排序方式: 共有18条查询结果,搜索用时 15 毫秒
1.
结合氢在GaN中的扩散特性,运用阴极荧光(CL)谱,对氢化前后低能电子束辐照下GaN带边发光强度的演变进行了研究.实验发现,氢化前GaN在低能电子束辐照下带边发光强度呈现衰减的趋势,而氢化后带边发射强度先上升后衰减,而且氢化后的衰减比氢化前弱.1 h辐照过程中,氢化后GaN带边发光强度的变化比氢化前要小很多.另外,实验中发现经过氢化处理的GaN在辐照后20 h内没有观察到带边发射强度的恢复.研究表明氢原子在GaN中可以钝化缺陷来增强发光,但这种钝化缺陷的作用必须通过克服高的扩散势垒来实现,而低能电子束可以
关键词:
阴极荧光
低能电子束
氢化
演变 相似文献
2.
Identification and elimination of inductively coupled plasma-induced defects in AlxGa1 - xN/GaN heterostructures
下载免费PDF全文
![点击此处可从《中国物理 B》网站下载免费的PDF全文](/ch/ext_images/free.gif)
By using temperature-dependent Hall,variable-frequency capacitance-voltage and cathodoluminescence (CL) measurements,the identification of inductively coupled plasma (ICP)-induced defect states around the Al x Ga 1-x N/GaN heterointerface and their elimination by subsequent annealing in Al x Ga 1-x N/GaN heterostructures are systematically investigated.The energy levels of interface states with activation energies in a range from 0.211 to 0.253 eV below the conduction band of GaN are observed.The interface state density after the ICP-etching process is as high as 2.75×10 12 cm 2 ·eV 1.The ICP-induced interface states could be reduced by two orders of magnitude by subsequent annealing in N 2 ambient.The CL studies indicate that the ICP-induced defects should be Ga-vacancy related. 相似文献
3.
Comparision between Ga- and N-polarity InGaN solar cells with gradient-In-composition intrinsic layers
下载免费PDF全文
![点击此处可从《中国物理 B》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Performances of Ga-and N-polarity solar cells(SCs) adopting gradient-In-composition intrinsic layer(IL) are compared.It is found the gradient ILs can greatly weaken the negative influence from the polarization effects for the Gapolarity case,and the highest conversion efficiency(η) of 2.18%can be obtained in the structure with a linear increase of In composition in the IL from bottom to top.This is mainly attributed to the adsorptions of more photons caused by the higher In composition in the IL closer to the p-GaN window layer.In contrast,for the N-polarity case,the SC structure with an InGaN IL adopting fixed In composition prevails over the ones adopting the gradient-In-composition IL,where the highest η of 9.28%can be obtained at x of 0.62.N-polarity SC structures are proven to have greater potential preparations in high-efficient InGaN SCs. 相似文献
4.
Recently GaN-based high electron mobility transistors (HEMTs) have
revealed the superior properties of a high breakdown field and high
electron saturation velocity. Reduction of the gate leakage current
is one of the key issues to be solved for their further improvement.
This paper reports that an Al layer as thin as 3 nm was inserted
between the conventional Ni/Au Schottky contact and n-GaN epilayers,
and the Schottky behaviour of Al/Ni/Au contact was investigated
under various annealing conditions by current--voltage (I--V)
measurements. A non-linear fitting method was used to extract the
contact parameters from the I--V characteristic curves.
Experimental results indicate that reduction of the gate leakage
current by as much as four orders of magnitude was successfully
recorded by thermal annealing. And high quality Schottky contact
with a barrier height of 0.875 eV and the lowest reverse-bias
leakage current, respectively, can be obtained under 12 min
annealing at 450°C in N2 ambience. 相似文献
5.
针对AlGaN基多量子阱中有效的平衡载流子注入问题,研究了有源区势垒层中Al组分调制形成的非规则H形量子势垒对AlGaN基深紫外发光二极管(LED)器件性能的影响及载流子的输运行为。研究发现,与多量子阱中常用的单Al组分势垒相比,加入Al组分较高的双尖峰势垒可以有效地提高内量子效率和光输出功率。进一步研究表明,电子在有源区因凸起的尖峰势垒而得到了有效的阻挡,减少了电子的泄露,而空穴获得更多的动能从而穿过较高的势垒进入有源区。因此,采用非对称H形量子势垒的深紫外LED器件中载流子输运实现了较好的平衡,量子阱中的载流子复合速率远高于普通的深紫外发光二极管。 相似文献
6.
Epitaxial evolution on buried cracks in a strain-controlled AlN/GaN superlattice interlayer between AlGaN/GaN multiple quantum wells and a GaN template
下载免费PDF全文
![点击此处可从《中国物理 B》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Epitaxial evolution of buried cracks in a strain-controlled AlN/GaN superlattice interlayer(IL) grown on GaN template, resulting in crack-free AlGaN/GaN multiple quantum wells(MQW), was investigated. The processes of filling the buried cracks include crack formation in the IL, coalescence from both side walls of the crack, build-up of an MQW-layer hump above the cracks, lateral expansion and merging with the surrounding MQW, and two-dimensional step flow growth.It was confirmed that the filling content in the buried cracks is pure GaN, originating from the deposition of the GaN thin layer directly after the IL. Migration of Ga adatoms into the cracks plays a key role in the filling the buried cracks. 相似文献
7.
Leakage current reduction by thermal oxidation in Ni/Au Schottky contacts on lattice-matched Ino.18Al0.82N/GaN heterostructures
下载免费PDF全文
![点击此处可从《中国物理 B》网站下载免费的PDF全文](/ch/ext_images/free.gif)
By using temperature-dependent current-voltage, variable-frequency capacitance-voltage, and Hall measurements, the effects of the thermal oxidation on the electrical properties of Ni/Au Schottky contacts on lattice-matched Ino.18Alo.82N/GaN heterostructures are investigated. Decrease of the reverse leakage current down to six orders of magni- tude is observed after the thermal oxidation of the Ino.18Alo.82N/GaN heterostructures at 700 ℃. It is confirmed that the reverse leakage current is dominated by the Frenkel-Poole emission, and the main origin of the leakage current is the emis- sion of electrons from a trap state near the metal/semiconductor interface into a continuum of electronic states associated with the conductive dislocations in the InxAll-xN barrier. It is believed that the thermal oxidation results in the formation of a thin oxide layer on the InxAll-xN surface, which increases the electron emission barrier height. 相似文献
8.
运用电流-电压(I-V), 变频电容-电压(C-V)和原子力显微镜 (AFM) 技术研究In组分分别为15%, 17%和21%的Ni/Au/-InAlN肖特基二极管InAlN 样品表面态性质 (表面态密度、时间常数和相对于InAlN 导带底的能级位置). I-V和变频 C-V方法测量得到的实验结果表明, 随着In组分增加, 肖特基势垒高度逐渐降低, 表面态密度依次增加. 变频 C-V特性还表明,随着测试频率降低, C-V曲线有序地朝正电压方向移动, 该趋势随着In组分的增加而变得更加明显, 这可能归结于InAlN表面态的空穴发射. AFM表面形貌研究揭示InAlN 表面粗糙度增加可能是表面态密度增加的主要原因.
关键词:
不同In组分的InAlN材料
表面态
电流-电压特性
变频电容-电压特性 相似文献
9.
Different temperature dependence of carrier transport properties between AlxGal-xN/InyGal-yN/GaN and Alx Gal-xN/GaN heterostruct ures
下载免费PDF全文
![点击此处可从《中国物理 B》网站下载免费的PDF全文](/ch/ext_images/free.gif)
The temperature dependence of carrier transport properties of Alx Gal-xN/InyGal-yN/CaN and AlzGal-xN/GaN heterostructures has been investigated. It is shown that the Hall mobility in Alo.25Gao.75N/Ino.03Gao.97N/GaN heterostructures is higher than that in Alo.25Gao.75N/GaN heterostructures at temperatures above 500 K, even the mobility in the former is much lower than that in the latter at 300 K. More importantly, the electron sheet density in Alo.25Gao.75N/Ino.03Gao.97N/GaN heterostructures decreases slightly, whereas the electron sheet density in Al0.25Gao.75N/CaN heterostructures gradually increases with increasing temperature above 500 K. It is believed that an electron depletion layer is formed due to the negative polarization charges at the Iny Can-yN/GaN heterointerface induced by the compressive strain in the InyCal-yN channel, which effectively suppresses the parallel conductivity originating from the thermal excitation in the underlying GaN layer at high temperatures. 相似文献
10.
The leakage current mechanisms in the Schottky diode with a thin Al layer insertion between Al0.245Ga0.755N/GaN heterostructure and Ni/Au Schottky contact
下载免费PDF全文
![点击此处可从《中国物理 B》网站下载免费的PDF全文](/ch/ext_images/free.gif)
This paper investigates the behaviour of the reverse-bias leakage current of the Schottky diode with a thin Al inserting layer inserted between Al0.245Ga0.755 N/GaN heterostructure and Ni/Au Schottky contact in the temperature range of 25-350°C. It compares with the Schottky diode without Aluminium inserting layer. The experimental results show that in the Schottky diode with Al layer the minimum point of I-V curve drifts to the minus voltage, and with the increase of temperature increasing, the minimum point of I-V curve returns the 0 point. The temperature dependence of gate-leakage currents in the novelty diode and the traditional diode are studied. The results show that the Al inserting layer introduces interface states between metal and Al0.245Ga0.755N. Aluminium reacted with oxygen formed Al2O3 insulator layer which suppresses the trap tunnelling current and the trend of thermionic field emission current. The reliability of the diode at the high temperature is improved by inserting a thin Al layer. 相似文献