排序方式: 共有6条查询结果,搜索用时 15 毫秒
1
1.
有机-无机杂化凝胶法合成YAG∶Ce~(3+)荧光粉的包膜及其稳定性 总被引:1,自引:0,他引:1
本文以金属硝酸盐为原料,柠檬酸为配位剂的有机-无机杂化凝胶法来合成掺杂三价铈离子的钇铝石榴石荧光粉,采用X-射线衍射法研究了杂化凝胶在煅烧过程中的相转变机制。结果表明:杂化凝胶在煅烧过程中可以通过两条途径形成Y3Al5O12(YAG)相:一是由无定形Y2O3和Al2O3直接向YAG相的一步相转变;二是由无定型Y2O3和Al2O3经由YAlO3(YAP)和γ-Al2O3向YAG相的两阶段相转变,在900℃得到结晶性好的纯YAG∶Ce3 荧光粉,其最大激发波长为459nm,最大发射峰波长为550nm;在荧光粉表面包覆氧化铝和氧化镧,将使荧光粉的荧光强度稍有降低,但对荧光粉的稳定性有很好的改进作用。 相似文献
2.
3.
Uniform hollow Au@TiO2 core shell spheres with moveable Au nanoparticles were synthesized based on templating against Au@carbon spheres. The diameter of the shell of the Au@TiO2 spheres could be controlled by adjusting the Ti(OC4H9)4 hydrolyzing reaction time or the ratio of Ti(OC4H9)4 to Au@carbon spheres, and the shell thickness of the core-shell spheres can be varied from 25 nm to 40 nm. As prepared hollow Au@TiO2 core-shell spheres display enhanced photocatalytic activity in the initial stage of photocatalytic degradation of methylene blue compared with pure hollow TiO2 spheres and the commercial photocatalyst TiO2(P-25). 相似文献
4.
5.
用聚丙烯酰胺凝胶法来合成YAG:Ge^3+荧光粉,用XRD对煅烧过程粉体的结构进行了跟踪测定。结果发现,当直接煅烧凝胶时,可观察到θ-Al2O3,YAM和YAP等中间相的形成,而当煅烧含有α-Al2O3,YAM和YAP的形成,加速其与Y203的反应而在较低温度下直接生成YAG相。合成YAG:Ce^3+荧光粉的发射峰为处于550nm的宽峰,其激发光谱有两个主要的吸收峰,主峰位于460nm,可以与GaN LED的蓝色发射相匹配而用于白光LED的组装。一些助熔剂可以提高荧光粉的光致发光特性,这归因于助熔剂对YAG结晶过程的改进作用和对YAG:Ce^3+中三价铈离子的稳定作用。 相似文献
6.
稀土Tb3+,Eu3+对N-苯基邻氨基苯甲酸及邻菲咯啉间能量传递与蓝色发射的强化作用 总被引:2,自引:0,他引:2
合成了一种由稀土离子与N—苯基邻氨基苯甲酸(N—HPA)和邻菲咯啉(phen)形成的蓝色发光配合物。该配合物是典型的配体发光配合物,其发射峰位于444nm,激发波长为334nm和407nm。元素分析、红外光谱、紫外—可见光谱和差热—热重的分析结果表明:配合物中含有大量的N—HPA和相对较少的稀土离子和phen,其中稀土离子与N—PA中的羧酸根配位,而N—PA中的氨基通过氢键与phen的氯原子结合,形成了有利于配体之间的能量传递和电子转移的通道。稀土离子Tb^3 ,Eu^3 的共同存在促进了这一能量转移通道的形成,进而强化了配体的蓝色发射。 相似文献
1