Vinylic polymerization of Norbornenecarboxylic Acid Esters by Palladium Complexes

In recent years certain new technologies demand optically transparent high Tgpolymer materials.Some aliphatic polymers containing cyclic structure are in the marketalready and have been applied to manufacture various devices in optics industry.However,these polymers are usually of nonpolar character and their difficulties inadhesion and solubility in solvents limited their applicability in many technologies[1 ,2 ] .The polymerization of polar group-containing internal cyclic olefins by transit…     

BaLaB_9O_(16)∶Eu,Tb的真空紫外光谱特性

采用高温固相反应法合成了BaLaB9O1 6 ∶RE (RE =Eu ,Tb)等离子荧光体 ,测量了它们的真空紫外激发光谱和 14 7nm激发下的发射光谱。结果表明 ,硼氧阴离子基团基质吸收带位于 15 0nm附近 ,Eu3 电荷迁移带位移 2 5 0nm附近 ,Tb3 的 4f 5d吸收位于 15 0～ 2 60nm的区域内 ,相关数据表明 ,基质与稀土离子之间存在能量传递。     

Eu~(3 )在CaYBO_4中的取代和发光

用固相法制备化合物CaY1 -xBO4∶xEu ,研究Eu3 在CaYBO4中的取代格位和发光特性。当Eu3 掺杂浓度不大时 ,存在两个发光中心 ,认为是取代基质中有两个Y格位的结果 ;通过对Eu O的电荷迁移激发带位置的分析 ,表明Eu3 所处八面体中心格位的对称性越低 ,Eu O的电荷迁移带越偏向于短波 ;当Eu3 的掺杂浓度较大 (x >0 1 0 )时 ,Eu3 离子也可占据Ca2 格位 ,同时Eu3 还原成Eu2 。     

Y1.95-xGdxSiO5:Eu0.05的真空紫外光谱

利用高温固相法合成了Ｙ１．９５－ｘＧｄｘＳｉＯ５：Ｅｕ０．０５（ｘ＝０．６ｍｏｌ％）荧光体。结构测定表明所合成的荧光体为单斜晶系的Ｘ２型Ｙ２ＳｉＯ５相,空间群为Ｂ２／ｂ。真空紫外光谱表明：随着Ｇｄ＾３＋含的增加,在１９２ｎｍ附近,出现了Ｇｄ＾３＋的激发峰,且此峰的强度随着Ｇｄ＾３＋含量的增加而增在;同时位于１５０￣１８５ｎｍ之间的基质吸收带的强度也增大;而位于２００￣３００ｎｍ之间的Ｅｕ的电荷迁移     

The effects of external optical feedback on the power penalty of DFB-LD modules for 2.5Gbs−1 optical transmission systems

We report the effects of external optical feedback on the power penalty of commercial distributed feedback laser diode (DFB-LD) modules for 2.5Gbs–1 optical transmission systems. External optical feedback presented to the DFB-LD modules causes the excitation of external cavity modes, resulting in increased relative intensity noise (RIN) and intensity noise ripples at low frequency region below 500MHz. For a 10–10 bit error rate (BER), the minimum power penalty is as much as 1.25dB for a feedback ratio of –8.8dB. An excess power penalty of 0.5dB per 3dB increase in the feedback ratio was also empirically obtained. We suggest that optical isolators in 2.5Gbs–1 DFB-LD modules used in conventional optical transmission systems or WDM systems must have a peak isolation ratio of better than 54.5dB, instead of the previously recommended 30dB, for negligible power penalty induced by external optical feedback.     

YP1xVxO4∶Eu3+在真空紫外区发光的优化

系统地考查了Eu3 + 在YPO4 YVO4 固溶体中的发光。当V5+ 的浓度低于 0 3 ,出现VO4 3 -离子团的蓝色发射 ;直到V5+ 的浓度等于或大于 0 3时 ,VO4 3 -离子团的蓝色发射才被Eu3 + 离子的红色发射所猝灭 ,发射主波长在 61 9nm。在真空紫外线的激发下 ,Eu3 + 在YPO4 YVO4 固溶体有较强发光 ,并随着P5+ 浓度的增加 ,Eu3 + 离子的发光增强。经过优化的组成为YP0 7V0 3 O4 ∶Eu3 + 的荧光粉在真空紫外激发下既具有较强的发光 ,又具有优良的色纯度 ,将是一种新型的良好的等离子体平板显示用荧光粉。     

BaMgAl_(10)O_(17)∶R~(2+)(R=Eu,Mn)的真空紫外光谱特性

采用高温固相反应法合成了BaMgAl10 O17∶R(R =Eu ,Mn)荧光体 ,测量了荧光体的真空紫外激发光谱和相应的发射光谱 ,观察到基质吸收带位于 16 5nm附近 ,Mn2 + 离子的吸收位于 170～ 2 40nm范围 ,Eu2 + 离子的 4f→ 5d吸收位于 2 10～ 40 0nm范围。真空紫外光谱特性的研究表明基质与激活离子之间存在较好的能量传递。     

Y_(1.95-x)Gd_xSiO_5:Eu_(0.05)的真空紫外光谱

利用高温固相法合成了 Ｙ１．９５－ｘＧｄｘＳｉＯ５：Ｅｕ０．０５（ｘ＝０．６ｍｏｌ％）荧光体。结构测定表明所合成的荧光体为单斜晶系的Ｘ２型Ｙ２ＳｉＯ５相,空间群为Ｂ２／ｂ。真空紫外光谱表明：随着Ｇｄ３＋含量的增加,在１９２ｕｍ附近,出现了Ｇｄ＋的激发峰,且此峰的强度随着Ｇｄ３＋含量的增加而增大;同时位于１５０～１８５ｎｍ之间的基质吸收带的强度也增大;而位于２００～３００ｎｍ之间的Ｅｕ的电行迁移带的强度却随着Ｇｄ３＋含量的增加而降低。