Synthesis of nano-polycrystalline diamond from glassy carbon at pressures up to 25 GPa

ABSTRACT

Nano-polycrystalline diamond (NPD) with various grain sizes has been synthesized from glassy carbon at pressures 15–25?GPa and temperatures 1700–2300°C using multianvil apparatus. The minimum temperature for the synthesis of pure NPD, below which a small amount of compressed graphite was formed, significantly increased with pressure from ～1700°C at 15?GPa to ～1900°C at 25?GPa. The NPD having grain sizes less than ～50?nm was synthesized at temperatures below ～2000°C at 15?GPa and ～2300°C at 25?GPa, above which significant grain growth was observed. The grain size of NPD decreases with increasing pressure and decreasing temperature, and the pure NPD with grain sizes less than 10?nm is obtained in a limited temperature range around 1800–2000°C, depending on pressure. The pure NPD from glassy carbon is highly transparent and exhibits a granular nano-texture, whose grain size is tunable by selecting adequate pressure and temperature conditions.     

Preparation and properties of the biodegradable graded blend of poly(L‐lactic acid) and poly(ethylene oxide)

We prepared biodegradable poly(ethylene oxide) (PEO)/poly(L ‐lactic acid) (PLLA) graded blends by the dissolution–diffusion process, and discussed the biodegradability and tensile strength of the graded blends by comparing isotropic blend and PLLA only. All the graded blends were degraded more largely than the PLLA only and isotropic blend (PEO: 37.5 wt %), which had the same content as the total content of those graded blends. The graded blend having most excellent wide compositional gradient was degraded most largely with the enzyme. Thus, graded structure of the blends promoted their biodegradabilities large. It was considered that the dissolution of PEO with water increased the surface area attacked by the enzyme, while PEO caught PLLA oligomers to promote the biodegradation of PLLA. Then, the biodegradabilities of the graded blends were suppressed by the increasing crystallinity of PLLA. Furthermore, the strengths of all the graded blends were larger than those of the isotropic blend. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2972–2981, 2007     

Hyperspaces of Normed Linear Spaces with the Attouch–Wets Topology

Let Cld _AW (X) be the hyperspace of nonempty closed subsets of a normed linear space X with the Attouch–Wets topology. It is shown that the space Cld _AW (X) and its various subspaces are AR's. Moreover, if X is an infinite-dimensional Banach space with weight w(X) then Cld _AW (X) is homeomorphic to a Hilbert space with weight 2 ^w(X).     

Enhancement of Magneto-Optic Effect in Optical Isolator with Semiconductor Guiding Layer by Selective Oxidation of AlInAs

Selective oxidation of an AlInAs layer was investigated for enhancement of magneto-optic effect in an optical isolator. Twelve times nonreciprocal phase shift enhancement was estimated from a measured AlInAs-oxide refractive index.     

Endoscopic Observation of Tissue by Narrowband Illumination

We propose a new illumination method for a medical endoscope: narrow band imaging (NBI), in which the spectral bandwidth of the filtered light is narrowed. To confirm how the spectral specifications of the filtered light influence a reproduced image, an experiment was conducted observing the endoscopic images of the back mucosa of a human tongue. In addition, the effect of NBI on endoscopic images was investigated through preliminary clinical tests in colonoscopy and upper gastrointestinal endoscopy. It has been shown that NBI can enhance the capillary pattern and the crypt pattern on the mucosa. These patterns are useful features for diagnosing an early cancer.     

Application of novel SIMS technique for imaging the active sites of oxygen reduction at the SOFC cathode/electrolyte interfaces

The oxygen reduction active sites were visualized around the O₂/SOFC cathode/electrolyte triple phase boundaries (TPB) by the¹⁶O/¹⁸O exchange techniques and secondary ion mass spectrometry (SIMS) analysis. The higher¹⁸O concentration is observed on the cathode top surfaces (La_0.9Sr_0.1MnO₃-mesh, Au-mesh, and Ag-porous), which suggested the promotion of oxygen adsorption and oxygen surface exchange at the cathode. The oxygen diffusion through the bulk of cathode occurred at the La_0.9Sr_0.1MnO₃-mesh and the Ag-porous cathodes, not at the Au-mesh cathode. On the YSZ surfaces after removing the cathode, the active sites for oxygen incorporation were analyzed by SIMS. The active sites for oxygen incorporation were at the La_0.9Sr_0.1MnO₃/YSZ interface as well as the TPB. On the other hand, the active sites for oxygen incorporation are limited to the TPB in the case of the Au-mesh removed YSZ surface. From the SIMS analysis, the expansion of the active sites for oxygen incorporation is less than a few μm from the TPB lines. Paper presented at the 8th EuroConference on Ionics, Carvoeiro, Algarve, Portugal, Sept. 16–22, 2001.     

Successive phase transitions of [(PyO)(H/D)][AuCl4] (PyO=C5H5NO)

³⁵Cl NQR as well as heat capacity measurements of [(PyO)H][AuCl₄] and its deuterated analog [(PyO)D][AuCl₄] revealed successive phase transitions at 70.5 and 62.5 K, and at 71 and 63 K, respectively. The NQR frequency varied continuously through the upper transition point while discontinuously through the lower transition point. In the intermediate-temperature phase a remarkable decrease in the signal intensity was observed. These NQR observations as well as the feature of the heat capacity anomaly in which a broad peak is succeeded by a sharp peak with decreasing temperature suggest a possibility of normal-incommensurate-commensurate phase sequence.     

Performance evaluation of PVdF gel polymer electrolytes

A series of gel polymer electrolytes containing PVdF as homo polymer, a mixture of 1:1 Ethylene Carbonate (EC) : Propylene Carbonate (PC) as plasticizer and lithium-bistrifluoromethane sulphone imide [imide — LiN (CF₃SO₂)₂] has been developed. Amounts of polymer (PVdF), plasticizer and the imide lithium salt have been varied as a function of their weight ratio composition in this regard. Dimensionally stable films possessing appreciable room temperature conductivity values have been obtained with respect to certain weight ratio compositions. However, conductivity data have been recorded at different possible temperatures, i.e., from 20 °C to 65 °C. XRD and DSC studies were carried out to characterize the polymer films for better amorphicity and reduced glass transition temperature, respectively. The electrochemical interface stability of the PVdF based gel polymer electrolytes over a range of storage period (24 h – 10 days) have been investigated using A.C. impedance studies. Test cells containing Li/gel polymer electrolyte (GPE)/Li have been subjected to undergo 50 charge-discharge cycles in order to understand the electrochemical performance behaviour of the dimensionally stable films of superior conductivity. The observed capacity fade of less than 20% even after 50 cycles is in favour of the electrochemical stability of the gel polymer electrolyte containing 27.5% PVdF −67.5 % EC+PC −5% imide salt. Cyclic voltammetry studies establish the possibility of a reversible intercalation — deintercalation process involving Li⁺ ions through the gel polymer electrolyte.