Temperature scaling of ferroelectric hysteresis in hard lead zirconate titanate bulk ceramic

The temperature scaling of the ferroelectric hysteresis was investigated in hard lead zirconate titanate (PZT) bulk ceramic. The power-law temperature scaling relations were obtained for hystersis area 〈A〉, remnant polarization P_r, and coercivity E_C in the forms of 〈A〉∝T^-0.9650, P_r∝T^-0.0261, and E_C∝T^-0.8823, respectively, which are mostly comparable to those of its soft counterpart. The observation that P_r decayed more slowly with temperature than in soft PZT was attributed to the presence of the complex defects in hard PZT. However, the product of P_r and E_C still provided the similar scaling law on the T dependence in comparison with 〈A〉. PACS 77.80.-e; 77.80.Fm; 77.84.-s; 77.84.Dy     

Crystal structure and ferroelectric properties of Mn-doped ((Ka0.5Na0.5)0.935Li0.065)NbO3 lead-free ceramics

In this study, ceramics in Mn-doped ((Ka_0.5Na_0.5)_0.935Li_0.065)NbO₃ ceramics (Mn content = 0.25, 0.50, 1.00 and 1.50 mol%) were successfully prepared by the conventional mixed-oxide technique. The crystal structure was identified by XRD as a single-phase perovskite structure with tetragonal symmetry. The valence of Mn ions, characterized by the synchrotron XAS technique, was seen to change from Mn⁴⁺ to Mn³⁺ during the formation of the crystal. The valence state of Mn strongly affected the crystal structure and ferroelectric properties of the ceramics. The ferroelectric parameters show the decrease of remnant polarization and the increase of the coercive field with increasing MnO₂ content. The results confirm the Mn³⁺ in KNNL perovskite lattices, leading to the formation of oxygen vacancies and hardening effects.     

A Rhodamine‐based Fluorescent Chemodosimeter for Au3+ in Aqueous Solution and Living Cells

Journal of Fluorescence - A highly selective rhodamine hydrazide-based fluorescent chemosensor for Au3+ detection was developed. The aqueous solution of rhodamine N-hydroxysemicarbazide (RHS), in...     

Carbon encapsulated nickel nanoparticles synthesized by a modified alcohol catalytic chemical vapor deposition method

In this work, a simple and cost-efficient method was demonstrated for the production of carbon encapsulated nickel nanoparticles (CENPs). The CENPs were synthesized from nickel oxide by a modified alcohol catalytic chemical vapor deposition method at atmospheric pressure. Structural characterizations using scanning electron microscopy, transmission electron microscopy and X-ray diffraction indicated that the Ni-core mean diameter and the graphite-layer mean thickness were 98 ± 31 nm and 65 ± 35 nm, respectively. Room temperature magnetization results showed a ferromagnetic behavior of the CENPs, in which the saturation magnetization decreased with decreasing the Ni-to-C ratio whereas the coercivity increased with decreasing the Ni-core diameter.     

Changes in ferroelectric properties of lead indium niobate-lead titanate ceramics under compressive stress applied perpendicular to an electric field

The influences of perpendicular compressive stress on the ferroelectric properties of (1−x)Pb(In_1/2Nb_1/2)O₃-xPbTiO₃ (x=0.1-0.4) ceramics were investigated in this study. In general, with increasing compressive stress the coercive field and the dissipation energy of the ceramics were seen to increase. The stress-induced changes in the polarization, however, depended significantly on ceramic compositions. The observations were mainly interpreted in terms of competing influence of the domain switching through non-180° domain walls, clamping of domain walls, and the stress-induced decrease in the switchable part of spontaneous polarization.