Field-ion microscopy(FIM),a tool for surface analysis with atomic resolution,has been employed to observe the end structure of single-walled carbon nanotubes(SWCNTs).FIM images revealed the existence of open SWCNT ends,Amorphous carbon atoms were also observed to occur around SWCNTs and traditional field evaporation failed to remove them.Heat treatment was found to be efficacious in altering the end structures of SWCNT bundles.Carbon and oxygen atoms released from heated tungsten filament are believed to be responsible for the decoration imposed on the SWCNT ends. 相似文献
2.
3.
砷掺杂的ZnO纳米线的发光特性 总被引:3,自引:0,他引:3
在GaAs基底上制备了高质量的直径为10~100 nm、长度约几个微米的As掺杂ZnO纳米线. 扫描电镜、EDX分析及透射电镜分析显示, ZnO纳米线具有较好的晶态结构. 对As掺杂前后的ZnO纳米线进行光学特性测量, 结果表明, ZnO纳米线在385 nm处有较强的紫外发光峰, 在505 nm左右有较弱的蓝绿发光峰; As掺杂较大地改变了ZnO纳米线的发光性质, 使本征发光峰移到393 nm处, 蓝绿发光强度有了很大程度的提高. 相似文献
4.
5.
6.
采用化学气相沉积(CVD)的方法在砷化镓基底上合成直径为20 nm左右、长约数十微米的氧化锌纳米线,然后采用热扩散的方法,将生长于砷化镓基底之上的氧化锌纳米线通过600 ℃,30 min的有氧退火处理后,获得了砷掺杂的氧化锌纳米线.将获得的掺杂后的氧化锌纳米线采用电子束曝光以及真空溅射镀膜的方法将钛/金合金作为接触电极引出,从而构建成场效应晶体管.文中研究了单根氧化锌纳米线砷掺杂前后的电学特性,证实了通过砷掺杂来获得p型的氧化锌纳米线的可行性.构建的p型砷掺杂氧化锌场效应晶体管的跨导为35 nA/V,载流
关键词:
p型ZnO纳米线
砷掺杂
场效应晶体管
光致发光 相似文献
7.
THEORETICAL DEPENDENCE OF LONG WAVELENGTH PHOTOEMISSION UPON THE SIZE OF Ag NANOPARTICLES EMBEDDED IN BaO SEMICONDUCTOR THIN FILM 总被引:1,自引:0,他引:1 下载免费PDF全文
The dependence of long wavelength photoemission upon the size of Ag nanoparticles embedded in a BaO semiconductor is predicted and discussed theoretically. The calculated results show that the increase in the diameter of the Ag nanoparticle, in the range from 1.5 to 37.0nm, leads to the emergence of a roughly Gaussian form of the photoemission spectra and the peaks become markedly narrower. The results also show that the increase in the diameter of the Ag nanoparticle leads to the decrease of the long wavelength threshold. The incident light wavelength corresponding to the peak value of the photoemission gets bigger with the increase of the size of Ag nanoparticles, thus showing a redshift. 相似文献
8.
9.
用真空蒸发沉积的方法制备了纳米稀土(La、Nd、Sm)粒子 BaO介质薄膜.研究表明薄膜的光电发射光谱响应阈值受纳米稀土粒子形状和大小的影响,球形纳米稀土(Sm)粒子 BaO介质薄膜的光谱响应阈值波长为720 nm,条状纳米稀土(La和Nd)粒子 BaO介质薄膜阈值波长分别为650 nm和660 nm.研究得到纳米稀土粒子 介质薄膜等效界面位垒高度在1.7~2.0 eV之间.由于纳米稀土粒子与BaO介质各自逸出功不同,当构成薄膜后使得纳米粒子周围的空间电荷分布发生变化,纳米粒子周围的能带发生弯曲. 相似文献
10.
采用化学气相沉积方法制备的碳纳米管,用酸溶液进行弱氧化处理,经适当温度在大气中烧 灼后碳纳米管发生弯曲,在样品中出现大量的环状结构. 利用原子力显微镜、透射电子显微 镜和扫描电子显微镜对典型环直径为300 nm的碳纳米管环进行了表征. 烧灼温度和烧灼时间 对环的结构和产率有重要的影响. 实验数据统计结果表明,烧灼温度在510—530℃区间内 可得到超过40%的碳纳米管环产率,并且烧灼时间延长到120 min有利于提高碳纳米管环的产 率. 在加热情况下,碳纳米管端结合的羧基官能团脱水成酯,导致弯曲的碳纳米管结合成环 .
关键词:
碳纳米管环
化学气相沉积 相似文献