NiZnCu ferrite applied for LTCC microinductor

This paper describes the fabrication of thin magnetic layers for an LTCC planar-type inductor with a 0.11 mm thickness. The thin ferrite layers were fabricated by tape casting method. Synthesis conditions and X-ray analysis (300 K) of the Ni_0.3Zn_0.62Cu_0.08Fe₂O₄ ferrite are presented. A pure cubic, Fd 3m crystal structure was observed for the Ni_0.3Zn_0.62Cu_0.08Fe₂O₄ ferrite. The complex impedance and dielectric permittivity of Ni_0.3Zn_0.62Cu_0.08Fe₂O₄ ferrite were determined as a function of temperature (from −55 to 170 °C) and frequency (from 10 Hz to 2 MHz). Dc resistivity was measured in a temperature range from −55 to 170 °C. Magnetization and magnetic hysteresis were measured by a vibrating sample magnetometer (VSM) in an applied magnetic field up to 60 kOe. The inductance and quality factor were measured in a frequency range 0.1-120 MHz. With the help of finite elements method (FEM) simulation it is possible to calculate the elements electrical parameters and optimize the design. This paper presents a magnetic field modelling of an inductor structure.     

Analysis of nanopore arrangement and structural features of anodic alumina layers formed by two-step anodizing in oxalic acid using the dedicated executable software

Anodic porous alumina layers were fabricated by a two-step self-organized anodization in 0.3 M oxalic acid under various anodizing potentials ranging from 30 to 60 V at two different temperatures (10 and 17 ^°C). The effect of anodizing conditions on structural features and pore arrangement of AAO was investigated in detail by using the dedicated executable publication combined with ImageJ software. With increasing anodizing potential, a linear increase of the average pore diameter, interpore distance, wall thickness and barrier layer thickness, as well as a decrease of the pore density, were observed. In addition, the higher pore diameter and porosity values were obtained for samples anodized at the elevated temperature, independently of the anodizing potential. A degree of pore order was investigated on the basis of Delaunay triangulations (defect maps) and calculation of pair distribution or angle distribution functions (PDF or ADF), respectively. All methods confirmed that in order to obtain nanoporous alumina with the best, hexagonal pore arrangement, the potential of 40 V should be applied during anodization. It was confirmed that the dedicated executable publication can be used to a fast and complex analysis of nanopore arrangement and structural features of nanoporous oxide layers.     

Large-dimensional light-emitting elements with printed electroluminophore

In the paper, the influences of design and manufacturing technology on the performance of large-dimensional light-emitting elements with screen-printed luminophore are presented. The luminophore is based on Cu activated and Cl co-activated zinc sulphide ZnS. A particular instability when exposed to moisture and at rated electric load has been observed.     

Anodic alumina membranes with defined pore diameters and thicknesses obtained by adjusting the anodizing duration and pore opening/widening time

The through-hole porous anodic aluminum oxide (AAO) membranes were fabricated by a simple two-step anodization of aluminum in 0.3?M oxalic acid, 0.3?M sulfuric acid, and 2?wt.% phosphoric acid solutions under different operating conditions followed by the removal of the remaining Al substrate and the pore opening/widening process. The effect of duration of the second anodizing step on the thickness of the porous oxide layer and the influence of other anodizing conditions such as applied voltage, type of electrolyte, and purity of the substrate on the rate of porous oxide growth were discussed in detail. The pore opening procedure for all synthesized membranes was optimized, and the influence of the duration of chemical etching on structural features of AAO membranes, especially pore diameter, was studied. The rate of pore widening was established for AAO membranes formed in various anodizing electrolytes and for different temperatures of 5?wt.% H₃PO₄ used for alumina dissolution.     

The effect of anode surface area on nanoporous oxide formation during anodizing of low purity aluminum (AA1050 alloy)

Porous anodic alumina layers were obtained by a simple two-step anodization of low purity aluminum (99.5 % Al, AA1050 alloy) in a 0.3 M oxalic acid electrolyte at 45 V and 20 °C. The effect of anode surface area on structural features of nanoporous oxide and process of oxide formation was investigated. An ordered structure composed of nanostripes or nanopores was formed on the Al surface during electrochemical polishing in a mixture of perchloric acid and ethanol. This nanopattern is then replicated during the anodic oxide formation. It was found that the pore diameter, interpore distance, and porosity increase slightly with increasing surface area of the aluminum sample exposed to the anodizing electrolyte. On the other hand, a slight decrease in pore density and cell wall thickness was observed with increasing surface area of the sample. The detailed inspection of current density vs. time curves was also performed. The obtained results revealed that the higher surface area of the anode, the local current density minimum, was reached faster during first step of anodization and the increase in current density corresponding to the pore rearrangement process was observed earlier. Finally, a dense array of Pd nanowires (～90 nm in diameter) was synthesized by simple electrodeposition of metal inside the channels of through-hole nanoporous anodic alumina templates with relatively large surface areas (4 cm²).     

X-ray photoelectron spectroscopic and electrochemical impedance spectroscopic analysis of RuO2-Ta2O5 thick film pH sensors

The paper reports on investigation of the pH sensing mechanism of thick film RuO₂-Ta₂O₅ sensors by using X-ray photoelectron spectroscopy (XPS) and electrochemical impedance spectroscopy (EIS). Interdigitated conductimetric pH sensors were screen printed on alumina substrates. The microstructure and elemental composition of the films were examined by scanning electron microscopy and energy dispersive spectroscopy. The XPS studies revealed the presence of Ru ions at different oxidation states and the surface hydroxylation of the sensing layer increasing with increasing pH. The EIS analysis carried out in the frequency range 10 Hz–2 MHz showed that the electrical parameters of the sensitive electrodes in the low frequency range were distinctly dependent on pH. The charge transfer and ionic exchange occurring at metal oxide-solution interface were indicated as processes responsible for the sensing mechanism of thick film RuO₂-Ta₂O₅ pH sensors.     

Anodic alumina membranes with defined pore diameters and thicknesses obtained by adjusting the anodizing duration and pore opening/widening time

The through-hole porous anodic aluminum oxide (AAO) membranes were fabricated by a simple two-step anodization of aluminum in 0.3 M oxalic acid, 0.3 M sulfuric acid, and 2 wt.% phosphoric acid solutions under different operating conditions followed by the removal of the remaining Al substrate and the pore opening/widening process. The effect of duration of the second anodizing step on the thickness of the porous oxide layer and the influence of other anodizing conditions such as applied voltage, type of electrolyte, and purity of the substrate on the rate of porous oxide growth were discussed in detail. The pore opening procedure for all synthesized membranes was optimized, and the influence of the duration of chemical etching on structural features of AAO membranes, especially pore diameter, was studied. The rate of pore widening was established for AAO membranes formed in various anodizing electrolytes and for different temperatures of 5 wt.% H₃PO₄ used for alumina dissolution.

     

Porous alumina membranes with branched nanopores as templates for fabrication of Y-shaped nanowire arrays

Porous anodic alumina membranes with Y-branched and double-branched nanopores were fabricated by the stepwise reduction of anodizing potential during the second step of anodization carried out in 0.3 M oxalic acid. The process of nanoporous layer formation and influence of anodizing parameters on structural features of as-obtained anodic aluminum oxide (AAO) membranes were discussed in detail. The pore rearrangement process occurring after the potential decrease was investigated on the basis of the current density vs. time curves, and results were correlated with the field-emission scanning electron microscope images of the pore bottoms taken after different anodizing durations. It was found that the reorganization of nanopores begins after 600 and 500 s from the time of the potential reduction to 42 and 30 V and the process seems to be completed after about 900 and 800 s, respectively. The through-hole AAO membranes were used as templates for the fabrication of gold and polystyrene nanowires via electrochemical deposition and simple immersing in the polymer solution, respectively. The arrays of hierarchically branched nanowires were synthesized, and the dimensions of nanowires were consistent with the shape and structure of used AAO templates.