Preliminary study of the thermally stimulated blue luminescence of ulexite

In this paper, novel results on the blue thermally stimulated luminescence (TSL) emission of ulexite (NaCaB₅O₆(OH)₆·5H₂O) have been studied. The four maxima appearing at 60, 110, 200 and 240°C on the TSL glow curves of this borate could be respectively associated to: (i) the first dehydration (NaCaB₅O₆(OH)₆·5H₂O→NaCaB₅O₆(OH)₆·3H₂O), (ii) the creation-annihilation of the three-hydrated phase, (iii) the Na-coordinated chains dehydroxylation and the starting point of the alkali self-diffusion through the lattice and (iv) the amorphisation of the lattice. These results are fairly well correlated with the differential thermal analyses (DTA), in situ thermal observations under environmental scanning electron microscope (TESEM) and thermal X-ray diffraction (TXRD) techniques.     

Crosslinked polystyrene with improved mechanical properties

The synthesis of some divinyl monomers—bis(vinylphenyl)ethane ( 2 ), bis(vinylbenzyloxy)hexane ( 3a ), and bis(vinylbenzyloxy)dodecane ( 3b ) is reported. Copolymers of the new monomers and styrene were evaluated as an alternative to divinylbenzene-crosslinked polymers for use as matrices and absorbents. The mechanical properties and the amount of residual double bonds in the copolymers were compared. It was found that the new copolymers, unlike the divinylbenzene-crosslinked polymers, retained their mechanical strength even at high crosslinking degrees. Stress at break values of 79, 68, and 18 N/mm² were found for the polymers crosslinked with 20 mol % of 3a, 2 , and divinylbenzene; 5, 25 and 45% of the divinyl units in these polymers were left as pendant double bonds. Porous styrene– 2 copolymers were synthesized and shown to have lower surface areas than the corresponding divinylbenzene-crosslinked polymers. The pore size distribution showed that this was due to the absence of the smallest pores which are found in the divinylbenzene-crosslinked polymers in between heavily crosslinked nodules. © 1993 John Wiley & Sons, Inc.