Ne离子束辐照引起Gd2Ti2O7烧绿石体积肿胀效应研究

在液氮低温下用400 keV的Ne2+离子束对Gd₂Ti₂O₇多晶烧绿石进行了辐照实验研究, 离子束辐照量范围为5×1014—1×1016ions/cm2。利用掠X射线衍射技术对样品辐照层的结构变化进行了分析表征, X射线的掠射角分别为γ=0.25°, 0.5°, 1°和3°。结果表明: 在该实验条件的离子束辐照下, Gd₂Ti₂O₇辐照层会发生明显的体积肿胀效应, 体积肿胀程度随入射离子束辐照量的增大而增大; 在同一辐照量下, 辐照层的体积肿胀程度也随X射线入射角的增大而增大。当辐照量达到1×1016ions/cm2时, 辐照层发生非晶化相变。Polycrystalline pyrochlore Gd₂Ti₂O₇ compounds were irradiated with 400 keV Ne2+ ions at cryogenic temperature (~77 K). The irradiation fluences was ranging from 5×1014 to 1×1016 ions/cm2, corresponding to a peak ballistic damage dose of ~0.16 to 3.3 displacements per atom . Irradiation\|induced structural evolution was examined using grazing incidence X\|ray diffraction (GIXRD) at angles from 0.25° to 3° degrees. It was found that the lattice parameter increases as a function of (1) X\|ray incident angle and (2) ion irradiation fluence, suggesting that the irradiated layer is volumetrically swelled compared with the underlying un\|irradiated substrate. At ion fluence of 1×1016 ions/cm2, the irradiation layer was found to be amorphous.     

晶粒尺寸对掺氦纳米多晶铁机械性能影响的分子动力学模拟研究

采用分子动力学方法研究了晶粒尺寸对掺氦纳米多晶铁机械性能的影响.在拉伸形变过程中,纳米多晶铁将产生裂纹与晶格畸变,通过模拟XRD谱探索二者之间的联系.拉伸模拟结果显示,由于晶界氦原子的引入,峰值应力将显著减小.另外,在拉伸模拟中观察到,沿晶裂纹的产生与长大随着晶界氦原子的引入而增强.研究结果表明,晶界氦原子能够促进沿晶...