采用固相合成法制备了Nd:Y3Al5O12(Nd:YAG)透明激光陶瓷.用V型棱镜法测量了Nd:YAG陶瓷的折射率.用干涉仪测量了陶瓷的光学均匀性.测试了Nd:YAG透明陶瓷的透过光谱、吸收光谱和荧光光谱,在1064 nm的直线透过率达到80%以上,并计算其吸收系数、吸收截面和发射截面.根据Judd-Ofelt理论,拟合出晶体场强度参数Ωt(t=2, 4, 6)为:Ω2=0.32×10-20 cm2, Ω4=2.72×10-20 cm2, Ω6=5.39×10-20 cm2.荧光辐射寿命τrad为248.61 μs,计算的荧光分支比β为:β1=34.613%, β2=52.814%, β3=10.697%, β4=0.621%.并将Nd:YAG陶瓷的吸收光谱、荧光光谱与Nd:YAG单晶进行了对比. 相似文献
2.
用提拉法生长了掺铬、钕的钆镓石榴石(Cr^4 ,Nd^3 :GGG)自调Q激光品体。报道了室温下的吸收光谱和荧光光谱特性。分析了Cr离子浓度对光谱性质的影响。比较了Cr^4 :GGG,Nd^3 :GGG和(Cr^4 ,Nd^3 ):GGG晶体吸收光谱的关系。测量了(Cr^4 ,Nd^3 ):GGG晶体和Nd^3 :GGG晶体的荧光寿命,它们分别是33μs和250μs。实验表明,(Cr^4 ,Nd^3 ):GGG晶体是一种非常有潜力的自调Q激光晶体,可以实现大功率激光器的小型化和全固态化。 相似文献
3.
采用提拉法生长了Yb3+掺质浓度为5;原子分数、 50;原子分数和100;原子分数的Yb:Y3Al5O12(Yb: YAG)晶体,系统地分析了不同Yb3+掺质浓度晶体的吸收光谱和荧光光谱.从吸收峰和吸收系数可以看出采用940nm LD泵浦三种不同浓度的Yb:YAG晶体都比较合适.随着Yb3+离子掺质浓度的增高,晶体中出现的自吸收现象越为明显.通过对三种不同Yb掺质浓度晶体激光性能参数的计算,得出高掺质浓度Yb:YAG和YbAG晶体是有前景的激光增益介质. 相似文献
4.
Transparent Nd:YAG/YAG composite ceramics are synthesized by solid-state reaction method using high- purity Y203, A1203, and Nd203 powders as raw materials. The mixed powder compacts are sintered at 1780 ℃ for 10 h under vacuum and annealed at 1450 ~C for 20 h in air. The Nd:YAG/YAG ceramics exhibit a pore free structure with an average grain size of about 30 μm. The microstructure of the Nd:YAG/YAG composite transparent ceramics is studied and there is no interface between Nd:YAG and YAG ceramics. The Nd ion distribution in one grain is also studied, which shows that there is no segregation of Nd ions as in Nd:YAG crystals. 相似文献
5.
Lasers from a Tm:YAG slab is end-pumped by continuous-wave output of the Tm:YAG ceramic ceramic am~e reported for the t~rst time to our best knowledge. The Tm:YAG ceramic a laser diode with central wavelength 792nm. At room temperature, the maximum power is 4.5 W, and the sloping efficiency is obtained to be 20.5%. The laser spectrum is centered at 2015nm. 相似文献
6.
Comparative spectroscopic investigation
of Yb-doped YAG, YSAG and YLaO3 transparent ceramics 下载免费PDF全文
Transparent Yb doped YAG, YSAG and YaLaO3 ceramics are fabricated by using the co-precipitation method. The spectral properties and thermal parameters of these Yb doped cubic phase transparent ceramics are compared, and their different and potential applications are also analysed. The absorption cross-section and the emission cross-section of these ceramics are measured and calculated. The essential properties of these materials especially for the rep-rated pulsed high-energy diode-pumped solid-state lasers are investigated. The results show that Yb doped YAG, YSAG and YaLaO3 are all suitable materials used for diode-pumped solid-state lasers. 相似文献
7.
用提拉法生长了掺铬、钕的钆镓石榴石(Cr4+,Nd3+∶GGG)自调Q激光晶体。报道了室温下的吸收光谱和荧光光谱特性。分析了Cr离子浓度对光谱性质的影响。比较了Cr4+∶GGG,Nd3+∶GGG和(Cr4+,Nd3+)∶GGG晶体吸收光谱的关系。测量了(Cr4+,Nd3+)∶GGG晶体和Nd3+∶GGG晶体的荧光寿命,它们分别是33μs和250μs。实验表明,(Cr4+,Nd3+)∶GGG晶体是一种非常有潜力的自调Q激光晶体,可以实现大功率激光器的小型化和全固态化。 相似文献
8.
用提拉法生长了掺铬、钕的钆镓石榴石(Cr^4 ,Nd^3 :GGG)晶体,研究了室温下的吸收光谱和荧光光谱性质,以及晶体中Cr离子浓度对Nd离子光谱性质的影响。应用Judd—ofelt理论计算了强度参数Ωt(t=2,4,6),自发辐射跃迁几率、荧光分支比和辐射辱命等光谱参数。应用McCumber理论计算^4F3/2→^4I11/2能级跃迁的受激发射截面。结果表明:Cr^3 在300~900nm之间较强地增加了吸收截面,尤其是伴随Cr^3 →Nd^3 有效的能量转移。Cr^4 在1.06μm附近的吸收减弱了Nd离子的发射截面。 相似文献
9.
10.
采用提拉法生长了Yb3+掺杂量分别为5.4at%, 16.3at%, 27.1at%, 53.6at%和100at%的Yb:Y3Al5O12晶体.系统地表征和分析了Yb3+掺杂量对晶体吸收光谱和荧光光谱的影响.随着Yb3+掺杂量的增加,各峰值吸收系数呈线性增加的趋势.应用Smakula公式计算了各吸收峰对应的振荡强度,并分析了Yb3+掺杂量对振荡强度的影响.当Yb3+掺杂量增加到27.1at%时观察到了荧光猝灭现象;当Yb3+掺杂量增加到53.6at%时,荧光光谱的线形发生了很大的变化. 相似文献