Silver Nanowires and Silanes in Hybrid Functionalization of Aramid Fabrics

New functionalization methods of meta- and para-aramid fabrics with silver nanowires (AgNWs) and two silanes (3-aminopropyltriethoxysilane (APTES)) and diethoxydimethylsilane (DEDMS) were developed: a one-step method (mixture) with AgNWs dispersed in the silane mixture and a two-step method (layer-by-layer) in which the silanes mixture was applied to the previously deposited AgNWs layer. The fabrics were pre-treated in a low-pressure air radio frequency (RF) plasma and subsequently coated with polydopamine. The modified fabrics acquired hydrophobic properties (contact angle Θ_W of 112–125°). The surface free energy for both modified fabrics was approximately 29 mJ/m², while for reference, meta- and para-aramid fabrics have a free energy of 53 mJ/m² and 40 mJ/m², respectively. The electrical surface resistance (R_s) was on the order of 10² Ω and 10⁴ Ω for the two-step and one-step method, respectively. The electrical volume resistance (R_v) for both modified fabrics was on the order of 10² Ω. After UV irradiation, the Rs did not change for the two-step method, and for the one-step method, it increased to the order of 10¹⁰ Ω. The specific strength values were higher by 71% and 63% for the meta-aramid fabric and by 102% and 110% for the para-aramid fabric for the two-step and one-step method, respectively, compared to the unmodified fabrics after UV radiation.     

Magnetic Fe doped ZnO nanofibers obtained by electrospinning

We demonstrate structural and room temperature magnetic properties of Fe doped ZnO nanofibers (NFs) obtained by electrospinning followed by calcination. The observed NFs, formed from crystalographically oriented, approximately 4.5?nm particles conglomerates, were approximately 200?nm in diameter. The reported synthesis of room temperature ferromagnetic Fe doped ZnO NFs is both facile and economical, and is therefore suggested as a generic method of fabricating biocompatible magnetic materials. The major substrates selected for the NFs synthesis (Zn, Fe) comprised of relatively low toxicity materials. Incorporating 10% Fe into ZnO does not modify the wurtzite crystal structure of the host material. No evidence of impurity phase was detected by either X-ray or electron diffraction. Magnetometry studies and Magnetic Force Microscopy imaging reveal a local ferromagnetic order that persists up to room temperature. We suggest that the observed phenomenon is either due to a mechanism mediated by presence of oxygen vacancies and/or is related to iron-rich precipitates.     

The growth kinetics of colloidal ZnO nanoparticles in alcohols

We have studied the synthesis of ZnO nanostructures over a wide range of parameters to determine the kinetics of the nanocrystals growth. The initial rapid nucleation and growth is kinetically controlled, the subsequent ZnO nanocrystals growth is thermodynamically controlled through the diffusion limited Ostwald coarsening. The ZnO coarsening rates increased with number of alcohol’s alkyl group carbons and temperature increase, pointing to importance of the solvent viscosity, dielectric constants, surface energy and the bulk solubility. The results are consistent with the Lifshitz–Slyozov–Wagner model. For all alcohols, in the NaOH induced reaction, a lower activation energy was observed compared to the aqueous reaction. A lower ZnO solubility, obtained by the water synthesis could be responsible for these observations. Our results point to the importance of the reactant selection in controlling the kinetics of the nanostructure formation, their size and the nature of the surface defects responsible for their luminescence.