This paper reports that the m-plane GaN layer is grown on (200)-plane LiAlO2 substrate by metal-organic chemical wpour deposition (MOCVD) method. Tetragonal-shaped crystallites appear at the smooth surface. Raman measurement illuminates the compressive stress in the layer which is released with increasing the layer's thickness. The high transmittance (80%), sharp band edge and excitonic absorption peak show that the GaN layer has good optical quality. The donor acceptor pair emission peak located at -3.41 eV with full-width at half maximum of 120 meV and no yellow peaks in the photoluminescence spectra partially show that no Li incorporated into GaN layer from the LiAlO2 substrate. 相似文献
2.
利用激光脉冲沉积(PLD)技术在(302)γ-LiAlO2衬底上成功生长了非极性的a面(1120) ZnO薄膜. 衬底温度为350℃时,薄膜是混合取向(a向和c向),以c面ZnO为主,且晶粒尺寸分布很宽;提高温度达500℃,薄膜变为单一的(1120)取向,摇摆曲线半高宽0.65°,晶粒尺寸分布趋窄,利用偏振透射谱可以明显看出其面内的各向异性. 衬底温度650℃下制备的样品晶粒继续长大,虽然摇摆曲线半高宽变大,但光致发光谱(PL)带边发射峰半高宽仅为105meV,比在350℃,500℃下制备的样品小1/5.
关键词:
非极性ZnO
2')" href="#">γ-LiAlO2
PLD
透射谱 相似文献
3.
4.
LiGaO2衬底上ZnO外延膜的结构与光学特性 总被引:3,自引:2,他引:1
采用磁控溅射法在(001),(100)及(010)LiGaO2衬底上制备了ZnO薄膜,通过X射线衍射(XRD)、原子力显微镜(AFM)、透过光谱以及光致发光谱(PL)对薄膜的结构、形貌及光学性质进行了表征.结果表明LiGaO2衬底不同晶面上制备的ZnO薄膜具有不同的择优取向,在(001)、(100)及(010)LiGaO2上分别获得了[001]、[1100]及[1120]取向的ZnO薄膜;不同取向的ZnO薄膜表面形貌差异较大;薄膜在可见光波段具有较高的透过率;在ZnO薄膜的光致发光谱中只观察到了位于378 nm的紫外发射峰,而深能级发射几乎观察不到,(1100)取向的薄膜紫外发射峰强度最大,半高宽也最小,薄膜光致发光件质的差异丰要和晶粒尺寸有关. 相似文献
5.
利用激光脉冲沉积(PLD)技术在(302)γ-LiAlO2衬底上成功生长了非极性的a面(11■0)ZnO薄膜.衬底温度为350℃时,薄膜是混合取向(a向和c向),以c面ZnO为主,且晶粒尺寸分布很宽;提高温度达500℃,薄膜变为单一的(11■0)取向,摇摆曲线半高宽0.65°,晶粒尺寸分布趋窄,利用偏振透射谱可以明显看出其面内的各向异性.衬底温度650℃下制备的样品晶粒继续长大,虽然摇摆曲线半高宽变大,但光致发光谱(PL)带边发射峰半高宽仅为105meV,比在350℃,500℃下制备的样品小1/5. 相似文献
6.
本文采用提拉法成功地生长了钛掺杂浓度为0.1%原子分数的LiAlO2单晶体,借助光学显微镜,结合化学腐蚀法,对Ti:LiAlO2晶体(100)面空气退火前后的缺陷特征进行了研究,用AFM观测了(100)面晶片在不同温度下流动N2气氛退火过的表面形貌。结果表明:Ti:LiAlO2晶体(100)面的位错腐蚀坑是底面为平行四边形的锥形坑,位错密度约为5.0×104cm-2,900℃空气退火后晶片表面的位错腐蚀坑变大;N2退火能显著影响晶片的表面形貌,当退火温度为900℃时,晶片的均方根粗糙度(RMS)达到最低值。 相似文献
7.
通过研究提拉法生长的掺杂Ti浓度为0.2at%的LiAlO2晶体吸收光谱,荧光光谱和红外光谱,来分析此新型晶体的结构.分析发现光谱中仅出现了四价Ti离子的196nm的特征吸收峰,用235nm光激发得到384nm的特征发射峰;针对吸收光谱中660-820nm出现的四个弱小吸收峰提出了一个色心模型,从而解释了空气和富Li气氛处理后吸收峰消失的现象;对比纯LiAlO2晶体的红外光谱发现,Ti的掺入仅影响了[AlO4]键强,而[LiO4]及相关键强几乎不变;结合ICP测试估算出直径50mm,厚1mm的Ti:LiAlO2的Li空位为5.5×1020个. 相似文献
8.
9.
类钙钛矿新铌酸盐Ba6LaTi3Nb3O21的合成、结构与介电特性 总被引:1,自引:0,他引:1
A New Niobate Ba6LaTi3Nb3O21 was synthesized by high temperature solid state reaction in the BaO-La2O3-TiO2-Nb2O5 system. The chemical compositions, crystal structure, microstructure, density and melting point of the new compound were characterized by EPMA, XRD, DTA and so on. Ba6LaTi3Nb3O21 crystallizes the rhombohedral system with unit cell parameters a=0.57388(2) nm, c=4.928 3(3) nm, and space group R3m, Z=3. The structure may be described as six (Nb,Ti)O6 octahedra corner-sharing along c-axis to form perovskite layer connected by Ba atoms. The Ba6LaTi3Nb3O21 ceramics exhibits high dielectric of 74.1, low dielectric loss of 4.7×10-4 and small temperature coefficient of dielectric constant of -69 ppm·K-1 at 1 MHz due to its close structure and relative high dielectric polarizabilities of Ba2+, La3+, Ti4+ and Nb4+. Ba6LaTi3Nb3O21 might be a suitable candidate of high εr microwave dielectric ceramics. 相似文献
10.
通过研究提拉法生长的掺杂Ti浓度为0.2at%的LiAlO2晶体吸收光谱,荧光光谱和红外光谱,来分析此新型晶体的结构.分析发现光谱中仅出现了四价Ti离子的196nm的特征吸收峰, 用235nm光激发得到384nm的特征发射峰;针对吸收光谱中660—820nm出现的四个弱小吸收峰提出了一个色心模型,从而解释了空气和富Li气氛处理后吸收峰消失的现象;对比纯LiAlO2晶体的红外光谱发现,Ti的掺入仅影响了[AlO4]键强,而[LiO4
关键词:
2')" href="#">Ti: LiAlO2
色心
光谱 相似文献