Effect of carbon nanotubes dispersion on morphology, internal structure and thermal stability of electrospun poly(vinyl alcohol)/carbon nanotubes nanofibers

The current work reports the effect of multi walled carbon nanotubes and single walled carbon nanotubes dispersion on morphological, structural and thermal degradation of electrospun poly(vinyl alcohol) (PVA)/carbon nanotubes (CNTs) dispersed in sodium dodecyl sulfate (SDS) (PVA/CNTs–SDS) composites nanofibers. (PVA/CNTs–SDS) nanocomposites fibers were elaborated using the traditional electrospinning process to disperse and align CNTs into the fibers, especially for low CNTs loading fraction: 0.3 and 0.7 wt%. The morphology of the electrospun fibers was studied using the scanning electronic microscopy. The average diameter of the fibers changes significantly after the incorporation of the CNTs in the PVA. Furthermore, Fourier transform infrared spectroscopy elucidated the effect of CNTs on the crystallization of the PVA which was confirmed by X-ray diffraction analysis. Thermogravimetric analysis showed that the thermal stability of the composite fibers depends on the loading fraction and on the type of carbon nanotubes.     

Synthesis and characterization of nanocomposites films with graphene oxide and reduced graphene oxide nanosheets

Graphene oxide (GO) and reduced graphene oxide (CRGO), as a graphene derivatives, possess unique properties and a high aspect ratio, indicating great potential in nanocomposite fields. The present work reports the fabrication of the nanocomposite films by a simple and environmentally friendly process using aqueous solution and optimized time sonication for better exfoliation of the graphene sheets within Poly(Vinyl alcohol) (PVA) as matrix. The films were characterized using high-resolution TEM (HRTEM), X-ray diffraction (XRD), Microtensile testing, Differential scanning calorimetry (DSC) and Thermogravimetric analysis (TGA). The TEM images revealed a successfully exfoliation of the GO/CRGO nanosheets. XRD combined with TGA and DSC measurements showed an improvement in the thermal stability and tunable thermal properties. In addition, the Young's modulus and tensile yield strength of the composite films containing 1 wt% GO were obtained to be 4.92 GPa and 66 MPa respectively. These excellent reinforcement effects were achieved by the strong interaction between the components.