Gesamtinhaltsverzeichnis der „Semesterberichte“ (1932–2007)

Ohne Zusammenfassung     

Dielectric relaxation analysis of starch oligomers and polymers with respect to their chain length

Starch belongs to the polyglucan group. This type of polysaccharide shows a broad β-relaxation process in dielectric spectra at low temperatures, which has its molecular origin in orientational motions of sugar rings via glucosidic linkages. This chain dynamic was investigated for α(1,4)-linked starch oligomers with well-defined chain lengths of 2, 3, 4, 6, and 7 anhydroglucose units (AGUs) and for α(1,4)-polyglucans with average degrees of polymerization of 5, 10, 56, 70, and so forth (up to 3000; calculated from the mean molecular weight). The activation energy (E_a) of the segmental chain motion was lowest for dimeric maltose (E_a = 49.4 ± 1.3 kJ/mol), and this was followed by passage through a maximum at a degree of polymerization of 6 (E_a = 60.8 ± 1.8 kJ/mol). Subsequently, E_a leveled off at a value of about 52 ± 1.5 kJ/mol for chains containing more than 100 repeating units. The results were compared with the values of cellulose-like oligomers and polymers bearing a β(1,4)-linkage. Interestingly, the shape of the E_a dependency on the chain length of the molecules was qualitatively the same for both systems, whereas quantitatively the starch-like substances generally showed higher E_a values. Additionally, and for comparison, three cyclodextrins were measured by dielectric relaxation spectroscopy. The ringlike molecules, with 6, 7, and 8 α(1,4)-linked AGUs, showed moderately different types of dielectric spectra. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 188–197, 2004     

Synthesis and gas barrier characterization of poly(ethylene isophthalate)

Poly(ethylene isophthalate) (PEI) was synthesized for this research with essentially a condensation polymerization of isophthalic acid and ethylene glycol catalyzed by zinc acetate and antimony trioxide. Several samples were obtained, and their characteristics were observed and compared with poly(ethylene terephthalate) (PET). The synthesized PEI samples were chemically identified by ¹H NMR. Thermal analysis with differential scanning calorimetry (DSC) yielded results that indicate the samples were primarily amorphous, with a glass‐transition temperature of 55–60 °C. Molecular weights of these PEI samples were also obtained through intrinsic viscosity measurements (Mark–Houwink equation). Molecular weights varied with conditions of the polymerization, and the highest molecular weight achieved was 21,000 g/mol. Finally, the diffusion coefficient, solubility, and permeability of CO₂ gas in PEI were measured and found to be substantially lower than in PET, as anticipated from their isomeric chemical structures. This is because in PET the phenyl rings are substituted in the para (1,4) positions, which allows for their facile flipping, effectively permitting gases to pass through. However, the meta‐substituted phenyl rings in PEI do not permit such ring flipping, and thus PEI may be more suitable for barrier applications. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4247–4254, 2004     

Shell effects in the symmetric-modal fission of pre-actinide nuclei

Mass distributions of fragments in the low-energy fission of nuclei from ¹⁸⁷Ir to ²¹³At have been analysed. This analysis has shown that shell effects in symmetric-mode fragment mass yields from the fission of pre-actinide nuclei could be described if one assumes the existence of two strongly deformed neutron shells in the arising fragments with neutron numbers N₁ ≈ 52 and N₂ ≈ 68. A new method has been proposed for quantitatively describing the mass distributions of the symmetric fission mode for pre-actinides with A ≈ 180–220.