一种新型锂离子电池用聚合物电解质复合膜的制备和性能表征

阐述了一种新型锂离子电池用PVDF-HFP(聚偏氟乙烯-六氟丙烯聚合物树脂)基聚合物电解质复合膜的制备过程. 对复合膜中使用的无机TiO2纳米颗粒进行固体超强酸化处理, 并进行颗粒表面酸强度H0测试、XRD晶体结构分析以及复合膜的电解液吸附率测试和电化学阻抗谱测试. 采用PE无纺布支撑体作为增强材料, 以浸涂方法制备复合膜,并进一步组装为锂离子电池, 性能测试表明该电池具有良好的电化学性能.     

非晶Si/SiO2超晶格的制备及其光谱研究

用磁控溅射方法在玻璃基底上制备了非晶Si/SiO₂超晶格.利用透射电子显微镜 (TEM) 和X射线衍射技术对其结构进行了分析,结果表明,超晶格中Si层大部分区域为非晶相,局域微区呈现有序结构,其厚度由1.8—3.2nm变化,SiO₂层厚度为4.0nm.并采用多种光谱测量技术,如吸收光谱、光致发光光谱和Raman光谱技术,对该结构的光学性质进行了系统研究.结果表明,随纳米Si层厚度的减小,光学吸收边以及光致荧光峰发生明显蓝移,Raman峰发生展宽,即观测到明显的量 关键词：     

Formation of Interfacial Layers in LaAlO3/Silicon during Film Deposition

We have studied the interracial reactions between amorphous LaAlO3 thin films and Si substrates, using high- resolution transmission electron microscopy and x-ray photoelectron spectroscopy. It has been shown that the interracial layer between LaAlO3 film and Si substrate chemical states show that the ratio of La 4d3/2 to Al 2p is SiLaxAlyOz. The depth distributions of La, Si and Al of the interfacial layer remains unchanged with the depth compared to that of the LaAlO3 film. Moreover, the Si content, in the interracial layer gradually decreases with increasing thickness of the interracial layer. These results strongly suggest that the Al element is not deficient in the interracial layer, as previously believed, and the formation of a SiLaxAlyOz interracial layer is mainly due to the diffusion of Si from the substrate during the LaAlO3 film deposition. With the understanding of the interracial layer formation, ones can control the interface characteristics to ensure the desired performances of devices using high-k oxides as gate dielectrics.     

Optical Properties of Co-BaTiO3/Mg（100） Nano-Composite Films Grown by Pulsed Laser Deposition Method

Co nanoparticles embedded in a BaTiO3 matrix, namely Co-BaTiO3 nano-composite films are grown on Mg（100） single crystal substrates by the pulsed laser deposition （PLD） method at 650℃. Optical properties of the CoBaTiO3 nano-composite films are examined by absorption spectra （AS） and photoluminescence （PL） spectra. The results indicate that the concentration of Co nano-particles strongly influences the electron transition of the Co BaTiO3 nano-composite films. The PL emission band ranging from 1.9 to 2.2eV is reported. The AS and PL spectra suggest that the band gap is in the range of 3.28-3.7eV.     

GROWTH MODE OF Cu-RICH PARTICLES ON LASER-ABLATED YBa2Cu3O7 THIN FILMS

The microstructure of the laser-ablated YBa₂Cu₃O₇ (YBCO) thin film deposited on heated (100) SrTiO₃ substrate was examined by transmission electron microscope. The par-ticles on the film mainly consist of CuO and few CuYO₂. Most of these non-superconducting particles nucleate on or near the surface of the film and protrude about 100-400 nm in height, A large amount of a-axis YBCO grains also exist in the film, which nucleate at the substrate surface and grow perpendicularly above the c-axis YBCO film. The YBCO thin film deposited under low oxygen pressure has very different microstructure compared with YBCO thin film deposited under high oxygen pressure.     

在GaAs-Al矩形光栅界面上表面增强二次谐波产生

我们以GaAs-Al矩形光栅界面为例具体推导了二次谐波产生的公式.依据Bloembergen和Pershan关于非线性介质的理论,用微扰论方法求解了麦克斯韦方程.理论公式和数值计算均表明,表面增强二次谐波起源于共振激励表面电磁波.     

用红外激光脉冲触发半绝缘GaAs光电导开关的实验研究

报道了用光子能量低于GaAs禁带宽度的红外激光脉冲，触发电极间隙为3mm和8mm的半绝缘GaAs光电导开关的实验结果。使用单脉冲能量为1.9mJ的1 064nm Nd:YAG激光触发开关， 在偏置电压分别为3kV和5kV条件下，光电导开关分别工作于线性和非线性模式。用900nm半导体激光器和1 530nm掺铒光纤激光器分别进行触发实验，得到了重复频率分别为5kHz和20MHz的电脉冲波形。结果表明，半绝缘GaAs光电导开关可以吸收大于本征吸收限波长红外激光脉冲。     

激光分子束外延制备高质量的YBCO超导薄膜

利用活化气体做氧源,使生长气压比普通脉冲激光沉积方法(PLD)低2～3个数量级,用激光分子束外延在SrTiO₃(100)衬底上制备出临界转变温度T_c0=85～87K,临界电流密度J_c≥1×10⁶A/cm²的高质量YBCO超导薄膜.原子力显微镜(AFM)测得表面无明显颗粒,均方根粗糙度约为7.8nm.在这种薄膜基础上制备的Josephson量子干涉器件(DC-SQUID)具有良好的温度循环稳定性.     

BaTiO3 /SrTiO3超晶格的激光分子束外延生长与二阶光学非线性研究

使用激光分子束外延 ,在SrTiO₃ ( 1 0 0 )单晶衬底上成功生长了一系列c轴取向的 ,具有原子量级控制精度的BaTiO₃/SrTiO₃超晶格 .利用晶格失配导致的薄膜表面台阶密度的周期性变化 ,讨论了反射式高能电子衍射 (RHEED)强度在BaTiO₃ 层和SrTiO₃ 层中的周期性调制 .系统研究了二阶非线性光学极化率同超晶格结构的关系 .实验测量和理论拟合结果表明 ,BaTiO₃ /SrTiO₃ 超晶格的二阶非线性光学极化率显著增强 ,其最大值比BaTi₃体单晶提高一个数量级以上 .从应力导致的晶格畸变和极化增强出发 ,讨论了二阶光学非线性增强的物理机制     

金属Fe薄膜的PLD制备及其非线性光学性质研究

采用脉冲激光沉积（PLD）技术在MgO基片上制备了金属Fe薄膜.利用原子力显微镜研究了不同制备温度对薄膜表面形貌的影响.x射线衍射分析表明沉积温度大于500℃时，Fe薄膜在MgO基片上有很好的结晶性，并有单一取向.通过z扫描方法测量了超薄Fe膜的光学非线性，得到了Fe薄膜的非线性折射率n₂＝709×10^-5cm²/ kW，非线性吸收系数 β＝-552×10^-3cm/W. 关键词： Fe薄膜 非线性 脉冲激光沉积