Milling time and BPR dependence on permeability and losses of Ni0.5Zn0.5Fe2O4 synthesized via mechanical alloying process

Ni_0.5Zn_0.5Fe₂O₄ has been synthesized using mechanical alloying method with two variables (milling time and ball-to-powder weight ratio (BPR)) were varied in order to study its effect on the magnetic properties of the material. The effects of these two variables were studied using XRD, SEM, TEM and later by impedance analyzer with the frequency range from 1 MHz to 1.8 GHz. The results obtained however show that there are no significant trends to relate the milling time and BPR with the permeability and losses of the material studied. After being sintered at 1150 °C, all the effects of alloying process seem to diminish.     

Effects of sintering temperature on grain growth and the complex permeability of Co0.2Ni0.3Zn0.5Fe2O4 material prepared using mechanically alloyed nanoparticles

Nanoparticle-sized Co_0.2Ni_0.3Zn_0.5Fe₂O₄ was prepared using mechanical alloying and sintering. The starting raw materials were milled in air and subsequently sintered at various temperatures from 600 to 1300 °C. The effects of sintering temperature on physical, magnetic and electrical characteristics were studied. The complex permittivity and permeability were investigated in the frequency range 10 MHz to 1.0 GHz. The results show that single phase Co_0.2Ni_0.3Zn_0.5Fe₂O₄ could not be formed during milling alone and therefore requires sintering. The crystallization of the ferrite sample increases with increasing sintering temperature; which decrease the porosity and increase the density, crystallite size and the shrinkage of the material. The maximum magnetization value of 83.1 emu/g was obtained for a sample sintered at 1200 °C, while both the retentivity and the coercivity decrease with increasing the sintering temperature. The permeability values vary with both the sintering temperature and the frequency and the absolute value of the permeability decreased after the natural resonance frequency. The real part of the permittivity was constant within the measured frequency, while the loss tangent values decreased gradually with increasing frequency.     

Dependence of developing magnetic hysteresis characteristics on stages of evolving microstructure in polycrystalline yttrium iron garnet

The microstructure evolution in several polycrystalline yttrium iron garnet samples as a result of a sintering scheme was studied in detail, in parallel with the changes in their magnetic properties. Samples with nanometer sized starting powder were synthesized by employing the High-Energy Ball Milling technique and then sintering toroidal compacts of the milled powder. Nine sintered samples were obtained, each corresponding to a particular sintering from 600 °C to 1400 °C. The samples were characterized for their evolution in crystalline phases, microstructure and magnetic hysteresis-loops parameters. The results showed an increasing tendency of the saturation magnetization and saturation induction with grain size, which is attributed to crystallinity increase and to reduction of demagnetizing fields in the grains. The variation in coercivity could be related to anisotropy field changes within the samples due to grain size changes. In particular, the starting appearance of room temperature ferromagnetic order suggested by the sigmoid-shaped B-H loops seems to be dependent on a sufficient number of large enough magnetic domain-containing grains having been formed in the microstructure. Viewed simultaneously, the hysteresis loops appear to belong to three groups with different magnetism-type dominance, respectively dependent on phase purity and three different groups of grain size distributions.     

Dependence of magnetic properties and microstructure of mechanically alloyed Ni0.5Zn0.5Fe2O4 on soaking time

Possible soaking-time effects on the magnetic and microstructural properties of polycrystalline samples of Ni_0.5Zn_0.5Fe₂O₄ have been studied. Nanosize powder produced by mechanical alloying was sintered at 800 °C with various soaking times. All samples showed the signature peak of Ni_0.5Zn_0.5Fe₂O₄ even with one hour of soaking time. The size distributions show a slow growth of microstructural evolution related to density, porosity and also to the magnetic hysteresis loops. Within these distributions it is observed that the formation of multi-domains is not possible and probably there are the regions of superparamagnetic and single-domain grains. From the permeability studies, it is believed that the rise of the magnetic moment on the B sites give rise to the total saturation magnetization with increase of soaking time. The hysteresis loop of one-hour soaking time showed paramagnetic behavior dominating while longer soaking times showed ferromagnetic behavior starting to dominate. The coercivity was observed to increase with soaking time, signaling the increase of the anisotropy fields which was attributed to the shape anisotropy and also to the magnetocrystalline anisotropy. By correlating the morphology, phase analysis, permeability and hysteresis loops results, it is believed that there was an increase in number of crystalline-growth regions which together formed a total mass of mixed superparamagnetic and ferromagnetic grains with the latter starting to dominate the samples.     

Systematic microstructural development with thermal diffusivity behaviour from nanometric to micronic grains of strontium titanate

Journal of Thermal Analysis and Calorimetry - Strontium titanate is a promising candidate for applications in thermoelectric, thermal management applications, and modern electronic devices because...