1.
A. Sanusi M. Z. A. Yahya S. Navaratnam W. J. Basirun Y. Alias N. S. Mohamed A. K. Arof 《Ionics》2003,9(3-4):253-257
In this study, lead sulphide (PbS) was prepared by the chemical bath deposition technique. The sample was characterized by
X-ray diffraction (XRD), Energy Dispersive Analysis of X-rays (EDAX) and cyclic voltammetry. EDAX spectrum shows peaks attributable
to lead and sulphur. The EDAX analysis also shows that the prepared sample is stoichiometric. Cyclic voltammetry experiments
were recorded at 100 mV·s−1 and 400 mV·s−1 scan rates. Results show that the rate controlling electrochemical reaction is electron transfer. The presence of redox waves
shows that the lithium intercalation and deintercalation can occur as a result of lattice expansion in PbS. There were no
differences in the PbS XRD data before and after the cyclic voltammetry experiments indicating that the PbS structure is not
modified upon lithium ion intercalation and deintercalation in PbS. The discharge characteristics for 35 cycles of the cell
using the LiCoO2/PbS couple is presented indicating the possible development of such materials as anode in lithium ion cells. 相似文献
2.
Yuanwei Liu Kishneth Palaniveloo Siti Aisyah Alias Jaya Seelan Sathiya Seelan 《Molecules (Basel, Switzerland)》2021,26(11)
Soft corals are widely distributed across the globe, especially in the Indo-Pacific region, with Sarcophyton being one of the most abundant genera. To date, there have been 50 species of identified Sarcophyton. These soft corals host a diverse range of marine fungi, which produce chemically diverse, bioactive secondary metabolites as part of their symbiotic nature with the soft coral hosts. The most prolific groups of compounds are terpenoids and indole alkaloids. Annually, there are more bio-active compounds being isolated and characterised. Thus, the importance of the metabolite compilation is very much important for future reference. This paper compiles the diversity of Sarcophyton species and metabolites produced by their associated marine fungi, as well as the bioactivity of these identified compounds. A total of 88 metabolites of structural diversity are highlighted, indicating the huge potential these symbiotic relationships hold for future research. 相似文献
3.
This study aimed to evaluate the effects of ultrasound on Lactobacillus fermentum BT 8633 in parent and subsequent passages based on their growth and isoflavone bioconversion activities in biotin-supplemented soymilk. The treated cells were also assessed for impact of ultrasound on probiotic properties. The growth of ultrasonicated parent cells increased (P < 0.05) by 3.23-9.14% compared to that of the control during fermentation in biotin-soymilk. This was also associated with enhanced intracellular and extracellular (8.4-17.0% and 16.7-49.2%, respectively; P < 0.05) β-glucosidase specific activity, leading to increased bioconversion of isoflavones glucosides to aglycones during fermentation in biotin-soymilk compared to that of the control (P < 0.05). Such traits may be credited to the reversible permeabilized membrane of ultrasonicated parent cells that have facilitated the transport of molecules across the membrane. The growing characteristics of first, second and third passage of treated cells in biotin-soymilk were similar (P > 0.05) to that of the control, where their growth, enzyme and isoflavone bioconversion activities (P > 0.05) were comparable. This may be attributed to the temporary permeabilization in the membrane of treated cells. Ultrasound affected probiotic properties of parent L. fermentum, by reducing tolerance ability towards acid (pH 2) and bile; lowering inhibitory activities against selected pathogens and reducing adhesion ability compared to that of the control (P < 0.05). The first, second and third passage of treated cells did not exhibit such traits, with the exception of their bile tolerance ability which was inherited to the first passage (P < 0.05). Our results suggested that ultrasound could be used to increase bioactivity of biotin-soymilk via fermentation by probiotic L. fermentum FTDC 8633 for the development of functional food. 相似文献
4.
Wee Ching Tan Siti Salwa Alias Ahmad Badri Ismail Ahmad Azmin Mohamad 《Journal of Solid State Electrochemistry》2012,16(6):2103-2112
The effect of a gel polymer electrolyte (GPE) as the redox electrolyte used in dye-sensitized solar cells was studied. A GPE solution consisting of 0.5?M sodium iodide, 0.05?M iodine, and ethylene carbonate/propylene carbonate (1:1 w/w) binary solvents was mixed with increasing amounts of styrene–acrylonitrile (SAN). Bulk conductivity measurements show a decreasing trend from 4.54 to 0.83×10?3?S?cm?1 with increasing SAN content. The GPE exhibits Newtonian-like behavior and its viscosity increases from 0.041 to 1.093?Pa?s with increasing SAN content. A balance between conductivity (1.3?×?10?3?S?cm?1) and viscosity (1.4?Pa?s) is observed at 19?wt.% SAN. Fourier transform infrared spectroscopy detects elevated ring torsion at 706?cm?1 upon the addition of SAN into the liquid electrolyte. This indicates that SAN does not bond with the liquid electrolyte. Finally, the potential stability window of 19?wt.% SAN, which ranges from ?1.68 to 1.38?V, proves its applicability in solar cells. 相似文献
5.
High-performance oxide vertical-cavity surface-emitting (VCSEL) laser is fabricated, and its usefulness is demonstrated as a suitable transmitting light source at 850 nm operating wavelength for Gigabit Ethernet application. Utilization of barrier reduction layers reveals low-threshold current requirement for operation at high modulation bandwidth. The electrical and optical characteristics, measured from the fabricated VCSEL, are simulated for Gigabit Ethernet transmission. Data rates of 1.25 Gbps with a bit error rate of 10−11 are achieved by the use of a specific multimode network simulator. 相似文献
6.
Zn/Zn5(OH)8Cl2·H2O flower-like nanostructures was electrodeposited on the coated Zn with poly (N-methyl pyrrole) in 0.1 M Zn (NO3)2 and 0.1 M KCl solution. The morphology and the structure of the Zn/Zn5(OH)8Cl2·H2O were characterized by Field Emission Scanning Electron Microscopy (FESEM), Fourier transform infrared (FT-IR) spectroscopy and X-ray diffraction analysis (XRD). The FT-IR results showed special peaks at 908 and 728 cm−1 related to Zn5(OH)8Cl2·H2O. The FESEM results indicated that Zn/Zn5(OH)8Cl2·H2O consists of a flower-like nanostructure and these flower-shaped structures contain many shaped nanopetals with the thickness of 27.8 nm. The XRD result confirmed that the major phase of electrodeposited product in 0.1 M KCl as supporting electrolyte was Zn5(OH)8Cl2·H2O. The ability of PMPy to create a thin film and the existence of several pores in its matrix act as a mold for the growth of Zn/Zn5(OH)8Cl2·H2O flower-like nanostructure. The trapping of Cl− and OH− within pores can be considered as the reason for the formation of flowerlike Zn/Zn5(OH)8Cl2·H2O nanostructures in 0.1 M KCl. 相似文献
7.
Chemical modification of natural rubber (NR) has frequently been attempted to improve the performance in specific application.
30% poly (methyl metacrylate) grafted NR (MG 30) has been explored as a potential candidate for polymer electrolytes. The
complexation effect of LiCF3SO3, ethylene carbonate (EC) and Al2SiO5 in polymer host electrolytes has been investigated using FTIR ICP-OES spectrometry. Thermal studies of the systems have displayed
a stable trend of glass temperature transition at elevated salt concentration whereas incorporation of EC and filler into
the system results in the same pattern in their Tg values.
Paper presented at the International Conference on Functional Materials and Devices 2005, Kuala Lumpur, Malaysia, June 6 –
8, 2005. 相似文献
8.
The paper essentially deals with the analysis of photonic band-gap fibers in analogy with the electron wave motion in periodic crystal lattice. As such, the analyses are based on Bloch formulation. The dispersion characteristics of such fibers are presented by considering some illustrative values of design parameters. The effect of design parameters on the dispersion characteristics is also presented in terms of the variation of widths of allowed and forbidden bands of band-gap fibers. It is found that the number of allowed bands increases with the increase in difference between refractive indices of different layers. Further, widths of the allowed and forbidden bands increase with the increase in layer thickness. 相似文献
9.
Gel polymer electrolytes were prepared using agar polymer host, NH4I, and I2 salts. The sample of agar paste with 1.0 M of NH4I and 0.2 μM of I2 exhibits the highest conductivity and lowest viscosity values at room temperature of (2.64?±?0.19)?×?10?3?S?cm?1 and 1.17?±?0.29 Pa?s, respectively. All of the gel polymer electrolytes display Arrhenian behavior, and the optimum agar paste gave the lowest activation energy of 0.25 eV. It also had a good physical appearance compared with the other samples. This gel polymer electrolyte had a good potential and was applicable to a role as electrolyte in ITO-ZnO (N719 dye)/agar paste?+?1.0 M NH4I?+?0.2 μM I2/Au-Pd-ITO dye-sensitized solar cell. 相似文献
10.
This study is to investigate the magnetohydrodynamic (MHD) stagnation point flow and heat transfer characteristic nanofluid of carbon nanotube (CNTs) over the shrinking surface with heat sink effects. Similarity equations deduced from momentum and energy equation of partial differential equations are solved numerically. This study looks at the different parameters of the flow and heat transfer using first phase model which is Tiwari-Das. The parameter discussed were volume fraction nanoparticle, magnetic parameter, heat sink/source parameters, and a different type of nanofluid and based fluids. Present results revealed that the rate of nanofluid (SWCNT/kerosene) in terms of flow and heat transfer is better than (MWCNT/kerosene) and (CNT/water) and regular fluid (water). Graphically, the variation results of dual solution exist for shrinking parameter in range for different values of volume fraction nanoparticle, magnetic, heat sink parameters, and a different type of nanofluid. However, a unique solution exists at , and no solutions exist at which is a critical value. In addition, the local Nusselt number decreases with increasing volume fraction nanoparticle when there exists a heat sink effect. The values of the skin friction coefficient and local Nusselt number increase for both solutions with the increase in magnetic parameter. In this study, the investigation on the flow and heat transfer of MHD stagnation point nanofluid through a shrinking surface with heat sink effect shows how important the application to industrial applications. 相似文献