Large directional asymmetries were observed in photoelectron distributions from core and valence levels in metals and adsorbate atoms. Intensities varied by factors up to 25 as the angle between A and p was varied. The energy dependence of asymmetry showed atomic behavior similar to that expected for free atoms, modified for the tendency p∥A.     

Transparent conducting oxides: texture and microstructure effects on charge carrier mobility in MOCVD-derived CdO thin films grown with a thermally stable, low-melting precursor

A series of low-melting, thermally stable cadmium metal-organic chemical vapor deposition (MOCVD) precursors have been synthesized, structurally and spectroscopically characterized, and implemented in growth of highly conductive and transparent CdO thin films. One member of the series, bis(1,1,1,5,5,5-hexafluoro-2,4-pentanedionato)(N,N-diethyl-N',N'-dimethyl-ethylenediamine)cadmium(II), Cd(hfa)(2)()(N,N-DE-N',N'-DMEDA), represents a particularly significant improvement over previously available Cd precursors, owing to the low melting point and robust thermal stability. High-quality CdO films were grown by MOCVD on glass and single-crystal MgO(100) between 300 and 412 degrees C. Film growth parameters and substrate surface have large effects on microstructure and electron carrier transport properties. Enhanced mobilities observed for highly biaxially textured films grown on MgO(100) vs glass are attributed, on the basis of DC charge transport and microstructure analysis, to a reduction in neutral impurity scattering and/or to a more densely packed grain microstructure. Although single-grained films grown on MgO(100) exhibit greater mobilities than analogues with discrete approximately 100 nm grains and similar texture, this effect is attributed, on the basis of charge transport and Hall effect measurements as well as optical reflectivity analysis, to differences in carrier concentration rather than to reduced grain boundary scattering. Unprecedented conductivities and mobilities as high as 11,000 S/cm and 307 cm(2)/V.s, respectively, are obtained for epitaxial single-grained films (X-ray diffraction parameters: fwhm(omega) = 0.30 degrees, fwhm(phi) = 0.27 degrees ) grown in situ on MgO(100) at a relatively low temperature (400 degrees C).     

The synthesis and characterisation of ferromagnetic CaMn2O4 nanowires.

The synthesis of marokite CaMn(2)O(4) nanowires using a hydrothermal method is reported. Transmission electron microscopy and electron diffraction measurements show that the nanowires are polycrystalline in nature with diameters between 10 and 20 nm and lengths ranging from approximately 100 to 500 nm. Most interestingly, in contrast with the bulk material, magnetization measurements show that these nanowires exhibit ferromagnetic ordering with a Curie temperature (T(C)) of approximately 40 K.