在GaAs-Al矩形光栅界面上表面增强二次谐波产生

我们以GaAs-Al矩形光栅界面为例具体推导了二次谐波产生的公式.依据Bloembergen和Pershan关于非线性介质的理论,用微扰论方法求解了麦克斯韦方程.理论公式和数值计算均表明,表面增强二次谐波起源于共振激励表面电磁波.     

GROWTH MODE OF Cu-RICH PARTICLES ON LASER-ABLATED YBa2Cu3O7 THIN FILMS

The microstructure of the laser-ablated YBa₂Cu₃O₇ (YBCO) thin film deposited on heated (100) SrTiO₃ substrate was examined by transmission electron microscope. The par-ticles on the film mainly consist of CuO and few CuYO₂. Most of these non-superconducting particles nucleate on or near the surface of the film and protrude about 100-400 nm in height, A large amount of a-axis YBCO grains also exist in the film, which nucleate at the substrate surface and grow perpendicularly above the c-axis YBCO film. The YBCO thin film deposited under low oxygen pressure has very different microstructure compared with YBCO thin film deposited under high oxygen pressure.     

金属Fe薄膜的PLD制备及其非线性光学性质研究

采用脉冲激光沉积（PLD）技术在MgO基片上制备了金属Fe薄膜.利用原子力显微镜研究了不同制备温度对薄膜表面形貌的影响.x射线衍射分析表明沉积温度大于500℃时，Fe薄膜在MgO基片上有很好的结晶性，并有单一取向.通过z扫描方法测量了超薄Fe膜的光学非线性，得到了Fe薄膜的非线性折射率n₂＝709×10^-5cm²/ kW，非线性吸收系数 β＝-552×10^-3cm/W. 关键词： Fe薄膜 非线性 脉冲激光沉积     

Pico-second photoelectric characteristic in manganite oxide La0.67Ca0.33MnO3 films

Ultrafast photoelectric characteristic has been observed in La_0.67Ca_0.33MnO₃ films on tilted SrTiO₃ substrates. A pico-second (ps) open-circuit photovoltage of the perovskite manganese oxide films has been obtained when the films were irradiated by a 1.064μm laser pulse of 25 ps duration. The rise time and full width at half-maximum of the photovoltage pulse are ～300 ps and ～700 ps, respectively. The photovoltaic sensitivity was as large as ～500 mV/mJ.     

激光分子束外延制备高质量的YBCO超导薄膜

利用活化气体做氧源,使生长气压比普通脉冲激光沉积方法(PLD)低2～3个数量级,用激光分子束外延在SrTiO₃(100)衬底上制备出临界转变温度T_c0=85～87K,临界电流密度J_c≥1×10⁶A/cm²的高质量YBCO超导薄膜.原子力显微镜(AFM)测得表面无明显颗粒,均方根粗糙度约为7.8nm.在这种薄膜基础上制备的Josephson量子干涉器件(DC-SQUID)具有良好的温度循环稳定性.     

BaTiO3 /SrTiO3超晶格的激光分子束外延生长与二阶光学非线性研究

使用激光分子束外延 ,在SrTiO₃ ( 1 0 0 )单晶衬底上成功生长了一系列c轴取向的 ,具有原子量级控制精度的BaTiO₃/SrTiO₃超晶格 .利用晶格失配导致的薄膜表面台阶密度的周期性变化 ,讨论了反射式高能电子衍射 (RHEED)强度在BaTiO₃ 层和SrTiO₃ 层中的周期性调制 .系统研究了二阶非线性光学极化率同超晶格结构的关系 .实验测量和理论拟合结果表明 ,BaTiO₃ /SrTiO₃ 超晶格的二阶非线性光学极化率显著增强 ,其最大值比BaTi₃体单晶提高一个数量级以上 .从应力导致的晶格畸变和极化增强出发 ,讨论了二阶光学非线性增强的物理机制     

Formation of Interfacial Layers in LaAlO3/Silicon during Film Deposition

We have studied the interracial reactions between amorphous LaAlO3 thin films and Si substrates, using high- resolution transmission electron microscopy and x-ray photoelectron spectroscopy. It has been shown that the interracial layer between LaAlO3 film and Si substrate chemical states show that the ratio of La 4d3/2 to Al 2p is SiLaxAlyOz. The depth distributions of La, Si and Al of the interfacial layer remains unchanged with the depth compared to that of the LaAlO3 film. Moreover, the Si content, in the interracial layer gradually decreases with increasing thickness of the interracial layer. These results strongly suggest that the Al element is not deficient in the interracial layer, as previously believed, and the formation of a SiLaxAlyOz interracial layer is mainly due to the diffusion of Si from the substrate during the LaAlO3 film deposition. With the understanding of the interracial layer formation, ones can control the interface characteristics to ensure the desired performances of devices using high-k oxides as gate dielectrics.     

钴氧化物中晶格与自旋的关联耦合效应研究

强关联电子体系具有多序参量耦合且极易受到外场高效调控的特性.钴氧化物(LaCoO₃)是一类典型的多铁性(兼具铁弹性和铁磁性)氧化物材料,受到了研究者们广泛和深入的研究.过去,针对钴氧化物的研究都集中于应力作用下的铁弹性相变和结构调控方面.近年来,研究人员新奇地发现钴氧化物薄膜在张应力作用下发生顺磁到铁磁相转变,但其根源一直存在较大争议.部分实验证据表明应力将会导致钴离子价态降低产生自旋态转变,而另一些研究者认为应力诱导的纳米畴结构会呈现高自旋态的长程有序排列,才是钴氧化物薄膜铁磁性的主要原因.本综述主要介绍近几年来钴氧化物薄膜和异质结中自旋与晶格之间关联耦合效应的系列进展.在保持钴离子价态不变时,通过薄膜厚度、晶格失配应力、晶体对称性、表面形貌、界面氧离子配位和氧八面体倾转等结构因素诱导钴氧化物薄膜的自旋态可逆转变,从而形成高度可调的宏观磁性.进而,研究者们利用原子级精度可控的薄膜生长技术构筑了单原胞层钴氧化物超晶格,通过高效的结构调控,实现了超薄二维磁性氧化物材料.这些系列进展不仅澄清了强关联电子体系中晶格与自旋等序参量之间的强耦合关系,而且为实现氧化物自旋电子...     

BaTiO3/SrTiO3超晶格的二次谐波产生研究

用激光分子束外延技术生长了BaTiO3 /SrTiO3 超晶格并首次对之采用二次谐波产生的方法进行了研究 .实验表明其结构为类似BaTiO3 的四方相结构 .实验得到的材料的有效倍频系数远大于BaTiO3 薄膜 ,也大于BaTiO3 体材料的值 .这表明这种人为控制的BaTiO3 /SrTiO3 超晶格结构具有较大的非线性光学的应用前景 .     

MgB2超导薄膜的微波测量

报道了利用蓝宝石介质谐振器技术测量MgB2超导薄膜的微波表面电阻Rs、OK时的穿透深度λ(O)和超导能隙△(O)．λ(O)和△(O)的值是通过先测量样品穿透深度λ(T)的变化量△λ(T)，然后由BCS理论模型拟合△λ（T)的实验数据得到的．测试样品是利用化学气相沉积技术在MgO(111)基片上制备的c轴织构的MgB2超导薄膜，薄膜的超导转变温度和转变宽度分别为38K和0．1K．微波测试结果表明在10K，18GHz下MgB2薄膜的Rs约为100μΩ，可以和高质量的YBCO薄膜的Rs值相比拟；BCS理论拟合得到的MgB2超导薄膜的λ(0)=102nm，△(0)：1．13kTc．