1.
2.
Pt3Co核-Pt壳型纳米粒子的制备及磁性 总被引:1,自引:1,他引:1
Pt3Co alloy nanoparticles were prepared by the reduction of H2PtCl6 and Co(OOCCH3)2 using NaBH4 as a reducing agent. The Pt3Co core-Pt shell nanoparticles (Pt3Co@Pt) were synthesized using hydrogen absorption reduction and characterized by plasma-atomic emission spectrometry (ICP), transmission electron microscopy (TEM), X-ray diffraction (XRD) and SQUID magnetometer. The results show that average size of Pt3Co@Pt nanoparticles is 3.6 nm with a standard deviation of 0.9 nm. Heating Pt3Co nanoparticles in air at 700 ℃ for 1 h, Co in Pt3Co nanoparticles was oxidized to Co3O4 and CoO; while no oxidation tendency was detected for Pt3Co@Pt nanoparticles. The crystallize structure of Pt3Co@Pt changed from the face centered cube (fcc) to the face centered tetragonal (fct) after the heating treatment. The coercivity of the heated Pt3Co@Pt reached to 276 Oe at room temperature. 相似文献
3.
载体对负载型TiO2催化剂光催化性能的影响 总被引:22,自引:0,他引:22
以活性碳(AC)和镁铝尖晶石(MA)为载体,采用真空吸附水解法制备了负载型光催化剂TiO2/AC和TiO2/MA,并采用TiO2溶胶负载法制备了活性碳负载催化剂TiO2(C)/AC.以氯仿为探针分子研究了其在催化剂上的吸附及光催化降解反应性能.结果表明,催化剂的制备方法、TiO2负载量与载体的吸附性能对光催化活性有明显的影响.通过优化制备条件,TiO2/AC催化剂的催化活性可提高到纳米TiO2的2.5倍.氯仿在AC上的饱和吸附量较高,但吸附强度较弱;在纳米TiO2上的吸附情况则正好相反.氯仿在AC和TiO2上吸附性质的差异有利于吸附在TiO2/AC上的氯仿分子从活性碳载体向TiO2光催化活性中心迁移.镁铝尖晶石载体对光催化反应没有明显的促进作用,与其基本上不吸附氯仿分子有关.与TiO2胶体负载法相比,真空吸附水解法是一种较好的负载型TiO2光催化剂制备方法. 相似文献
4.
大学化学实验电势-pH曲线测定中采用的电极反应S 2H 2e-=H2S(g)的电极电势表达式有误,导致所绘制的电势-pH曲线与教科书要求不符;没有给出电极反应FeY- e-= FeY2-的标准电极电势φθ,易使学生误将电极反应Fe3 e-=Fe2 的φθ=0.771V作为电极反应FeY- e-= FeY2-的φθ;仅从两个电极反应电极电势的差值来确定脱硫氧化-还原反应的最佳pH范围不够全面,应结合溶液中络合物的稳定性、液相催化湿法脱硫原理、脱硫溶液pH对H2S吸收反应的影响、对再生反应的影响和脱硫过程的经济性等多方面考虑,使学生有全面综合的认识. 相似文献
5.
Pt/Au双金属纳米粒子的制备及表征 总被引:6,自引:1,他引:6
Poly (N-vinyl-2-pyrrolidone)-protected Pt/Au bimetallic nanoparticles were obtained by reducing the mixture of HAuCl4 and H2PtCl6 with sodium borohydride. UV-vis spectra, transmission electronic microscopy and X-my diffraction reveal that the prepared bimetallic nanoparticles are of alloy structure. 相似文献
6.
用溶胶 凝胶法制备了一系列掺杂钼量不同的TiO2纳米薄膜.用XRD,SEM和CAS(ContactAngleSystem)对TiO2薄膜的结构和性能进行了表征.结果表明,Mo6+掺杂浓度对薄膜的热致亲水性和光致亲水性均有影响,当掺Mo6+质量分数为0.75%,热处理温度为400℃时,掺钼TiO2薄膜在黑暗中放置72h后仍能表现超亲水性. 相似文献
7.
负载型无铬超细铁基变换催化剂的制备和催化性能 总被引:11,自引:0,他引:11
以镁铝尖晶石为载体,以过渡金属氧化物为助剂,用吸附γ-Fe2O3胶体法制备了负载型无铬铁基变换催化剂.TEM,XRD,BET和活性测试结果表明,采用胶体负载法制备的变换催化剂,其活性组分Fe3O4以分立的超细微颗粒分布在镁铝尖晶石载体表面上,颗粒之间存在一定的间隔.过渡金属氧化物NiO或V2O5能够进入Fe3O4晶格形成固溶体,起到代替氧化铬的作用,提高催化活性.负载型催化剂FeNi/MgAl2O4(m(NiO)/m(Fe2O3)=3%)在汽/气比为1和空速为2000h-1的反应条件下,CO转化率在400和350℃时分别为95%和80%;在高空速和低汽/气比条件下也具有很好的催化性能.稳定性实验结果表明,该催化剂
具有良好的热稳定性和一定的抗硫能力.与非负载型催化剂相比,负载型催化剂具有更为优越的催化性能. 相似文献
8.
Fe3+/V5+/TiO2复合纳米微粒光催化性能的研究 总被引:29,自引:1,他引:29
采用溶胶凝胶法制备了Fe^3 /V^5 /TiO2复合纳米微粒作为光催化剂。光降解反应结果表明,其掺杂催化剂Fe^3 /V^5 /TiO2的光催化活性明显提高。光电化学研究显示,铁离子可以成为电荷陷阱,促进空穴的界面传递反应。适量钒离子掺杂使TiO2电极的光电流升高,导带中电子浓度的增大,加快了界面的电子传递反应。共掺杂催化剂中,Fe^3 、V^5 分别提供了空穴与电子的陷阱,同时加快了电子与空穴的界面传递反应,从 更有效地提高光催化活性。双组份共掺杂为提高TiO2光催化活性提供新的途径。 相似文献
9.