贮氢材料电极循环寿命的定量预测定时放电半衰期法的应用

贮氢材料电极循环寿命的定量预测定时放电半衰期法的应用韩剑文，袁满雪，周作祥，赖城明（南开大学化学系天津３０００７１）关键词：贮氢电极，循环寿命，半衰期。前文￣［１］讨论了应用定终点电位放电半衰期法来预测贮氢材料电极循环寿命的问题。本文讨论如何采用定时...     

电化学法测定几种稀土贮氢合金的热力学函数

贮氢材料由于能可逆地吸放氢,得到了广泛地应用.特别是以贮氢材料为负极制成的氢镍二次电池,容量为同类型镉镍电池的1.5～2倍,且电压又相近,是镉镍电池的理想换代产品,受到人们普遍的关注。LaNi_(4.5)Mn_(0.5),LaNi_(4.9)Sn_(0.1)和La_(0.8)Nd_(0.2)Ni_(2.5)Co_(2.4)Al_(0.1)是电化学性能较优越的贮氢合金。LaNi_(4.5)Mn_(0.5)的电化学容量高,理论容量可达400mAh.g~(-1).LaNi_(4.9)Sn_(0.1)和La_(0.8) Nd_(0.2)     

锆系Laves相储氢合金电极的性能研究

Ｚｒ（Ｖ０．２Ｍｎ０．２Ｍｏ０．０６Ｎｉ０．５４）２．４合金经ＨＦ溶液处理后，合金表面由富Ｚｒ和富Ｍｎ层转变成富Ｎｉ层，从而使电极初期活化周期明显缩短，电极表面氢吸附性能改善。表面反应电阻减小。本文探讨了上述电极表面反应机理，即表面Ｎｉ的催化、氢吸附和氢转移机理，对阻抗谱进行拟合，给出了相应的电极反应等效电路。     

金属蒸气合成法制备燃料电池电极催化剂Ⅰ.Ag_n/C电极的制备及性质

金属蒸气合成法(MVS)已用于新材料的制备。我们曾报道用此法制备负载型金属催化剂。本文报道用MVS法制备的Ag_n/C燃料电池电极的结构与催化性能。     

Maxima and minima of independent and non-identically distributed bivariate Gaussian triangular arrays

In this paper, joint limit distributions of maxima and minima on independent and non-identically distributed bivariate Gaussian triangular arrays is derived as the correlation coefficient of ith vector of given nth row is the function of i/n. Furthermore, second-order expansions of joint distributions of maxima and minima are established if the correlation function satisfies some regular conditions.     

一类非平稳高斯序列超过数点过程与和的渐近性

设{X_i}_(i=1)~∞是标准化非平稳高斯序列,N_n为X_1,X_2,…,X_n依次对水平μ_(n1),μ_(n2),…,μ_(nn)的超过数形成的点过程.记Υ_(ij)=X_iX_j,S_n=■X_i.当Υ_(ij)满足一定条件时,证明了N_n依分布收敛到Poisson过程,且N_n与S_n渐近独立.     

Mg1.8La0.2Ni-xNi nanocomposites for electrochemical hydrogen storage

Mg1.8La0.2Ni hydrogen storage alloy was ball-milled with Ni powder, leading to the formation of a nanocrystalline and amorphous microstructure with particle sizes less than 50 nm in diameter. Each sample was examined by transmission electron microscopy (TEM), energy-dispersive spectroscopy (EDS), and X-ray diffraction (XRD). This structure was beneficial for the reduction of electrochemical impedance, as well as significant improvement of its discharge capacity, cycle life, and rate capability for electrochemical hydrogen storage in an alkaline solution. When the molar ratio (x) of Ni over Mg1.8La0.2Ni was equal to 2, the dehydriding capacity reached 2.55 wt % from electrochemical pressure-temperature isotherms (P-C-T). It was in good agreement with its initial discharge capacity, 716 mA*h/[g of (Mg1.8La0.2Ni)], observed from the electrochemical charge and discharge process. After 50 cycles, its discharge capacity still reached 381 mA*h/[g of (Mg1.8La0.2Ni)]. Further results showed that this composite had a promising high rate capability. At the current density of 1200 mA/g its discharge capacity reached 48% of its initial capacity.     

Pickands型估计的推广

本文把Ｐｉｃｋａｎｄｓ型估计推广到更一般情形，证明了它的相合性，强收敛速度．     

电化学方法测定氢在TiNi貯氢合金中的扩散系数

在20±0.3 ℃时, 用电化学方法测得氢在TiNi贮氢合金中的扩散系数为(6.45±0.78)×10~(-7)cm~2sec~(-1), 氢在这种合金中扩散过程的活化能为16.59 kJ mol~(-1)。TiNi合金电极在NaOH溶液中, 经过多次电化学渗氢以后, 在合金表面覆盖着一层钛的氧化物, 在这氧化物层的下面为富镍层。     

Co对Ni（OH）2电极中质子扩散行为的研究

本文采用恒电位阶跃，循环伏安及恒电流放电池，考察含Ｃｏ量０％－５３％的Ｎｉ（ＯＨ）２电极充电过程中质子的扩散系数：充电过程该值为１０＾－９－１０＾－１０ｃｍ＾２／ｓ，放电过程则为１０＾－１１ｃｍ＾２／ｓ．数据处理时对文献中有关公式进行了修正。