Detecting pore size distribution of activated carbon by low-field nuclear magnetic resonance

In this study, the transverse relaxation time (T₂) of activated carbon (AC) in different relative environment humidity was detected firstly by low-field nuclear magnetic resonance (LFNMR). The pore size (diameter) of AC distributions was calculated by the relationship between T₂ and surface relaxation rate (ρ), where ρ was obtained by the detection of nine porous materials with known pore size. The results showed that the pore size distributions of AC calculated by ρ < 0.19 nm/ms were in good agreement with that obtained by nitrogen adsorption method and proved that LFNMR as a new detection method was feasible for characterizing AC pore size distribution.     

Preparation and gas sensing activity of La and Y co-doped titania nanoparticles

Journal of Sol-Gel Science and Technology - A novel gas sensing material, La–Y co-doped TiO2 nanoparticles, was synthesized by sol–gel method and applied to detect organic pollutants...     

织构C60薄膜的生长与光致发光特性

用Hot Wal方法，在氟金云母单晶上生长出了（111）织构的C₆₀薄膜．用X射线衍射、Raman散射、扫描电子显微镜和原子力显微镜研究了织构C₆₀薄膜的结晶质量和结构特性．测量了织构C₆₀薄膜在室温300K和低温77K的光致发光光谱．对所得结果进行了分析与讨论 关键词：     

金属与金刚石薄膜接触的电学特性研究

用热丝辅助化学汽相沉积技术在Si衬底上合成了含少量受主型杂质的近于本征的金刚石薄膜，并研究了三种金属（Cu，Ag和Al）与它接触的电学特性，以及退火对接触特性的影响．结果表明Cu，Ag与金刚石薄膜接触的电学特性比较类似，而Al则明显不同；而且退火对它们的接触特性影响很大 关键词：     

Studies on basicity of alkali metal catron exchanged β and X zeolites by pyrrole-IR spectroscopy

The strength of basic sites has been measured by pyrrole-IR on alkali metal cation exchanged β and X zeolites, as well as NaOH loaded Naβ. The influence of cation type and the structure of zeolites on their basicity has been studied. The acidic and basic properties of the samples were investigated by NH3-TPD and isopropanol reaction. It was shown that the strength of basic sites on samples could be characterized by the shift of vNH band in the pyrrole-IR spectra. The framework oxygen charges were calculated from the Sanderson electronegativity. The changes in basic properties with various alkali metal cation are consistent with the changes of local oxygen charges of the zeolite framework.     

介质折射率对一维三元光子晶体带隙的影响

利用光学传输矩阵法,数值模拟了一维二元、三元光子晶体的带隙结构,得出:三元光子晶体的主带隙略宽于二元光子晶体的主带隙;三元光子晶体的主带隙主要取决于最高折射率的介质和最低折射率的介质,而与居于两者之间的介质关系不大,并作出了相应的关系曲线。最后推导了三元光子晶体的色散关系。     

Study of asymmetric charge writing on Pb(Zr,Ti)O3 thin films by Kelvin probe force microscopy

Polycrystalline Pb(Zr_0.55Ti_0.45)O₃ thin film was deposited on Pt/Ti/SiO₂/Si(1 0 0) by radio-frequency-magnetron sputtering method, and the writing of charge bits on the surface of PZT thin film was studied by Kelvin probe force microscopy. It is found that the surface potential of the negative charge bits are higher than those of the corresponding positive ones. When ferroelectric polarization switching occurs, the potential difference becomes even more remarkable. A qualitative model was proposed to explain the origin of the asymmetric charge writing. It is demonstrated that the internal field in the interface layer, which is near the ferroelectric/electrode interface in ferroelectric film, is likely to be the cause for the occurrence of this phenomenon.     

O′-β′复相Sialon陶瓷中相组成的控制

用Si₃N₄,SiO₂和Al₂O_?作原料,以Y₂O_?为添加剂,研究了O’-β’所在的四个相容性区中组成,于1400—1800℃之间,O’和β’的形成动力学。O’于1400℃开始生成,1600℃达到最大形成量。高于1600℃,O’减少乃至消失。研究发现,O’的这种不稳定性,并非自身热分解的结果。Al含量的增加,液相出现和β’的形成,才是导致O’-Sialon溶解而消失的原因。 此外,认为Si₃N₄-O’(x=0.3)-Y₂Si₂O₇-YAG相容性区,是在制备具有合理的O’-β’平衡相组成的复相陶瓷时,可供实际选用的组成区。     

The effects of doubly excited states on ionization balance

The effects of highly doubly excited states on ionization balance are investigated. In the calculation, A Collisional-Radiative model in Detailed-Configuration-Accounting (DCA) is applied to population calculations for NLTE plasmas. Configuration-averaged rate coefficients that needed in the rate equations are obtained based on the first order perturbation theory. The Hatree-Fock-Slater self-consistent-field method is used to calculate the electron wave functions. The mean ionization stage of high-Z plasma Lu is presented. The comparison shows that the mean ionization stage increases more than 3 stages when doubly excited states 5l6l' and 5l5l' are not included in the population calculations.     

NiTi合金中马氏体相的低频力学谱研究

我们用最近研制成功的LMA型低频力学谱测试系统对NiTi合金马氏体相进行了在很大频率范围内（0．003～1Hz）的低频等温力学谱和温度谱的测量．我们研究的形状记忆合金NiTi（Ni50．2at％）试样长34mm，直径1mm细丝．经一定热处理，分别在333K．343K和353K做了内耗随频率的变化的测量。实验表明：频率越小，内耗越大，也就是内耗随频率减少而增大。同时我们采用阶梯升温的方法在八个温度下每个温度测量三种频率（1Hz，0．1Hz，0．01Hz）的内耗，结果清楚地表明：不同频率下，内耗峰都出现在372K（99℃）。而且频率越低，峰高越高。这是具有相变峰的特点：相变峰的峰温不随测量频率不同而变化，相变峰高度随频率减少而增大。我们还测量了在1Hz与0．5Hz频率下内耗随温度的变化。本文用马氏体相的位错理论初步讨论了上述实验结果。