1.
CV Tomy D Pal SS Banerjee S Ramakrishnan AK Grover S Bhattacharya MJ Higgins G Balakrishnan McK Paul 《Pramana》2002,58(5-6):925-935
The weakly pinned single crystals of the hexagonal 2H-NbSe2 compound have emerged as prototypes for determining and characterizing the phase boundaries of the possible order-disorder
transformations in the vortex matter. We present here a status report based on the ac and dc magnetization measurements of
the peak effect phenomenon in three crystals of 2H-NbSe2, in which the critical current densities vary over two orders of magnitude. We sketch the generic vortex phase diagram of
a weakly pinned superconductor, which also utilizes theoretical proposals. We also establish the connection between the metastability
effects and pinning. 相似文献
2.
Summary The various techniques and methodologies of thermal conductivity measurement have been conventionally based on the determination of the rate of directional heat flow through a material having a unit temperature differential between its opposing faces. The constancy of this rate depends on the material density, its thermal resistance and the heat flow path itself. The last of these variables contributes most significantly to the true value of steady-state axial and radial heat dissipation depending on the magnitude of transient thermal diffusivity along these directions. The purpose of this paper is to exemplify the above features by defined parameters of heat flow measurement by existing methodologies. No new method is proposed here. Importantly, the relationship between the rate of heat transfer, total heat transferred and thermal conductivity at a given temperature under steady-state conditions for a fixed heat flow path will be illustrated. 相似文献
3.
Subhash C. Mojumdar 《Journal of Thermal Analysis and Calorimetry》2007,90(3):625-626
The fifth CBRATEC (V Congresso Brasileiro de Análise Térmica e Calorimetria) conference was held in April 02–05, 2006 in Poços de Caldas, MG. One third of the 370 participants was graduates and Ph.D. students well representing the continuous interest in thermal analysis among Brazilian researchers. The structure of conference was characteristic and refreshing, since every morning one of the leading Brazil thermoanalysts held an opened teaching course especially for the representatives of the young generation. After then plenary lecturers and keynote speakers (J. Rouquerol, Cs. Novák, D. Burlett, M. Suchyta and A. Riga) occupied the podium. The afternoon sessions consisted of mainly short lectures and poster exhibitions; both provided excellent possibility for the Ph.D. students to introduce their scientific work. The scope of conference covered practically all aspects of thermal analysis. Since 1998, when the first CBRATEC conference was held, the participation of young scientists and the organization of teaching courses played essential role for them. As an effort to increase international experiences, the universities pay continuous attention to foreign language education (first of all English), so the communication between the invited international researchers, the representatives of the instrument companies and the domestic conference attendants became much more efficient in recent years. During the conference the new Executive Committee was elected. Prof. Valter José Fernandes Junior was elected as President of ABRATEC supported by the members of the Executive (Jivaldo do Rosário Matos (Vice-President), Massao Ionashiro, Lázaro Moscardini D’Assunção, Clóvis Augusto Ribeiro, Elias Yuki Ionashiro, Carlos Isidoro Braga, Manoel Luiz Cunha Rodrigues, Rodrigo Maciel). In recognition of his continuous cooperation for the development of thermoanalytical researches in Brazil and its scientific divulgation in Thermal Analysis, the ‘Special Award’ of ABRATEC (Brazilian Association for Thermal Analysis and Calorimetry) was presented to Prof. Csaba Novák. For their outstanding achievements in developing the international relation of ABRATEC, Honourable Membership of the Thermoanalytical Sub-Branch of the Hungarian Chemical Society was presented to Prof. Jivaldo do Rosário Matos, Massao Ionashiro, Prof. Valter José Fernandes Junior and Prof. Éder Tadeu Gomes Cavalheiro at the opening ceremony. At last but not least, according to the decision of ICTAC Council during the 13th ICTAC (2004, Chia Laguna, Italy) Brazil was elected as the host of ICTAC 14 in 2008. The Brazilian thermoanalytical community feels extremely honored to be entrusted with the organization of the 14thICTAC Conference that will take place in São Pedro, SP, in September 14–19, 2008, where the scientists, researchers and students, who are acting in the field of thermal analysis and calorimetry are cordially invited. The link to the conference site is www.ictac14.com.br. 相似文献
4.
Mojumdar S. C. Kozánková J. Chocholoušek J. Majling J. Fábryová D. 《Journal of Thermal Analysis and Calorimetry》2004,78(1):73-82
Fluoroapatite containing glass-ceramics were prepared from Li2O-CaO-CaF2-P2O5-SiO2 system. The glass was melted at 1480°C for 1 h. The object of observation was the preparing crystal phase of fluoroapatite
in amorphous glass matrix. The morphology of lithium disilicate glass-ceramics was studied by SEM. The crystal growth and
thermal properties of fluoroapatite were studied by X-ray diffraction and DTA. The more the content of P2O5, the more the presence of fluoroapatite particles. SEM investigation clearly indicated the phase separation and formation
of a primary crystalline phase of fluoroapatite in the studied glass-ceramics. DTA curves of the fluoroapatite samples exhibit
exothermic effects in the temperature range 337-694°C depending on the composition of the materials. The position of exothermic peak for lithium disilicate on DTA curves moves with increasing specific surfacetowards lower temperatures which points on its preferential surface crystallization. As far as physical qualities are concerned,
mainly color and gloss, the best qualities of all observed materials belong to glass-ceramics with 10% P2O5.
This revised version was published online in July 2006 with corrections to the Cover Date. 相似文献
5.
Mojumdar S. C. Kozánková J. Chocholoušek J. Majling J. Nemecek V. 《Journal of Thermal Analysis and Calorimetry》2004,78(1):145-152
The conditions to fabricate the bulk porous specimens have been studied on account of sodium borosilicate (NBS) glasses. Glass
composition, heat treatment at phase separation and TiO2 addition have been considered in this study. Original glass samples of composition in mol%: sample A: 9.19 Na2O - 23.58 B2O3 - 67.23 SiO2, sample B: 9.29 Na2O - 3.17 TiO2 - 23.82 B2O3 - 63.72 SiO2 were prepared by melting reagent grade chemicals (Na2CO3, HBO3, SiO2 and AgNO3) in platinum crucibles at 1480°C for 1 h in air. The melts were poured onto stainless steel plates and were annealed at 500°C
for 0.5 h after cooling. Thus, obtained samples were phase separated at 700°C for 2, 15, 25 and 50 h to study their microstructure
by scanning electron microscope (SEM). Besides the direct study of the microstructure by SEM, information on glass structural
changes of samples are provided by measuring in situ changes by the optical transmittance thermal analysis. The isothermal
measurements were carried out at 700, 720 and 740°C. The temperature of phase separation, the leaching and nucleator addition
(TiO2), significantly influence the microstructure of the resulting leached product. TiO2 additive seems to suppress crystallization of cristobalite: especially at the extended above heat treatment phase separation
runs. The phase-separated domains of glasses containing above 80 moles of SiO2 are so small that it is very hard to observe them by SEM. The glass composition in our case was selected in a way to have
relatively large phase separated areas easily observed by SEM at magnification 20 000·. The influence of TiO2 is not too pronounced. It seems to suppress the cristobalite crystallization, especially of longer heating runs. The image
analysis of leached glasses shows the prevailing content of the skeletal phase in a comparison to pores. The TiO2 content diminishes the content of the skeletal phase.
This revised version was published online in July 2006 with corrections to the Cover Date. 相似文献
6.
E. Jóna G. Rudinská M. Sapietová V. Pavlík M. Drábik S. C. Mojumdar 《Journal of Thermal Analysis and Calorimetry》2007,90(3):687-691
Interactions of 3-R-and 2-R pyridine (R=CH3, Cl, NH2) with Ni(II)-exchanged montmorillonite have been studied. Thermal and X-ray analyses indicate that pyridine derivatives are intercalated into the interlayer spaces of montmorillonite. Infrared spectral data shown that the Lewis and/or Brönsted type of interactions of pyridine derivatives is connected with different steric and inductive effects of the substituents (R) on the pyridine ring. The alkylpyridines increase the electron density on the donor nitrogen atom and support the coordination to the central atom. The halogen substituents have a negative inductive effect (–I), so that those ligands show a lower basicity and weaker σ-bonding properties than pyridine and also the lower possibility of the coordination. 相似文献
7.
This research provides a fundamental understanding of the early stage hydration of Portland cement paste, tricalcium aluminate
(C3A) paste at water to cement ratio of 0.5 and C3A suspension at water to cement ratio of 5.0 modified by 2 or 4 mass% of sodium carbonate. A high conversion of unreacted
clinker minerals to gel-like hydration products in the cement-Na2CO3 pastes takes place rapidly between 1st to 24th h. Contrary the Ca(OH)2 formation within the same time interval is retarded in the excess of CO32− ions due to intensive rise and growth of CaCO3 crystals in hydrated cement. Later, the conversion of clinker minerals to the hydrate phase is reduced and higher contents
of calcite and vaterite relative to that of Ca(OH)2 in comparison with those found in the Portland cement paste are observed. As a consequence a decrease in strength and an
increase in porosity between hardened Portland cement paste without sodium carbonate and those modified by Na2CO3 are observed. C3A hydrates very quickly with sodium carbonate between 1st and 24th h forming hydration products rich in bound water and characterized also by complex salts of (x)C3A·(y)CO2·(zH2O type, whereas C3A-H2O system offers C3AH6 as the main hydration product. Higher content of the formed calcium aluminate hydrates in C3A-Na2CO3-H2O system also contributes to early strength increase of Portland cement paste. 相似文献
8.
G. Madhurambal M. Mariappan S. Hariharan P. Ramasamy S. C. Mojumdar 《Journal of Thermal Analysis and Calorimetry》2013,112(2):1127-1132
Mixed crystals of 0.1 and 0.25 zinc magnesium ammonium sulphate were grown by slow evaporation of aqueous solution at room temperature. The bright and transparent crystals obtained were characterized by thermal (TG–DTA), FTIR and XRD analyses. A fitting decomposition pattern for the compound was formulated on the TG curve which shows two stage mass losses between 133 and 478.75 °C. In this temperature range, DTA curve shows exothermic peaks supporting the formulated decomposition pattern. The FTIR spectra show the vibration frequencies due to the formation of zinc magnesium ammonium sulphate mixed crystals. Detailed structural analysis of the compound is under progress. 相似文献
9.
M. Amutha G. Ramasamy S. P. Meenakshisundaram S. C. Mojumdar 《Journal of Thermal Analysis and Calorimetry》2011,104(3):949-954
The influence of the s-, p-, d-, and f-block elements (Cs, Sb, Pd, and Ce) doping on the properties of ammonium dihydrogen
phosphate (ADP) crystals has been described. Incorporation of small quantity of dopants into the crystalline matrix is well
confirmed by energy dispersive X-ray spectroscopy (EDS) and inductively coupled plasma (ICP) techniques. The reduction in
the intensity observed in powder X-ray diffraction (XRD) of doped specimens and slight shifts in vibrational frequencies confirm
the lattice stress. Surface morphological changes due to doping of metals are observed by scanning electron microscopy (SEM).
The differential scanning calorimetry (DSC) curves show only a slight variation in endothermic peak temperatures. The sharpness
of the DSC peaks shows the good degree of crystallinity of the material. The cell parameters have been determined using single
crystal XRD analysis of pure ADP and ADP:Cs/ADP:Sb/ADP:Pd/ADP:Ce specimens. The influence of metals on the second harmonic
generation (SHG) efficiency is also investigated. 相似文献
10.
P. Lizák Subhash Chandra Mojumdar 《Journal of Thermal Analysis and Calorimetry》2013,112(2):1095-1100
Objective evaluation techniques were used in this study of thermal properties of textile fabric. The Alambeta, P tester, and Togmeter measure the passages of air which were used for evaluation of the physiological properties. Fibrous materials were prepared in the form of textile knitting fabric COOLMAX. It is clear from the measurement that there are considerable differences in the results of measurement with described methods. Device Alambeta is convenient for the measurement and evaluation of various thermal properties. Finally, it can be concluded that this field of measurements is developing and will be the subject of further research of other methods, more suitable for measurement of the various characteristics. 相似文献