Improving electrochemical performance of poly(vinyl butyral)-based electrolyte by reinforcement with network of ceramic nanofillers

This study has concerned the development of polymer composite electrolytes based on poly(vinyl butyral) (PVB) reinforced with calcinated Li/titania (CLT) for use as an electrolyte in electrochemical devices. The primary aim of this work was to verify our concept of applying CLT-based fillers in a form of nano-backbone to enhance the performance of a solid electrolyte system. To introduce the network of CLT into the PVB matrix, gelatin was used as a sacrificial polymer matrix for the implementation of in situ sol–gel reactions. The gelatin/Li/titania nanofiber films with various lithium perchlorate (LiClO₄) and titanium isopropoxide proportions were initially fabricated via electrospinning, and ionic conductivities of electrospun nanofibers were then examined at 25 °C. In this regard, the highest ionic conductivity of 2.55 × 10⁻⁶ S/cm was achieved when 10 wt% and 7.5 wt% loadings of LiClO₄ and titania precursor were used, respectively. The nanofiber film was then calcined at 400 °C to remove gelatin, and the obtained CLT film was then re-dispersed in solvated PVB-lithium bis(trifluoromethanesulfonyl)imide (PVB-LiTFSI) solution before casting to obtain reinforced composite solid electrolyte film. The reinforced composite PVB polymer electrolyte film shows high ionic conductivity of 2.22 × 10⁻⁴ S/cm with a wider electrochemical stability window in comparison to the one without nanofillers.

     

Coherent beam combination of narrow-linewidth 1.5 μm fiber amplifiers in a long-pulse regime

We report what we believe to be the first experimental demonstration of coherent beam combining of two fiber amplifiers in a 100 ns pulse regime using a signal leak between the pulses. Pulses of ～100 W stimulated-Brillouin-scattering limited peak power are combined with 95% efficiency, a residual phase error of λ/27, and no significant beam quality degradation.     

An optical study of cobalt nanowires dispersed in liquid phase

The Co nanowires were electrodeposited in polycarbonate membrane (PCT). SEM, TEM and XPS techniques were used to characterize the morphology, structure and size of nanowires as well as chemical composition. The influence of different mediums was studied on the optical absorption of dispersed cobalt nanowires. The absorption spectrum of cobalt nanowires in water showed a broad shoulder at 290 nm, but in ethanol solution it was not observed in the visible region of the spectra up to 200 nm. Cobalt nanowires dispersed in methanol presented a peak at 236 nm. We attribute the data to oxidation of cobalt in water and low dielectric constant of methanol relative to ethanol and water. We found rather good agreement between the experimental results and the calculation based on Gans’ theory.     

Facile synthesis of Fe@Pd nanowires and their catalytic activity in ligand-free CN bond formation in water

This work reports a facile synthesis of Fe@Pd nanowires. Ligand-free cross coupling reactions of arylboronic acids with various amines in aqueous medium proceed in very good to excellent yield with the use of Fe@Pd nanowires. Furthermore, the catalyst could be easily separated from the reaction mixture using a magnet and could be recycled several times without loss of catalytic activity.