶的存在有关。对两种不同晶体相结构进行ＸＲＤ分析表明：柱晶结构表现出一定的择优取向。     

Al2O3陶瓷表面的准分子激光活化沉积金属Cu技术

本文研究了通过ＸｅＣｌ准分子激光照射Ａｌ２Ｏ３陶瓷表面后,使其表面沉积金属Ｃｕ的技术,实验结果表明,Ａｌ２Ｏ３试样浸入Ｃｕ２ＳＯ４溶液后,金属Ｃｕ膜只沉积于激光照射区。经准分子激光照射,Ａｌ２Ｏ３表面结构的变化和Ａｌ富集区的产生是金属Ｃｕ沉积的主要原因。     

脉冲激光溅射沉积PZT膜

利用脉冲激光溅射沉积ＰＺＴ压电陶瓷薄膜。着重研究了制备过程对膜层成分和结构的控制。     

COLORATION EFFECT OF PULSED LASER ON WO3

When laser pulses irradiate the surface of the sample WO₃, an interesting coloration effect is obtained. Only by one pulse of XeCl laser irradiation (wavelength: 308 nm, pulse duration: 36 ns, output power: 100 mJ/pulse), a significant color change appears. X-ray photoelectron spectroscopy (XPS) shows that a partial reduction process of WO₃ occurs and conduction band electrons appears. X-ray diffraction pattern indicates that the lattice parameters of the colored samples are increased. A molten layer can be seen in scanning electron microscopy (SEM) image. It may be concluded that the coloration effect of pulsed laser undergoes a process different from that of electro- or photo- chromism, and may be attributed to thermochromism and substoichiometric WO₃ is formed. The coloration process is characterized by its high speed and stability.