GROWTH MODEL OF TEXTURED DIAMOND (111) FILM IN CH4/O2/H2 ATMOSPHERE

Partially oriented and highly textured diamond films on Si( 111 ) substrates were achieved by hot-filament chemical vapor deposition(HFCVD). High nucleation density greater than 5×10⁸cm^-2 was realiged in 3 min by near-surface glow discharge. The os-grown films were characterized by scanning electron microscopy(SEM), X-ray diffraction(XRD) and Raman spectroscopy. It was found that by adding a small amount of oxygen to the mixture of CH₄/H₂, the appearance of facet(111) was well controlled, and the secondary nucleation on the facet(111) was suppressed greatly. Growth feature of homoepitaxy on diamond (111) surface was demonstrated to be in Stranski-Krastanov model by SEM.     

GROWTH MODEL OF TEXTURED DIAMOND (111) FILM IN CH4/O2/H2 ATMOSPHERE

Partially oriented and highly textured diamond films on Si( 111 ) substrates were achieved by hot-filament chemical vapor deposition(HFCVD). High nucleation density greater than 5×10⁸cm^-2 was realiged in 3 min by near-surface glow discharge. The os-grown films were characterized by scanning electron microscopy(SEM), X-ray diffraction(XRD) and Raman spectroscopy. It was found that by adding a small amount of oxygen to the mixture of CH₄/H₂, the appearance of facet(111) was well controlled, and the secondary nucleation on the facet(111) was suppressed greatly. Growth feature of homoepitaxy on diamond (111) surface was demonstrated to be in Stranski-Krastanov model by SEM.