Evidence of polymorphic transformations of Sn under high pressure

The high-pressure polymorphs and structural transformation of Sn were experimentally investigated using angledispersive synchrotron x-ray diffraction up to 108.9 GPa. The results show that at least at 12.8 GPa β-Sn→bct structure transformation was completed and no two-phase coexistence was found. By using a long-wavelength x-ray, we resolved the diffraction peaks splitting and discovered the formation of a new distorted orthorhombic structure bco from the bct structure at 31.8 GPa. The variation of the lattice parameters and their ratios with pressure further validate the observation of the bco polymorph. The bcc structure appears at 40.9 GPa and coexists with the bco phase throughout a wide pressure range of40.9 GPa–73.1 GPa. Above 73.1 GPa, only the bcc polymorph is observed. The systematically experimental investigation confirms the phase transition sequence of Sn as β-Sn→bct→bco→ bco + bcc→bcc upon compression to 108.9 GPa at room temperature.     

Unusual softening behavior of yield strength in niobium at high pressures

In situ synchrotron angle-dispersive x-ray diffraction experiments on niobium powders have been conducted at pressures up to 61 GPa and room temperature using the diamond anvil cell technique. From the full width at half maximum of the measured diffraction lines, the yield strength was derived with the line-width analysis theory. The niobium powder sample was found to be compressed more packed firstly and then yielded at~14 GPa–18 GPa. Following an initial increase in the yield strength with pressure, an obvious decrease was observed occurring at ~42 GPa–47 GPa accompanying with a typical pressure dependence above 47 GPa. The experimentally observed anomalous softening of the yield strength in niobium surprisingly follows the trend of the predicted unusual softening in the shear modulus by the recent theoretical investigations. The possible mechanisms, applicable to interpret the yield strength softening of materials at high pressure,were also discussed in detail.