Amine‐cured epoxy/clay nanocomposites. II. The effect of the nanoclay aspect ratio

The thermophysical and mechanical properties of a nanocomposite material composed of amine‐cured diglycidyl ether of bisphenol A (DGEBA) reinforced with organomontmorillonite clay are reported. The storage modulus at 100 °C, which was above the glass‐transition temperature (T_g), increased approximately 350% with the addition of 10 wt % (6.0 vol %) of clay. Below the T_g, the storage modulus at 30 °C increased 50% relative to the value of unfilled epoxy. It was determined that the T_g linearly increased as a function of clay volume percent. The tensile modulus of epoxy at room temperature increased approximately 50% with the addition of 10 wt % of clay. The reinforcing effect of the organoclay nanoplatelets is discussed with respect to the Tandon–Weng and Halpin–Tsai models. A pseudoinclusion model is proposed to describe the behavior of randomly oriented, uniformly dispersed platelets in nanocomposite materials. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4391–4400, 2004     

Adhesive transfer of thin viscoelastic films

Micellar suspensions of acrylic diblock copolymers are excellent model materials for studying the adhesive transfer of viscoelastic solids. The micellar structure is maintained in films with a variety of thicknesses, giving films with a well-defined structure and viscoelastic character. Thin films were cast onto elastomeric silicone substrates from micellar suspensions in butanol, and the adhesive interactions between these coated elastomeric substrates and a rigid indenter were quantified. By controlling the adhesive properties of the film/indenter and film/substrate interfaces we were able to obtain very clean transfer of the film from the substrate to the portion of the glass indenter with which the film was in contact. Adhesive failure at the film/substrate interface occurs when the film/indenter interface is able to support an applied energy release rate that is sufficient to result in cavity nucleation at the film/substrate interface. Cavity formation is rapidly followed by delamination of the entire region under the indenter. The final stage in the transfer process involves the failure of the film that bridges the indenter and the elastomeric substrate. This film is remarkably robust and is extended to three times its original width prior to failure. Failure of this film occurs at the periphery of the indenter, giving a transferred film that conforms to the original contact area between the indenter and the coated substrate.     

Spectral and scattering theory for a Schrödinger operator with a class of momentum-dependent long-range potentials

Let be the selfadjoint operator for the static electromagnetic field where W _j for 0, 1, 2, ..., n is a sum of (i) a short-range potential and (ii) a smooth long-range potential decreasing at as |x|^- with in (0, 1]. Then for >1/2, asymptotic completeness holds for the scattering system (H, H ₀).     

Microfibrillated cellulose/cellulose acetate composites: Effect of surface treatment

Microfibrillated cellulose (MFC), which consists of a web‐like array of cellulose fibrils having a diameter in the range of 10–100 nm, was incorporated into a cellulose acetate (CA) matrix to form a totally biobased structural composite. Untreated and a 3‐aminopropyltriethoxysilane (APS) surface treated MFC was combined with a CA matrix by film casting from an acetone suspension. The effectiveness of the surface treatment was determined by infrared spectroscopy and X‐ray photoelectron spectroscopy. The Young's moduli of APS treated MFC composite films increase with increasing MFC content from 1.9 GPa for the CA to 4.1 GPa at 7.5 wt % of MFC, which is more than doubled. The tensile strength of the composite film increases to a maximum of 63.5 MPa at 2.5 wt % compared to the CA which has a value of 38 MPa. The thermal stability of composites with treated MFC is also better than the untreated MFC. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 153–161, 2010     

Raman spectroscopic investigation on the microenvironment of the liver tissues of Zebrafish (Danio rerio) due to titanium dioxide exposure

Nano titanium dioxide (nTiO₂), generally considered to be toxicologically inert, is manufactured in large quantities and extensively applied in consumer products. The small size and large surface area endow them with an active group or intrinsic toxicity. Advances in instrumentation are making Raman spectroscopy the tool of choice for an increasing number of (bio) chemical applications. One of the great advantages of this technique is its ability to provide information on the concentration, structure and interaction of biochemical molecules in their microenvironments within intact cells and tissues, non-destructively. Zebrafish (Danio rerio), one of the most important vertebrate model organisms used in developmental biology, are increasingly used in biomedical research, particularly as a model of human disease. In the present work, an attempt is made to study the effect of titanium dioxide, both nano and bulk, on the microenvironment of the liver tissues of Zebrafish using FT-Raman spectroscopy. The results of the present study suggest that TiO₂ exposure demonstrate a marked influence on the microenvironments of the liver tissues of Zebrafish. A shift to a higher wavenumber and an increase in the intensity of the band at ∼1087 cm⁻¹ in the TiO₂ exposed tissues suggest that some of the conformational changes resulting from the alkali recovery process takes place due to TiO₂ exposure. The decreased intensity ratio (I₃₂₂₀/I₃₄₀₀) observed in the titanium-exposed tissues suggests a decreased water domain size, which could be interpreted in terms of weaker hydrogen-bonded molecular species of water in the TiO₂ exposed tissues. The observed shift of COO⁻ bands to higher frequencies shows the disruption of salt bridges as a result of a change in the oppositely charged partners and due to the enhanced random coil conformation. The variation in the intensity ratio of the tyrosyl doublet (I₈₅₈/I₈₂₅) indicates variation in the hydrogen bonding of the phenolic hydroxyl group due to TiO₂ exposure. The results further suggest that the microenvironments are greatly altered due to titanium nano exposure when compared to titanium bulk. In conclusion, the results indicate that FT-Raman spectroscopy might be a useful tool for rapid assessment of nano particle biological interactions.     

Some relations between additive functions,II

Aequationes mathematicae -     

On the system of functional equationsf(x + y) = f(x) + f(y) andf(xy) = p (x)f(y) + q(y)f(x)

Aequationes mathematicae -