SiO2包覆铕(Ⅲ)配合物的荧光纳米粒子合成与性质

以前驱物pAB-DTPAA-APTEOS、正硅酸乙酯(TEOS)和三氯化铕(EuCl3)等为原料,采用油包水(W/O)的反相微乳液法,在正硅酸乙酯(TEOS)和3-氨丙基三乙氧基硅烷(APTEOS)的共同水解下,制备出新型的SiO2包覆铕配合物荧光纳米粒子Eu-pAB-DTPAA-AP-SiO2。运用TEM、IR、UV-Vis、荧光光谱等技术对荧光纳米粒子进行了表征。TEM结果表明:包覆体呈球形,分散均匀,平均粒径为40nm。纳米粒子与配体、前驱物的紫外吸收谱相比较,峰位发生了一定的红移,表明通过反相微乳液法得到的固体粉末与EuCl3反应后,已经生成配合物Eu-pAB-DTPAA-AP-SiO2。红外光谱研究表明,在801cm-1出现νSi—C的伸缩振动峰,471cm-1处出现νEu—O的伸缩振动峰。由此证实Eu-pAB-DTPAA-AP-SiO2配合物的存在。荧光光谱分析表明,纳米粒子Eu-pAB-DTPAA-AP-SiO2表现出较好的荧光性能,位于592,615,689nm的发射峰分别归属于Eu3 离子的5D0→7F1、5D0→7F2和5D0→7F4跃迁,其中最强峰615nm属于Eu3 的特征跃迁发射。作为一种新型的荧光试剂,该纳米粒子具有粒径小,亲水性强,荧光强度大,且表面的氨基能方便地与生物分子偶联,故可作为优良的时间分辨荧光标记物用于各种高灵敏生物检测技术中。     

铽异烟酸哌嗪三元配合物的合成及其荧光性能

以醋酸铽,异烟酸和哌嗪为原料,合成了铽异烟酸哌嗪三元固体配合物,其结构经UV-vis,IR,TC-DTA和元素分析表征,并用荧光光谱测定了其荧光性能.     

Ag-catalyzed Synthesis of Tb(BO2)3 Nanorods

Well-crystallized with excellent luminescent properties, Tb(BO₂)₃ nanorods were first suc-cessfully synthesized by a simple solid-state method with Ag as catalyst. The result of X-ray diffraction showed that the Tb(BO₂)₃ nanorods could be well-crystallized at 700 oC. As-prepared straight nanorods of Tb(BO₂)₃ had the typical diameters in the range of 100-200 nm, the thickness of 30-50 nm and the lengths up to 3 μm by transmission elec-tron microscopy and the corresponding selected area electron diffraction indicated that the nanorod calcined at 700 oC was single-crystalline. Based on the fact that Ag nanoparti-cles attached to the tips and middles of the Tb(BO₂)₃ nanorods, a growth model of the Tb(BO₂)₃ nanorods was proposed. Photoluminescence spectra under excitation at 369 nm showed that these Tb(BO₂)₃ phosphors had a green emission at 546 nm, which is ascribed to ⁵D₄→⁷F₅ transition. The effect of calcining temperature on the structures, morphologies, and luminescent properties of Tb(BO₂)₃ phosphors were studied.     

链状Eu(BO_2)_3的合成与发光性能研究

采用固相反应合成出链状结构的稀土硼酸盐Eu(BO2)3发光材料。分别利用XRD、TEM、SAED、EDS和PL等测试技术对产物进行了研究,结果表明:链状结构的Eu(BO2)3属于单斜晶系,空间群为I2/a,直径约10～15nm,长度达几个微米,探讨了链状Eu(BO2)3的生长机理。在395nm紫外光激发下,Eu(BO2)3能发出Eu3+的特征红色荧光,发射主峰位于591nm,归属于5D0→7F1磁偶极跃迁。     

溶胶-凝胶法制备Tb-PDA/PVA薄膜及其荧光性能

采用溶胶-凝胶法制备了铽(Ⅲ)-吡啶-2,6-二羧酸/聚乙烯醇(Tb-PDA/PVA)发光薄膜,其结构经IR,差热分析,原子力显微镜及荧光光谱表征.分析结果表明:薄膜表面平整,PVA中的纳米Tb-PDA(平均粒径为90 nm)分散均匀,在270 ℃以下具有良好的热稳定性.在紫外光照射下,薄膜发出较强的绿色荧光,最大发射峰位于544 nm,归属于Tb3+的5D4→7F5跃迁.