Effects of O ions beam irradiation on crystal structure of rare earth sesquioxides

We report the results of ion irradiation influence on rare earth sesquioxides structure, which are materials of practical importance as a radiation resistant ceramics in nuclear applications. Y₂O₃, Gd₂O₃ and Er₂O₃ sesquioxides in the pellet form were irradiated by oxygen ions (O²⁺) beam with the energy of 30 keV and implantation fluence of 5 × 10²⁰ m⁻². Samples are characterized by Grazing Incidence X-ray Diffraction (GIXRD), Raman spectroscopy and atomic force microscopy (AFM). By GIXRD it was found partial transformation from cubic (C) to monoclinic (B) phase only in Gd₂O₃, induced by O²⁺ irradiation. This was confirmed by Raman spectroscopy. Although full phase transition from C to B phase in Y₂O₃ was not observed, the splitting and broadening of the main intensity Raman band for C phase could be explained by the stress and the disorder induced by the quenching. Analysis done by AFM showed changes in surface topology, i.e. values of average roughness (Ra) and root mean squared roughness (RMS) were significantly changed after irradiation for all samples. RMSs in Y₂O₃ before and after irradiation were 35 nm and 26 nm, respectively.     

Subshell Resolved Measurements of Single Electron Capture in Slow Ne7+–Helium Collisions

Hyperfine Interactions - We have performed drying-humectation cyclical processes (CEBELCOR) on eight A36 low carbon steel coupons in NaCl solutions containing 1×10?2 M and...