Comparative study of spectroscopic properties of Er^3+/Yb^3+-codoped tellurite glass and fibres under 980nm excitation* 下载免费PDF全文
A tellurite fibre of TeO_{2}-ZnO-La_{2}O_{3}-Li_{2}O glass codoped with 20000 ppm ytterbium and 5000 ppm erbium was fabricated by the suction casting and rod-in-tube technologies. The absorption spectrum of Er^{3+}/Yb^{3+} -codoped bulk glass has been measured. From the Judd-Ofelt intensity parameters, the spontaneous emission probability and radiative lifetime τ_{rad} of Er^{3+}:{}^{4}I_{13/2}→{}^{4}I_{15/2} transition for the bulk glass have been calculated. The emission fluorescence spectra and lifetimes around 1.5μm, and subsequent upconversion fluorescence in the range of 500-700nm were measured in fibres and compared with those in bulk glass. The changes in amplified spontaneous emission with fibre length and pumping power was also measured. It was found that the emission spectrum from erbium in fibres is almost twice as broad as the corresponding spectrum in bulk glass when pumped at 980nm. 相似文献
4.
The Yb3+/Er3+ co-doped TeO2-WO3-ZnO glasses bubbling with different times were prepared. The infrared (IR) transmission spectra, emission spectra and fluorescence lifetime of Er3+ at 1.5 um were measured. The quench effects of OH groups on emission intensity of Er3+ at 1.5 um as well as the relationships between fluorescence decay rate and OH group content were investigated. The constant kOH-Er which represents the strength of the interactions between Er3+ ions and OH groups, is approximately 17.0×10-20 cm4/s, and is comparable to that for Er3+ in Yb3+/Er3+ co-doped phosphate glasses. 相似文献
5.
测量了不同Yb3+ 离子掺杂浓度下 ,Er3+ /Yb3+ 共掺SiO2 Al2 O3 La2O3玻璃的吸收光谱、荧光光谱和Yb3+离子2 F5/ 2 的能级寿命 ,应用迈克康伯 (McCumber)理论计算了Er3+ 的受激发射截面σemi,讨论了Yb3+ 离子浓度对其自身吸收性质、Er3+ 离子发光性质 ,以及Yb3+ →Er3+ 能量传递效率 (η)的影响 ,初步探明该基质玻璃中Yb3+ 离子掺杂数浓度的最佳范围为 3 .94× 1 0 2 0 cm- 3至 5 .92× 1 0 2 0 cm- 3,在此掺杂范围内 ,Yb3+ 离子的最大吸收系数为9.8cm- 1 ,Er3+ 的峰值发射截面和Yb3+ →Er3+ 能量传递效率 (η)分别为 0 64× 1 0 - 2 4 m2 和 92 %。 相似文献
6.
The emission properties of 2-μm region fluorescence of Tm~(3+)-Ho~(3+) co-doped tellurite glasses are investigated. Introducing F~- ions to the composition of tellurite glasses plays a positive effect on the 2-μm emission.A maximum intensity of 2-μm emission is achieved when 1.5-mol%Tm_2O_3 and l-mol% Ho_2_O3 concentration are doped in the glasses.The emission cross section and gain coefficient of the ~5I_8→~5I_7 transition of Ho~(3+) are calculated.The emission cross section has a maximum of 1.29×10~(-2... 相似文献
7.
A Novel Ce3+/Tb3+ Codoped Phosphate Glass as Down-Shifting Materials for Enhancing Efficiency of Solar Cells 下载免费PDF全文
For the purpose of improving conversion efficiency of solar cells by applying the effect of the wavelength conversion of rare earth ions, photo-luminescence and excitation spectrums of Ce3+-Tb3+ doped phosphate glass are investigated. Results show that incorporating Ce3+ ions to Tb3+-doped phosphate glass can greatly increase the absorption coefficient in the range 300-400 nm and then the energy transfer (ET) from Ce3+ to Tb3+ occurs. In addition, increasing Tb3+ concentration in Ce3+/Tb3+ co-doped phosphate glass can greatly enhance the ET efficiency and 545 nm emission intensity. This shows that Ce3+/Tb3+ co-doped phosphate glass would be a promising down-shifting material for enhancing the efficiency of solar cells. 相似文献
8.
在概述国内外高功率激光钕玻璃的发展及其主要性质的基础上,重点论述了上海光学精密机械研究所在大口径N31高功率激光钕玻璃半连续熔炼工艺、连续熔炼工艺、包边工艺等方面的研究进展。报道了半连续熔炼工艺制备的不同Nd2O3浓度N31钕玻璃的光吸收损耗和荧光寿命及小信号增益系数,并给出了这些钕玻璃坯片小信号增益系数的波动范围。通过对半连续熔炼和连续熔炼工艺制备的N31激光钕玻璃主要性能的比较,证明连续熔炼工艺制备的N31钕玻璃的主要性能指标与半连续熔炼的性能相当。对于400 mm大口径N31钕玻璃坯片的包边进行了模拟考核,结果表明,采用现有包边工艺的钕玻璃可以承受1 000次高功率氙灯辐射。 相似文献
9.
10.
在Er3+/Yb3+共掺TeO2-WO3-ZnO玻璃中引入Ce3+,研究了Ce3+对Er3+1.5μm发射性能及其上转换发光性能的影响.结果表明,随Ce3+浓度的增加Er3+1.5μm波段的荧光强度先增强后降低,优化的Ce3+掺杂浓度在2.07×1020/cm3左右;1.5μm波段的荧光寿命则随Ce3+浓度的增加有轻微降低,从3.4ms降到3.0ms,但Ce3+浓度的增加对1.5μm波段的荧光半高宽基本无影响;Er3+/Ce3+间的交叉弛豫Er3+(4I11/2+Ce3+(2F5/2→Er3+(4I13/2+Ce3+(2F7/2使玻璃的上转换发光强度大大降低,但在过高的Ce3+浓度下,Er3+/Ce3+间的另一交叉弛豫Er3+(4I13/2+Ge3+(2F5/2→Er3+(4I15/2+Ce3+(2F7/2则使Er3+4I13/2能级粒子数减少,导致1.5μm波段荧光强度和荧光寿命降低. 相似文献