Synthesis of nano-polycrystalline diamond from glassy carbon at pressures up to 25 GPa

ABSTRACT

Nano-polycrystalline diamond (NPD) with various grain sizes has been synthesized from glassy carbon at pressures 15–25?GPa and temperatures 1700–2300°C using multianvil apparatus. The minimum temperature for the synthesis of pure NPD, below which a small amount of compressed graphite was formed, significantly increased with pressure from ～1700°C at 15?GPa to ～1900°C at 25?GPa. The NPD having grain sizes less than ～50?nm was synthesized at temperatures below ～2000°C at 15?GPa and ～2300°C at 25?GPa, above which significant grain growth was observed. The grain size of NPD decreases with increasing pressure and decreasing temperature, and the pure NPD with grain sizes less than 10?nm is obtained in a limited temperature range around 1800–2000°C, depending on pressure. The pure NPD from glassy carbon is highly transparent and exhibits a granular nano-texture, whose grain size is tunable by selecting adequate pressure and temperature conditions.     

Organic–Inorganic Hybrid Gold Halide Perovskites: Structural Diversity through Cation Size

Crystal structures of a series of organic–inorganic hybrid gold iodide perovskites, formulated as A₂[Au^II₂][Au^IIII₄] [A=methylammonium (MA) ( 1 ) and formamidinium (FA) ( 2 )], A′₂[I₃]_1−x[Au^II₂]_x[Au^IIII₄] [A′=imidazolium (IMD) ( 3 ), guanidinium (GUA) ( 4 ), dimethylammonium (DMA) ( 5 ), pyridinium (PY) ( 6 ), and piperizinium (PIP) ( 7 )], systematically changed depending on the cation size. In addition, triiodide (I₃⁻) ions were partly incorporated into the AuI₂⁻ sites of 3 – 7 , whereas they were not incorporated into those of 1 and 2 . Such a difference comes from the size of the organic cation. Optical absorption spectra showed characteristic intervalence charge-transfer bands from Au^I to Au^III species, and the optical band gap increased as the size of the cation became larger.     

Alternating copolymerization of carbon dioxide and epoxide by manganese porphyrin: The first example of polycarbonate synthesis from 1-atm carbon dioxide

The first successful example of the formation of polycarbonate from 1-atm carbon dioxide and epoxide was demonstrated by the alternating copolymerization of carbon dioxide and epoxide with manganese porphyrin as a catalyst. The copolymerization of carbon dioxide and cyclohexene oxide with (porphinato)manganese acetate proceeded under the 1-atm pressure of carbon dioxide to give a copolymer with an alternating sequence. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3549–3555, 2003     

Affinity chromatographic purification of bovine lung endothelin receptor using biotinylated endothelin and avidin-agarose.

Endothelin receptor was purified from bovine lung by affinity chromatography using biotinylated endothelin and avidin-agarose. Endothelin was biotinylated with sulphosuccinimidyl 2-(biotinamido)ethyl-1,3-dithiopropionate, a reactive form of biotin with a cleavable spacer arm containing a disulphide bond designed for a simple elution by thiols. Starting from 3.5 kg of bovine lung, about 200 micrograms of pure receptor were obtained.     

Specific interaction between polyethylenimine and azo dyes carrying hydroxyl groups

The binding of acid azo dyes having phenolic hydroxyl groups such as orange I ( I ), orange II ( II ), chrome violet ( III ), 4-hydroxyazobenzene-4′-sulfonate ( IV ), and 2,4-dihydroxyazobenzene-4′-sulfonate ( V ) by polyethylenimine was studied by equilibrium dialysis and spectroscopic methods. The results obtained indicate that dyes ( III ) and ( V ) with two OH groups are bound much more strongly than dyes ( I ), ( II ), and ( IV ) with one OH group. Also polyethylenimine is far superior to any other polymers which have been examined, including bovine serum albumin, polyvinylpyrrolidone, and poly-L -lysine, in its ability to form complexes with these dyes ( III ) and ( V ). The OH groups involved participate preferentially in complex formation with polyethylenimine. The unusual affinity of polyethylenimine for the dyes carrying OH groups is discussed.     

Sol-Gel Preparation and Photoelectrochemical Properties of Fe2TiO5 Thin Films

Polycrystalline Fe₂TiO₅ films were prepared on nesa silica glass substrates by the sol-gel method, and their photoanodic properties were measured in a three-electrode wet cell with an aqueous buffer solution of pH = 7. Gel films were crystallized into Fe₂TiO₅ when fired at 500°C. The photoanodic current significantly increased when the films were fired at 700°C, and then decreased with increasing firing temperature. Thicker films obtained by repeating the gel film deposition and firing showed smaller photocurrent, and the 50 nm thick film prepared via non-repetitive deposition exhibited the maximum photocurrent. Although the photoresponse was extended to wavelengths near 500 nm, the maximum quantum yield was as low as 0.12 at a wavelength of 340 nm.     

Sol–gel preparation and properties of hydroxypropylcellulose–titania hybrid thin films

Hydroxypropylcellulose (HPC)–titania hybrid thin films were prepared by sol–gel method where titanium tetraisopropoxide Ti(OC₃H₇ ⁱ )₄ was hydrolyzed under acidic conditions in the presence of HPC, followed by dip-coating and drying at 120 °C for 24 h. The viscosity average molecular weight of HPC was 55,000–70,000 or 110,000–150,000, and the TiO₂/(HPC + TiO₂) mass ratio ranged from 0 to 1, which was calculated on the assumption that all Ti(OC₃H₇ ⁱ )₄ is converted into TiO₂. The films were 0.35–1.0 μm thick, transparent in visible region and opaque in ultraviolet (UV) region, where the optical absorption coefficient in UV region increased with increasing titania content. The refractive index increased with increasing titania content, ranging from 1.6 to 1.8 for the hybrid thin films. The pencil hardness increased from 6B to 5H, the durability in hot water significantly increased and the contact angle of water on films increased from 35° to 89° with increasing titania content. Crack-free films could be deposited on organic polymer substrates irrespective of titania or HPC contents, where cracking did not occur at higher HPC contents even when the substrate was bent.     

Control of optical properties of gel-derived oxide coating films containing fine metal particles

Control of the optical properties of gel-derived oxide films containing fine metal particles is described. The duration of the aging of Si(OC₂H₅)₄-derived sols and the amount of water for hydrolyzing Si(OC₂H₅)₄ were found to greatly affect the size and the shape of Au particles formed in the silica matrix, and accordingly the optical absorption of the Au/SiO₂ composite films. Employing dielectric media with high refractive indices like TiO₂ was shown to shift the absorption peak of Au particles to longer wavelengths. Pd/TiO₂ and Pt/TiO₂ composite films showed absorption in the visible region.     

Binding of metal ions by polyethylenimine and its derivatives

Measurements have been made of the binding of divalent metal ions, Cu²⁺, Ni²⁺, Co²⁺, and Zn²⁺ ions, by polyethylenimine (PEI) and its acetyl or alkyl derivatives by the equilibriumdialysis technique. These metal ions, in particular the Cu²⁺ ion, exhibited tremendously remarkable binding affinity toward PEI. The extent of complexation of the polymer with the metal ions was decreased markedly by acetylation or alkylation of the polymer. PEI with no primary amine showed an appreciable decrease in its affinity for the metal ion. These results indicate the participation of the primary amine of the polymer in the formation of the complex. A cooperative binding isotherm was observed in PEI–metal ion complex formation, suggesting swelling or conformational change of the polymer induced by this coordination process. Binding of the Cu²⁺ ion by PEI was found to be essentially independent of temperature over the range 5–35°C.