Preparation and properties of sol-gel coating films

The present state of our knowledge on sol-gel coating films has been reviewed. A qualitative discussion is made on the limit of the film thickness which can be achieved in the sol-gel method and the factors affecting the film thickness. Considering that properties of the film are intimately related to the microstructure, types of microstructures accomplished by the sol-gel coating are introduced with examples.     

Preparation of Polycrystalline Antimonic Acid Films by Electrophoretic Deposition

Cubic antimonic acid (Sb₂O₅·nH₂O) films were successfully prepared on stainless steel and Si(100) substrates by electrophoretic deposition (EPD) using two types of sols. The sols were prepared by reacting an H₂O₂ aqueous solution with Sb(O-i-C₃H₇)₃ or metallic Sb powder. The resulting films were found to consist of fine particles of cubic Sb₂O₅·nH₂O single crystals with uniform particle sizes of 30 nm and 150 nm. The weight of the Sb₂O₅·nH₂O deposit on the anode Si(100) substrate by EPD increased linearly with the current density in the range of 0–0.67 mA cm^–2, when the sol pH was over 7. The proton conductivity of the polycrystalline Sb₂O₅·nH₂O discs, formed from the two types of sols, was evaluated by an ac impedance method at room temperature under controlled levels of relative humidity.     

Control of optical properties of gel-derived oxide coating films containing fine metal particles

Control of the optical properties of gel-derived oxide films containing fine metal particles is described. The duration of the aging of Si(OC₂H₅)₄-derived sols and the amount of water for hydrolyzing Si(OC₂H₅)₄ were found to greatly affect the size and the shape of Au particles formed in the silica matrix, and accordingly the optical absorption of the Au/SiO₂ composite films. Employing dielectric media with high refractive indices like TiO₂ was shown to shift the absorption peak of Au particles to longer wavelengths. Pd/TiO₂ and Pt/TiO₂ composite films showed absorption in the visible region.     

A mesoporous non-precious metal boride system: synthesis of mesoporous cobalt boride by strictly controlled chemical reduction

Generating high surface area mesoporous transition metal boride is interesting because the incorporation of boron atoms generates lattice distortions that lead to the formation of amorphous metal boride with unique properties in catalysis. Here we report the first synthesis of mesoporous cobalt boron amorphous alloy colloidal particles using a soft template-directed assembly approach. Dual reducing agents are used to precisely control the chemical reduction process of mesoporous cobalt boron nanospheres. The Earth-abundance of cobalt boride combined with the high surface area and mesoporous nanoarchitecture enables solar-energy efficient photothermal conversion of CO₂ into CO compared to non-porous cobalt boron alloys and commercial cobalt catalysts.

Generating high surface area mesoporous transition metal boride is challenging but interesting because incorporation of boron atoms can generate lattice distortion to form amorphous metal boride which has unique properties in catalysis.     