本文研究了用低压金属有机化合物汽相外延(LP-MOCVD)技术在(100)InP衬底上生长InGaAsp体材料及InGaAP/InP量子阱结构材料的生长条件。三甲基镓(TM63)、三甲基铟(TMh)和纯的砷烷(A8H3)、磷烷(PH3)分别用作Ⅲ族和Ⅴ族源,在非故意掺杂情况下,InGaAsP材料的载流子浓度为3.6×1015cm-3;在液氦温度和室温下,与InP晶格匹配的InGaAsP光致发光半峰宽分别为19.2meV和63meV;对外延层的组分及厚度均匀性分别进行了转靶X光衍射仪,低温光致发光和扫描电子显微镜分析,对不同阱宽的量子阱结构材料测出了由于量子尺寸效应导致光致发光波长随阱宽增加而红移现象。 相似文献
2.
Effect of Different Substrate Temperature on Sb-Doped ZnO Thin Films Prepared by Pulsed Laser Deposition on Sapphire Substrates
下载免费PDF全文
![点击此处可从《中国物理快报》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Sb-doped ZnO thin films are deposited on c-plane sapphire substrates by pulsed laser deposition. Hall results indicate that the conductivity of the Sb-doped ZnO thin films is strongly dependent on the substrate temperature. The sample deposited at the temperature of 550°C exhibits p-type conductivity. It gives a resistivity of 15.25Ω・cm, with a Hall mobility of 1.79cm2V-1s-1 and a carrier concentration of 2.290×1017cm-3 at room temperature. The x-ray diffraction indicates that the Sb-doped ZnO thin films deposited in the range of 450-650°C are high c-axis oriented. Low-temperature photoluminescence spectra indicate that the sample deposited at 550°C shows the strong acceptor-bound exciton (A0X) emission. 相似文献
3.
Effect of Different Substrate Temperature on Phosphorus-Doped ZnO Thin Films Prepared by PLD on Sapphire Substrates
下载免费PDF全文
![点击此处可从《中国物理快报》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Phosphorus-doped ZnO (ZnO:P) thin films are deposited on a c-plane sapphire in oxygen at 350℃, 450℃, 550℃ and 650℃, respectively, by pulsed laser deposition (PLD), then all the ZnO:P samples are annealed at 650℃ in oxygen with a pressure of 1 × 10^5 Pa. X-ray diffraction measurements indicate that the crystalline quality of the ZnO:P thin films is improved with the increasing substrate temperature from 350℃ to 550℃. With a further increase of the deposition temperature, the crystalline quality of the ZnO:P sample is degraded. The measurements of low-temperature photoluminescence spectra demonstrate that the samples deposited at the substrate temperatures of 350℃ and 450℃ show a strong acceptor-bound exciton (A^0X) emission. The electrical properties of ZnO:P films strongly depend on the deposition temperature. The ZnO:P samples deposited at 350℃ and 450℃ exhibit p-type conductivity. The p-type ZnO:P film deposited at 450℃ shows a resistivity of 1.846Ω·cm and a relatively high hole concentration of 5.100 × 10^17 cm^-3 at room temperature. 相似文献
4.
衬底温度对PLD方法制备的ZnO薄膜的光学和电学特性的影响 总被引:1,自引:0,他引:1
利用脉冲激光沉积法(PLD)在c面蓝宝石衬底上制备了ZnO薄膜并对其进行了X射线衍射(XRD)、反射式高能电子衍射(RHEED)、光致发光(PL)谱和霍尔(Hall)测试.RHEED和XRD分析表明,温度在350℃至550℃之间时,ZnO薄膜的结晶质量随着衬底温度的升高而提高,当衬底温度进一步升高后,ZnO薄膜的结晶质量开始下降.四个样品中,衬底温度为550℃的样品具有最清晰的规则点状RHEED图像和半高宽最窄的(0002)衍射峰.PL谱和Hall测量的结果表明,衬底温度为550℃的样品还具有最好的发光性质和最大的霍尔迁移率. 相似文献
5.
利用选择液相外延的方法制备GaAs微尖阵列,通过扫描电子显微镜对微尖形貌进行了表征,并对此微尖阵列进行了场发射性能测试。结果表明,选择液相外延法制备的GaAs微尖呈金字塔状,两对面夹角为71°;微尖高度由生长窗口的尺寸决定,对底边为60μm的微尖,其高度约为42μm。此微尖阵列排列规则,具有场发射特性,开启电场约为5.1V/μm。发射电流稳定,当电场由8.0V/μm增加到11.9V/μm,发射电流由6μA增到74μA,在发射时间超过3h的情况下,电流波动不超过3%。另外,GaAs微尖阵列场发射的F-N曲线不为直线,分析表明是表面态和场渗透共同作用的结果。这对GaAs微尖阵列在场发射阴极方面的进一步研究具有重要的意义。 相似文献
6.
7.
采用脉冲激光沉积(PLD)法在单晶Si(100)衬底上生长ZnO薄膜,以X射线衍射(XRD)、原子力显微镜(AFM)和透射电镜(TEM)等手段分析了所得ZnO薄膜的晶体结构和微观形貌。优化工艺(700℃,20Pa)下生长的ZnO薄膜呈c轴高度择优取向,柱状晶垂直衬底表面生长,结构致密均匀。室温光致发光(PL)谱分析结果表明,随着薄膜生长时O2分压的增大,近带边紫外发光峰与深能级发光峰之比显著增强,表明薄膜的结晶性能和化学计量比都有了很大的改善。O2分压为20Pa时所生长的ZnO薄膜具有较理想的化学计量比和较高的光学质量。 相似文献
8.
任意截面光波导的模式计算 总被引:4,自引:0,他引:4
提出了一种计算近理想形状任意截面光波导模式特性的方法。首先运用微扰理论计算出光波导的电磁场分布,然后从麦克斯韦方程出发推导出一个计算光波导传播常数的公式并由此得出其色散曲线,该方法没有繁杂的计算过程。 相似文献
9.
10.
本文研究了用低压金属有机化合物汽相外延(LP-MOCVD)技术在(100)InP衬底上生长InGaAsp体材料及InGaAP/InP量子阱结构材料的生长条件。三甲基镓(TM63)、三甲基铟(TMh)和纯的砷烷(A8H3)、磷烷(PH3)分别用作Ⅲ族和Ⅴ族源,在非故意掺杂情况下,InGaAsP材料的载流子浓度为3.6×1015cm-3;在液氦温度和室温下,与InP晶格匹配的InGaAsP光致发光半峰宽分别为19.2meV和63meV;对外延层的组分及厚度均匀性分别进行了转靶X光衍射仪,低温光致发光和扫描电子显微镜分析,对不同阱宽的量子阱结构材料测出了由于量子尺寸效应导致光致发光波长随阱宽增加而红移现象。 相似文献